level of effectiveness of Glutathione - S - Transferees (GST), Glutathione peroxides (GPX),Malondialdehyde (MDA) the product of lipid peroxidation and some trace elements ( zinc,seleinum,iron ,copper ) had been measured in sera of (50) women with breast disease.which had been divided to : Control group (25),The first group (A) benign breast tumors (25),the second group (B) breast cancer (25). The results showed a clear moral high level of Glutathione - S - Transferees (GST), Glutathione peroxidase (GPX) , and Malondialdehyde (MDA) level in breast cancer group while a slight increase were observed in the levels of these enzymes and(MDA) in benign breast group. A significant reduction was evident in the levels of selenium and zinc

New 2-amino thiazole ,oxodiazole, sulphonilamide and diazin derivatives of N-(α-chloro aceto)-3-(tolyl imino)-5-bromo-2-oxo-indole(2) have been synthesized .The preparation process started by the reaction of 5-bromo isatin with  P-toluidine in the presence of glacial acetic acid and dimethylformamide(DMF) as a solvent to give  3-(tolyl imino)5-bromo-1H-indole-2-one.(1), Compound (1) with sodium hydride  in dimethylformamide(DMF) at 0C0 gave a suspension of the sodium salt of Schiff base derivative and subsequent reaction with monochloroacetylchloride obtained  the intermediate compound(2).Compound(2) was  reacted with different reagents  in four routes.The first route involved direct reaction with substituted  2-aminobenzothiazole u

BCl3 is toxic gas and its detection is of great importance. Thus, here, B3LYP, M06-2X, and B97D density functionals are utilized for probing the effect of decorating Zn, Cd, and Au on the sensing performance of an AlP nano-sheet (AlPNS) in detecting the BCl3. We predict that the interaction of pure AlPNS with BCl3 is physisorption, and the sensing response (SR) of AlPNS is approximately 9.2. The adsorption energy of BCl3 changes from −4.1 to −18.8, −19.1, and −19.5 kcal/mol by decorating the Zn, Cd, and Au metals into the AlPNS surface, respectively. Also, the corresponding SR meaningfully rises to 40.4, 59.0, and 80.9, indicating that by increasing the atomic number of metals, the sensitivity of metal decorated AlPNS (metal@AlPNS)

Abstract

In the present work, thermal diffusivity and heat capacity measurements have been investigated in temperature range between RT and 1473 K for different duplex stainless steel supplied by Outokumpu Stainless AB, Sweden. The purpose of this study is to get a reliable thermophysical data of these alloys and to study the effect of microstructure on the thermal diffusivity and heat capacity value. Results show the ferrite content in the duplex stainless steel increased with temperature at equilibrium state. On the other hand, ferrite content increased with increasing Cr/Ni ratio and there is no significant effect of ferrite content on the thermal diffusivity value at room temperature. Furthermore, the heat capacity of all sam

Copper tin sulfide (Cu2SnS3) thin films have been grown on glass
substrate with different thicknesses (500, 750 and 1000) nm by flash
thermal evaporation method after prepare its alloy from their
elements with high purity. The as-deposited films were annealed at
473 K for 1h. Compositional analysis was done using Energy
dispersive spectroscopy (EDS). The microstructure of CTS powder
examined by SEM and found that the large crystal grains are shown
clearly in images. XRD investigation revealed that the alloy was
polycrystalline nature and has cubic structure with preferred
orientation along (111) plane, while as deposited films of different
thickness have amorphous structure and converted to polycrystalline

In this work, yttrium oxide particles (powder) reinforced AL-Si matrix composites (Y2O3/Al-Si) and Chromium oxide particles reinforced AL-Si matrix composites (Cr2O3/AL-Si) were prepared by direct squeeze casting. The volume percentages of yttrium oxide used are (4, 8.1, 12.1, 16.1 vol %) and the volume percentages of the chromium oxide particles used are (3.1, 6.3, 9.4, 12.5 vol. %). The parameters affecting the preparation of Y2O3/Al-Si and Cr2O3/AL-Si composites by direct squeeze casting process were studied. The molten Al-Si alloy with yttrium oxide particles or with chromium oxide particles was stirred again using an electrical stirrer at speed 500 rpm  and the molten alloy was  poured  into the squeeze die cavity. Th