Nanocrystalline ZnO/Zeolite type A composite was prepared by simple method of operation by . the precipitation of zinc oxide and loading on zeolite 5A in one step. Characterization was made by X-ray diffraction (XRD), X-ray fluorescence(XRF), N2  adsorption- desorption for BET surface area, and Atomic force microscopy (AFM). Results showed that zinc oxide was loaded on zeolite as noticed by the characteristic peaks and was of nano scale having an average diameter of 88.57nm. The percentage loading of ZnO on zeolite A was 28.37% and the surface area was 222m2/g. The activity of the prepared catalyst was examined in the desulfurization of double hydrogenated diesel fuel. The process was investigated in a

The adsorption behavior of congo red dye from its aqueous solutions was investigated onto natural and modified bauxite clays. Both bauxite and modified bauxite are primarily characterized by using, FTIR, SEM, AFM, and XRD. Several variables are studied as a function of adsorption including contact time, adsorbent weight, pH, ionic strength, particle size and temperature under batch adsorption technique. The absorbance of the solution before and after adsorption was measured spectrophotometrically. The equilibrium data fit with Langmuir model of adsorption and the linear regression coefficient R2 is found to be 0.9832 and 0.9630 for natural and modified bauxite respectively at 37.5°C which elucidate the best fitting isotherm model. The gene

The toxic lead additives to gasoline are no longer used in many countries around the world. Many other countries are now phasing out the lead in gasoline. Although the lead fuel is still in use in Iraq, several plans are considered to phase out the lead. The use of organic compounds to replace the lead additives in gasoline is considered now as an option in Iraqi refineries. The main objective of this project was preparation of premium gasoline, by blending of gasoline with Alternative additives (alcohol, aromatic) to enhancing octane number of Al-Doura gasoline pool. Improved gasoline was tested by ASTM standard method which includes octane number measuring by CFR engine analyzer. Gasoline pool RON (80) was used and selective components

Fabrication of a photodetector consists of the conjugated polymer "MEH-PPV"- poly (2-methoxy-5-(2'-ethylhexyloxy)-1,4-phenlenevinylene) and MEH-PPV:MWCNT nanocomposite thin film. The volume ratio investigated was 0.75:0.25. MEH-PPV was dissolved in chloroform solvent and doped with MWCNTs. The spin coating method was used to achieve a facile and low cost photodetector. The absorption spectrum decreases by adding the CNTs. The PL spectrum detected recombination curve results by doping the polymer with CNTs, and AFM measurement showed an increase of roughness average from (0.168 to 2.43nm) of "MEH-PPV" and "MEH-PPV:CNTs", respectively. The doping ratio 0.25, which has a higher photoresponsivity, was evaluated at 1.70 A/W and 2.14 A/W of th

In this study, composite materials consisting of Activated Carbon (AC) and Zeolite were prepared for application in the removal of methylene blue and lead from an aqueous solution. The optimum synthesis method involves the use of metakaolinization and zeolitization, in the presence of activated carbon from kaolin, to form Zeolite. First, Kaolin was thermally activated into amorphous kaolin (metakaolinization); then the resultant metakaolin was attacked by alkaline, transforming it into crystalline zeolite (zeolitization). Using nitrogen adsorption and SEM techniques, the examination and characterization of composite materials confirmed the presence of a homogenous distribution of Zeolite throughout the activated carbon.

In this work an experimental study is performed to evaluate the thermal performance
of locally made closed loop solar hot water system using a shell and helical coiled tube
heat exchanger as a storage tank. Several measurements are taken include inlet and outlet
temperatures of both collectors and supply water and temperature distribution within the
storage tank. This is beside the water flow rate in both collectors and load cycle. The
main parameters of the system are obtained.