The current work concerns preparing cobalt manganese ferrite (Co0.2Mn0.8Fe2O4) and decorating it with polyaniline (PAni) for supercapacitor applications. The X-ray diffraction findings (XRD) manifested a broad peak of PAni and a cubic structure of cobalt manganese ferrite with crystal sizes between 21 nm. The pictures were taken with a field emission scanning electron microscope (FE-SEM), which evidenced that the PAni has nanofibers (NFs) structures, grain size 33 – 55 nm, according to the method of preparation, where the hydrothermal method was used. The magnetic measurements (VSM) that were conducted at room temperature showed that the samples had definite magnetic properties. Additionally, it was noted that the saturation magnetizatio

The rental activity receives "significant" interest from accounting organizations interested in issuing accounting standards worldwide, such as the Financial Accounting Standards Board (FASB), the International Accounting Standards Board (IASB). As leases represents an important source of finance for economic units as an alternative to financing assets through purchase or borrowing. Professional organizations have focused on addressing the situation of extra-budgetary funding through which the lessee hides many leases that are classified as financing without It shows in the budget, which gives an incorrect picture of the reality of the financial situation of economic unity, IASB has issued IFRS 16, which terminates off- Balance s

The purpose of my thesis is to prepare four new ligands (L1-L4) that have been ‎used to prepare a series of metal complexes by reacting them with metal ions:‎ ‎ M=(Mn(II), Co(II), Ni(II), Cu(II), Zn(II), Cd(II), Hg(II) ‎ ‎ Where succinyl chloride was used as a raw material for the preparation of ‎bi-dented ligands (L1-L4) by reacting it with potassium thiocyanate as a first ‎step and then reacting with (2-aminobenzothiazole, Benzylamine, 4-‎aminoantipyrine, Sulfamethoxazole) respectively as a second step with the use ‎of dry acetone as a solvent, the chemical formula of the four ligands prepared in ‎succession:‎ N1,N4-bis(benzo[d]thiazol-2-ylcarbamothioyl)succinamide (L1)‎ N1,N4-bis(benzylcarbamothioyl)succinami

The current research aims at identifying the new marketing directions that in the picture because if the changes and challenges that face the business nowadays, these effect on the future of the new product.

The problem of the research concentrate on the new marketing activities and how to make it appropriate between the product and the market's need, and to fulfill the needs and desire of the customer and it's importance for achieving the economical goals of the organization for a long relationship with the customer.

The resume of the research is about the impact of nowadays marketing and it's effect on knowing the customer instead of concentrating on the important roll of mark

Objective: The approximate life span of a silicone maxillofacial prosthesis is as short as1.5–2 years of clinical service, then a new prosthesis should be fabricated. The most common reasonfor re-making the prosthesis is silicone mechanical properties degradation. The aim of this studywas to assess some mechanical properties of VST-30 silicone for maxillofacial prostheses after addi-tion of intrinsic pigments.Methods: Two types of intrinsic pigments (rayon flocking and burnt sienna); each of them wasincorporated into silicone. One hundred and twenty samples were prepared and split into 4 groupsaccording to the conducted tests (tear strength, hardness, surface roughness, and tensile strengthand elongation percentage) with 30 samples for ea

Liquid membrane electrodes for the determination iron(III) were constructed based on chloramphenicol sodium succinate and iron(III) CPSS-Fe(III) as ion pair complex, with four plasticizers Di-butyl phosphate (DBP); Di-butyl phthalate (DBPH); Di-octyl phthalate (DOP); Tri-butyl phosphate (TBP); in PVC matrix . These electrodes give Nernstian and sub-Nernstian slopes (19.79, 24.60, 16.01 and 13.82mV/decade) and linear ranges from (1x10-5-1x10-2 M, 1x10-5-1x10-2 M, 1x10-6-1x10-2 M and 1x10-5-1x10-2 M) respectively. The best electrode was based on DBP plasticizer which gave a slope 19.79 mV/decade, correlation coefficient 0.9999, detection limit of 9×10-6 M, lifetime 37 day displayed good stability and reproducibility and used to determine

4,4'-(pyridine-2,6-diylbis(1,3,4-oxadiazole-5,2-diyl))bisphenol monomer (3)was synthesized from cyclization of N'2,N'6-bis(4-hydroxybenzylidene)pyridine-2,6-dicarbohydrazide (2)in the presence of bromine in glacialacetic acid. Newly five polymers (P1-P5) were synthesized from reaction bis-1,3,4-oxadiazole bisphenolmonomer with five different di acid chloride. The antibacterial activity of the synthesized polymers was screened against gram positive and gram negative bacteria. Polymers P4 and P5 exhibited significant antibacterial against all microorganisms, as well these polymers showed highest antifungal activity.