The present study was conducted to determine histopathological changes caused by chronic effect of Nitrofurantoin(NFT) in The albino mice Testes. The Study included 40 mice were divided on the five groups: the first group taken distilled water and become control group . the remaining group which are exposure with NFT drug in concentration (100-150-200-250) mg / kg, respectively, Doses were given orally for a period (month and two months). The results of histopathological changes included occurrence of congestion in the blood vessel and degeneration of spermatogonia and aggregation of spermatids in the lumen of semineferous tubules and inhibition of spermatogensis process and decrease of sperm inside the lumen

Corrosion resistance of metals is one of the most important topics for researchers. In this work, epoxy-TiO2 nanocomposite has been developed for protection of 6061AL alloy. The dip-coating technique used to deposit the coating on 6061 Al alloy substrate. Different concentrations of TiO2 NPs (1,3,5 )Wt% have been used to study the corrosion behavior in 3.5% NaCl medium. Also, 200,150 and 100 mm/min dipping speeds have been employed for 1%wt TiO2 to show their effects on coating layer and corrosion rate. Characterization of coated surfaces were investigated by AFM, FESEM andEDS,while theelectrochemical measurementswas using to evaluate protective nature of the coating. The results have shown that the corrosion rate has decreased with

Abstract

                The aim of the research is to demonstrate the impact of long-term investment on profitability, and in order to achieve this goal, long-term investment was chosen, represented by (the ratio of long-term investments to total investments, the ratio of long-term investment to the total (deposits) as independent variables, and studying its impact on the dependent variable, which is profitability as measured by the rate of return on investments, the rate of return on equity. In order to reach the results, the inductive approach and the analytical descriptive approach were used, and the research found a significant impac

Objective: Using green chemistry, an effective, inexpensive, and environmentally safe method, sulfur nanoparticles with specific properties can be prepared and used in nanotechnology. This research aimed to prepare sulfur nanoparticles from chilli pepper extract and determine their effectiveness against colon cancer. Method: Chilli pepper extract obtained from local markets was treated with aqueous sodium thiosulfate (Na2S2O7.5H2O). After mixing, it was continuously stirred, heated, and filtered. NaBH4 was then added, resulting in a yellow precipitate. The precipitate was centrifuged, purified, and dried at 250°C. Results: Standardised tests such as UV-Vis, XRD, SEM, TEM, AFM, and EDX were used, resulting in sulfur nanoparticles with an av

Metal and metal oxide NPs have shown to be perfectly synthesized by using plant extracts with high efficiency, low cost and low toxicity. Our goal was to synthesize ZnO NPs by using an extract of pomegranate seeds and investigate the anticorrosion, antimicrobial and antioxidant properties of the synthesized ZnO NPs. The results have shown that the use of pomegranate in the green synthesis of ZnO NPs gave a good yield, with a low cost and non-toxic approach. The electrophoretic deposition (EPD) was used to coat stainless steel (S.S) by synthesized ZnO NPs in an alcoholic solution at room temperature producing a good coating against corrosion. The corrosion properties were investigated in a saline solution and a temperature range of (293–32

The catalytic cracking of three feeds of extract lubricating oil, that produced as a by-product from the process of furfural extraction of lubricating oil base stock in AL-Dura refinery at different operating condition, were carried out at a fixed bed laboratory reactor. The initial boiling point for these feeds was 140 ºC for sample (1), 86 ºC for sample (2) and 80 ºC for sample (3). The catalytic cracking processes were carried out at temperature range 325-400 ºC and initially at atmospheric pressure after 30 minutes over 9.88 % HY-zeolite catalyst load. The comparison between the conversion at different operating conditions of catalytic cracking processes indicates that a high yield was obtained at 375°C, according to gasoline pr

This work deals with thermal cracking of three samples of extract lubricating oil produced as a by-product from furfural extraction process of lubricating oil base stock in AL-Dura refinery. The thermal cracking processes were carried out at a temperature range of 325-400 ºC and atmospheric pressure by batch laboratory reactor. The distillation of cracking liquid products was achieved by general ASTM distillation (ASTM D -86) for separation of gasoline fraction up to 220 ºC from light cycle oil fraction above 220 ºC. The comparison between the conversions at different operating conditions of thermal cracking processes indicates that a high conversion was obtained at 375°C, according to gasoline production. According to gasoline produ