Previous data indicated the effectiveness of silibinin as intraocular pressure (IOP) - lowering agent. The present study was performed to evaluate the interaction of silibinin with pilocarpine or cyclopentolate in lowering IOP in normotensive rabbits. The effects of topically instilled silibinin hemisuccinate solution (0.75%) alone or adjunctly combined with 2% pilocarpine or 1% cyclopentolate on the IOP of normotensive rabbits were evaluated using indentation tonometry. The results showed that 0.75% solution of silibinin was found more potent than pilocarpine (2% drops) in lowering IOP of normotensive rabbits, while their combination results in longer duration of action. Moreover, the elevated IOP values produced by cyclopentolate (1%drops

Previous data indicated the effectiveness of silibinin as intraocular pressure (IOP) - lowering agent.  The present study was performed to evaluate the interaction of silibinin with pilocarpine or cyclopentolate in lowering IOP in normotensive rabbits. The effects of topically instilled silibinin hemisuccinate solution (0.75%) alone or adjunctly combined with 2% pilocarpine or 1% cyclopentolate on the IOP of normotensive rabbits were evaluated using indentation tonometry. The results showed that 0.75% solution of silibinin was found more potent than pilocarpine (2% drops) in lowering IOP of normotensive rabbits, while their combination results in longer duration of action. Moreover, the elevated IOP values produced by cyclopentolate

In the present study, MIG welding is carried out on low carbon steel type (AISI 1015) by using electrode ER308L of 1.5mm diameter with direct current straight polarity (DCSP). The joint geometry is of a single V-butt joint with one pass welding stroke for different plate thicknesses of 6, 8, and 10 mm. In welding experiments, AISI 1015 plates with dimensions of 200×100mm and edge angle of 60^o from both sides are utilized. In this work, three main parameters related to MIG welding process are investigated, which are welding current, welding speed, heat input and plate thickness, and to achieve that three groups of plates are employed each one consists of three plates. The results indicate that increasing the weld heat input (t

This research aims to study the effect of microwave furnace heat on the mechanical properties and fatigue life of aluminum alloy (AA 2024-T3). Four conditions were used inside microwave furnace (specimens subjected to heat as dry for 30 and 60min. and specimens subjected to heat as wet (water) for 30 and 60 min.), and compared all results with original alloy (AA 2024-T3). Tensile, fatigue, hardness and surface roughness tests were used in this investigation. It is found that hardness of dry conditions is higher than wet conditions and it increases with increasing of time duration inside microwave furnace for dry and wet conditions. Also, tensile strength has the same behavior of hardness, but it increases with decreasing

   This research provides a novel technique for using metal organic frameworks (HKUST-1) as a gas storage system for liquefied petroleum gas (LPG) in Iraqi vehicles to avoid the drawbacks of the currently employed method of LPG gas storage. A low-cost adsorbent called HKUST-1 was prepared and characterized in this research to investigate its ability for propane storage at different temperatures (25, 30, 35, and 40 ^oC) and pressures of (1-7) bar. HKUST-1 was made using a hydrothermal method and characterized using powder X-ray diffraction, BET surface area, scanning electron microscopic (SEM), and Fourier Transforms infrared spectroscopy (FTIR). The HKUST-1 was produced using a hydrothermal technique and possesses a high crys

Background: In this study we evaluate the effect of plasma treatment (oxygen and argon) gas in two different exposure times on the surface of heat cure and light cure acrylic resin. Materials and method: 100 specimens of heat cure and light cure acrylic resin were fabricated. The measurements of the samples were (75mm, 25mm and 4.5mm) length, width and depth respectively with stopper of 3mm depth. Two types of gas used oxygen and argon in (5,10) min by using (DC-glow discharge plasma device) then we apply cold cure soft lining material, with the help of Instron machine we test the shear stress value. Results: A highly significant effect after argon and oxygen gases treatment in both 5 and 10 min exposure times on shear bond strength to soft