Influence of Liquid Asphalt on Resilient Modules and Permanent Deformation of Recycled Asphalt Concrete
...Show More Authors

Tests were performed on Marshall samples and were implemented for permanent deformation and resilient modulus (Mr) under indirect tensile repeated loading (ITRL), with constant stress level. Two types of liquid asphalt (cutback and emulsion) were tried as recycling agents, aged materials that were reclaimed from field (100% RAP), samples were prepared from the aged mixture, and two types of liquid asphalt (cutback and emulsion) with a weight content of 0.5% were utilized to prepare a recycled mixture. A group of twelve samples was prepared for each mixture; six samples were tested directly for ITRL test (three samples at 25˚C and three samples at 40˚C), an average value for ITRL for every three samples was calculated (ITRL for unconditioned samples). The other six samples were placed in volumetric flask 4000-ml heavy- wall glass filled with water at 25˚C under a vacuum pressure of (3.74 kPa) for 5 to 10 minutes. Then the samples were put in deep freeze for 16 hours at -18˚C. The samples were frozen then were transported to a water bath at 60ºC for 24 hours. Then they were soaked in a water bath for 1 hour at 25ºC and tested for the ITRL test (three samples at 25˚C and three samples at 40˚C), the average value of ITRL for every three samples was calculated (ITRL for conditioned samples). It was concluded that the reduction in (Mr) at the Conditioned test as compared to the Unconditioned test was (29.5%, 22.27% and 9.09%) at 25˚C, while at 40˚C, the reduction was (21.28%, 15.53%, and 17.89%) for aged and recycled mixtures with (cutback), and (emulsion) respectively. The change in permanent deformation at the Conditioned test as compared to Unconditioned one was (76.19%, 75.61% and 53.22%) at 25˚C, while at 40˚C it was (56.48%, 35.19%, and 78.33%) for aged and recycled mixtures with (cutback), and (emulsion) respectively.

 

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Tue May 01 2018
Journal Name
Journal Of Engineering
The Improvement of Thermal Insulating Concrete Panel
...Show More Authors

The Iraqi houses flattening the roof by a concrete panel, and because of the panels on the top directly exposed to the solar radiation become unbearably hot and cold during the summer and winter. The traditional concrete panel components are cement, sand, and aggregate, which have a poor thermal property. The usage of materials with low thermal conductivity with no negative reflects on its mechanical properties gives good improvements to the thermal properties of the concrete panel. The practical part of this work was built on a multi-stage mixing plan. In the first stage the mixing ratio based on the ratios of the sand to cement. The second stage mixing ratios based on replacing the coarse aggregate quantities with the

... Show More
View Publication Preview PDF
Crossref
Publication Date
Wed Nov 03 2021
Journal Name
Journal Of Engineering Research
Performance of quadrilateral perforated prestressed concrete rafters
...Show More Authors

This study focuses on the behavior of simply supported perforated prestressed concrete rafters (PPCRs) under single midspan monotonic static loading. The experimental program consisted of testing seven specimens; one solid (control) rafter, and six perforated with quadrilateral openings. The main investigated variables are the number and height of the openings. The test findings indicate that, in comparison to the solid rafter, the presence of quadrilateral openings in the PPCRs led to reducing the load capacity by (4.3-36%) and increase the midspan deflection at ultimate by (14.8-33%). Also, increasing the number of concrete posts between openings resulted in increasing the failure load and decreasing the deflection at all stages o

... Show More
View Publication
Crossref (1)
Crossref
Publication Date
Thu Sep 01 2022
Journal Name
Engineering Structures
Mesoscale analysis of Fiber-Reinforced concrete beams
...Show More Authors

Crossref (17)
Crossref
Publication Date
Sat Apr 07 2018
Journal Name
Civil Engineering Journal
Behavior of Precast Prestressed Concrete Segmental Beams
...Show More Authors

The structural behavior of Segmental Precast Post-tensioned Reinforced Concrete (SPPRC) beams largely depends on the behavior of the joints that connect between the segments. In this research, series of static tests were carried out to investigate the behavior of full-scale SPPRC beams with different types of epoxy-glued joint configurations; multi-key joint, single key, and plain key joint. The reference specimen was monolithically casted beam and the other specimens were segmental beams with five segments for each one. The general theme from the experimental results reflects an approximate similarity in the behavior of the four beams with slight differences. Due to the high tensile strength of the used epoxy in comparison to concr

