The ability of single and mixed bacterial culture to utilize Dora-refineries petroleum wastes was compared. Pseudomonas aeruginosa and Serratia ficaria mixed culture consumed the wastes better than the single bacterial cultures. The highest log. number of viable cells in mixed culture was 6.842 , while in single bacterial cultures it was 6.683 and 5.631, respectively. after 3 days in API medium containing the refinery wastes. The effect of some environmental conditions on the degradation of petroleum wastes was studied included aeration , NaCl concentration , pH and temperature. The growth of bacteria in the agitated culture was higher than stagnant culture the log. of cell no. was 6.021 in the first culture. The h

AA3003-H14 aluminum alloy plates were welded by friction stir welding and TIG welding.
Fatigue properties of the welded joints were evaluated based on the superior tensile properties for
FSW at 1500 rpm rotational speed and 80 mm/min welding speed. However, there is not much
information available on effect of welding parameters with evolution of fatigue life of friction stir
welds. The present study experimentally analyzed fatigue properties for base, FSW, and TIG welds
of AA 3003-H14 aluminum alloy. Fatigue properties of FSW joints were slightly lower than the
base metal and higher than TIG welding.

The ejector refrigeration system is a desirable choice to reduce energy consumption. A Computational Fluid Dynamics CFD simulation using the ANSYS package was performed to investigate the flow inside the ejector and determine the performance of a small-scale steam ejector. The experimental results showed that at the nozzle throat diameter of 2.6 mm and the evaporator temperature of 10^oC, increasing boiler temperature from 110^oC to 140^oC decreases the entrainment ratio by 66.25%. At the boiler temperature of 120^oC, increasing the evaporator temperature from 7.5 to 15 ^oC increases the entrainment ratio by 65.57%. While at the boiler temperature of 120^oC and

  In this paper, Cu2S/CdS solar cells were prepared with different thickness of CdS layer, these layers were prepared by using chemical spray pyrolysis technique. The chemical spray solution was prepared by mixing cadmium chloride CdCl2 and thiourea CS(NH2)2 of molar concentration 0.1 M/L, the CdS layer was formed after the solution was sprayed on hot Aluminum substrate at temperature 400°C. Experimentally the type of CdS film was found as n–type depending on the results of Hall Effect, the value of the Hall factor (RH) is about – 1.348 x 10–6 m3/C and the density of the majority charge carriers (N) is about 4.64x1018 cm–3.       The prepared film was tested by using X-Ray