This experiment was conducted to study the effect of injecting hatching eggs into a flock of broiler aged mothers with different concentrations of the alcoholic extract of Moringa oleifera powder on productive performance of broilers during the period of rearing of 35 days. The study included two experiments for a period at 2/10/2021 to 28/11/2021, where eggs were injected into the Mustafa Poultry Hatchery/ Wasit Governorate- Aziziyah District. A 400 hatching eggs of 308 Ross mothers of modern broilers used at age of 48 week, eggs of average weight 66 ± 1 g/egg were collected in same day then stored for two days. A quarter of treatments were randomly distributed with 100 eggs for each treatment. The first treatment T1 without injection as control treatment, and T4, T3, and T2 (while injected into the space air) on day 12 of, in an amount of 0.2 mL for each egg, with concentration of 450, 300, 150 µg/mL, respectively. The hatched chicks were bred in the same fields, where 180 chicks of the chicks were distributed into four treatments, 45 chicks for each treated and three replicates (15 chicks) for each T1, T2, T3 and T4 were placed in a cage for 35 days. The results Showed A significant (p<0.05) increase for T4 compared to the control in body weight, body weight gain and relative weight of the gizzard, will all injection treatment recorded a highly significant decrease in the total feed consumption and feed conversion ratio compared to control treatment. While there were no significant differences between treatments in the percentage of total Mortality, relative weights of the heart, liver, breast and thighs and dressing ratio.
Background: The main drawback of soft lining materials was that they debonded from the denture base after a certain period of usage. Therefore, the purpose of this research was to determine the impact of oxygen and argon plasma treatment on the shear bonding strength of soft liners to two different kinds of denture base materials: conventional acrylic resin and high impact acrylic resin. Materials and Methods: Heat cure conventional and high impact acrylic blocks (40 for each group) were prepared. A soft liner connected the final test specimen of two blocks of each acrylic material. Shear bond strength (SBS) was assessed using universal testing machine. Additional blocks were also prepared for analyzing Vickers microhardness, contact ang
... Show More
(14)
(4)
In this research, the study effect of irradiation on structural and optical properties of thin film (CdO) by spray pyrolysis method, which deposited on glasses substrates at a thickness of (350±20)nm , The flow rate of solution was 5 ml/min and the substrate temperature was held constant at 400˚C.The investigation of (XRD) indicates that the (CdO) films are polycrystalline and type of cubic. The results of the measuring of each sample from grain size, micro strain, dislocation density and number of crystals the grain size decreasing after irradiation with gamma ray from(27.41, 26.29 ,23.63)nm . The absorbance and transmittance spectra have been recorded in the wavelength range (300-1100) nm in order to study the optical properties. the op
... Show MoreBackground: Orthodontic force is considered to stimulate cells in the periodontium to release many mediators such as cytokines which play a responsible role for periodontal and alveolar bone remodeling, bone resorption and new bone deposition. Aim of this study was carried out to estimate changes of the (interleukin-one beta, tumor necrosis factor – alpha and C-reactive protein) levels in unstimulated whole saliva during the leveling stage of orthodontic tooth movement. Materials and methods: The sample consisted of thirty adult patients (12 males and 18 females) with ages ranges (19-23) years. Each sample had Class I and Class II malocclusion dental classification and required bilateral extraction of their maxillary first premolars, und
... Show MoreTwo field experiments were conducted during the spring seasons of 2000,2001.The aim was to study the effect of hardening to drought tolerance on moisture percentage in root and stem of sunflower plant during growth stages . Asplit-split plots design was used with three replications.The main plots included irrigation treatments:irrigation to100%(full irrigation),75and50%of available soil water.The sub plots were the cultivars Euroflor and Flame.The sub-sub plots represented four seed soaking treatments :Control(unsoaked),soaking in water ,Paclobutrazol solution(250ppm),and Pix solution(500ppm). The soaking continued for 24 hours then seeds were dried at room temperature until they regained their original weight. Amount of water
... Show More
A thin CdS Films have been evaporated by thermal evaporation technique with different thicknesses (500, 1000, 1500 and 2000Å) and different duration times of annealing (60, 120 180 minutes) under 573 K annealing temperature, the vacuum was about 8 × 10-5 mbar and substrate temperature was 423 K. The structural properties of the films have been studied by X- ray diffraction technique (XRD). The crystal growth became stronger and more oriented as the film thickness (T) and duration time of annealing ( Ta) increases.
Copper oxide thin films were deposited on glass substrate using Successive Ionic Layer Adsorption and Reaction (SILAR) method at room temperature. The thickness of the thin films was around 0.43?m.Copper oxide thin films were annealed in air at (200, 300 and 400°C for 45min.The film structure properties were characterized by x-ray diffraction (XRD). XRD patterns indicated the presence of polycrystalline CuO. The average grain size is calculated from the X-rays pattern, it is found that the grain size increased with increasing annealing temperature. Optical transmitter microscope (OTM) and atomic force microscope (AFM) was also used. Direct band gap values of 2.2 eV for an annealed sample and (2, 1.5, 1.4) eV at 200, 300,400oC respect
... Show More
(1)
A field experiment was conducted in the growth season 2019-2020 at the botanical garden of the Biology Department at the College of Education for Pure Sciences/Ibn Al-Haitham, University of Baghdad-Iraq. The experiments’ purpose is to determine the effects of different melatonin concentrations on some morphological and physiological characteristics of mung (Vigna radiata L.) plant under the influence of three periods of drought (5, 10, 15 days). The results were showed that the increasing of water stress periods had significant effects in the reducing rates of the studied characteristics, especially at the period 15 days. The external treatment of different concentrations of melatonin reduced the drought effects and that’s led to signif
... Show MoreObjective(s): The world of dentistry is constantly evolving, and with the advent of 3D printing technology, the possibilities are endless. However, little is known about the effects of adding ZrO2 NPs to the denture base resin of 3D additive manufacturing technique.Aim of this study is to evaluate the behavior of resin which is used to 3D printing of denture base with the addition of ZrO2 NPs on denture adaptation property and diametral compression strength.Methods: 60 samples were printed, 30 disks for diametral compressive test and 30 denture base for denture adaptation test. Three groups per test (n=10). The control group for each test included unreinforced 3Dprinted denture base resin, and the other groups were reinforced with (2&
... Show MoreObjective: The aim of this study was to evaluate the effect of pumice, burning investment material
and black sand on the surface roughness of heat cure acrylic resin.
Methodology: Sixty specimens were prepared from pink heat cure acrylic resin, the specimens
where grouped into; 20 specimens which polished with pumice and water (control group); 20
specimens which polished with investment material (after burning it) and water; and 20 specimens
which polished with black sand and water. The average surface roughness of specimens after
polishing procedure had been determined by profilometer (surface roughness tester).
Results: Through the application of ANOVA and LSD tests, the result of this study showed that there
wa
PVC/Kaolinite composites were prepared by the melt intercalation method. Mechanical properties, thermal properties, flammability and water absorption percentage of prepared samples were tested. Mechanical characteristic such as tensile strength, elongation at break; hardness and impact strength (charpy type) were measured for all samples. It was found that the tensile strength and elongation at break of PVC composites decreased with increasing kaolinite loading. Also, the hardness of the composites increases with increase in filler content .The impact strength of the composites at the beginning increases at lower kaolinite loadings is due to the lack of kaolin adhesion to the matrix. However, at higher kaolin loadings. This severe agglom
... Show More