... Show More
Crossref (10)
Clarivate Crossref
Publication Date
Fri Jul 21 2023
Journal Name
Journal Of Engineering
Corrosion-Resistance Characteristics of Concrete Containing Furfural
...Show More Authors

Corrosion inhibiting admixtures are unique among other methods to protect reinforced concrete from corrosion damage. In this study, the effect of furfural on the fresh and hardened properties of concrete mixes of 35 and 45 MPa compressive strengths as well as the corrosion inhibition of furfural was evaluated. Furfural was added at different dosages (1, 2 and 3% by weight of cement) with and without superplasticizer (HRWR). Different electrochemical measurements were performed (Half-cell potential, Tafel plot and linear polarization resistance). Electrochemical measurements confirmed that furfural dramatically reduces the rate of corrosion; the inhibition efficiencies were 62.7 and 63.8 % due to 3% furfural addition to 35 and 45MPa-concr

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Thu Sep 30 2004
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Corrosion Inhibition of Steel Reinforcement in Concrete
...Show More Authors

View Publication Preview PDF
Publication Date
Fri Jan 01 2016
Journal Name
Journal Of Engineering
Some Durability Test of No-Fine Concrete
...Show More Authors

In this study, two types of mixes were adopted by using two grading of coarse aggregate. The practical side of this study was to produce no-fine aggregate concrete by using crushed clay brick aggregates. The durability of the produced concrete and internal sulfate attack was studied.      For durability assessment, it is found that the no-fine concrete made with crushed brick aggregate lost about (15-25) % of its compressive strength after being subjected to 60 cycles of wetting and drying with age 120 days. The curing condition showed that the water curing improved the compressive strength with a rate higher than that when sealed or air dry curing were used. The crushed brick no-fine concrete de

... Show More
View Publication Preview PDF
Publication Date
Mon Jan 11 2021
Journal Name
Engineering, Technology & Applied Science Research
Impact Resistance of Bendable Concrete Reinforced with Grids and Containing PVA Solution
...Show More Authors

The development of new building materials, able of absorbing more energy is an active research area. Engineering Cementitious Composite (ECC) is a class of super-elastic fiberreinforced cement composites characterized by high ductility and tight crack width control. The use of bendable concrete produced from Portland Limestone Cement (PLC) may lead to an interest in new concrete mixes. Impact results of bendable concrete reinforced with steel mesh and polymer fibers will provide data for the use of this concrete in areas subject to impact loading. The experimental part consisted of compressive strength and impact resistance tests along with a result comparison with unreinforced concrete. Concrete samples, with dimensions of 100×

... Show More
Publication Date
Tue Jun 01 2021
Journal Name
Iop Conf. Series: Materials Science And Engineering
Enhancing the mechanical properties of lightweight concrete using mono and hybrid fibers
...Show More Authors
Abstract<p>This investigation aims to study some properties of lightweight aggregate concrete reinforced by mono or hybrid fibers of different sizes and types. In this research, the considered lightweight aggregate was Light Expanded Clay Aggregate while the adopted fibers included hooked, straight, polypropylene, and glass. Eleven lightweight concrete mixes were considered, These mixes comprised of; one plain concrete mix (without fibers), two reinforced concrete mixtures of mono fiber (hooked or straight fibers), six reinforced concrete mixtures of double hybrid fibers, and two reinforced concrete mixtures of triple hybrid fibers. Hardened concrete properties were investigated in this study. G</p> ... Show More
Publication Date
Tue Jun 01 2021
Journal Name
Iop Conf. Series: Materials Science And Engineering
Enhancing the mechanical properties of lightweight concrete using mono and hybrid fibers
...Show More Authors
Abstract<p>This investigation aims to study some properties of lightweight aggregate concrete reinforced by mono or hybrid fibers of different sizes and types. In this research, the considered lightweight aggregate was Light Expanded Clay Aggregate while the adopted fibers included hooked, straight, polypropylene, and glass. Eleven lightweight concrete mixes were considered, These mixes comprised of; one plain concrete mix (without fibers), two reinforced concrete mixtures of mono fiber (hooked or straight fibers), six reinforced concrete mixtures of double hybrid fibers, and two reinforced concrete mixtures of triple hybrid fibers. Hardened concrete properties were investigated in this study. G</p> ... Show More
Crossref (3)
Crossref