Objectives To tailor composites of polyethylene–hydroxyapatite to function as a new intracanal post for the restoration of endodontically treated teeth (ETT). Methods Silanated hydroxyapatite (HA) and zirconium dioxide (ZrO2) filled low-density polyethylene (LDPE) composites were fabricated by a melt extrusion process and characterised using infrared spectroscopy (FTIR), differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). The flexural strength and modulus were determined in dry state and post ageing in simulated body fluid and fractured surfaces analysed by SEM. The water uptake and radiographic appearance of the experimental composites were also measured and compared with a commercially known endodontic fibre

        New derivatives of thiosemicarbazide were synthesized by reaction of different aromatic aldehydes and ketones with thiosemicarbazide to give schiff-bases 1(a-d) . schiff-bases have been used for synthesized the thioimidazolidine 2(a-d)  by reaction of schiff-bases with ethyl chloroacetatein in presence of anhydrous sodium acetate that transformed part of it in to Beta-lactam 3(a-b) compounds with phenyl acetic acid and thionyl chloride , The compounds 4(a-b) came from the reactor of 4-bromobenzaldehyde with compounds 2(a-b) , as well as reaction of compounds 2(b-d) with methyl iodide and anhydrous potassium carbonate to give 5 (b-d) , then added  hydrazine hydrate formed 6(b-d) , then

    The aim of study was to  assess water stress for 2,8,14 days and spraying selenium at 0,10,20 mg/L-1 and brassinolide 0,1,2 mg/L-1 on vegetative growth and macro elements content (NPK) for Coriander (Coriandrum astivum L.) plant, The experiment was performed with Factorial Randomized Block Design (R.B.C.D) with three replicates .The results were summarized as follows: 1- The period of sever water stress for 14 days was passive effect on growth parameters. 2-  The means of elements content  NPK content  was increased at moderate stress for 8 days. 3- The effect of selenium and brassinolide was positively to increase studied parameters. 4- Selenium and Brassinolide decreased water stress also the triple in

This article includes designed and synthesized for bent-shaped liquid crystal molecules starting from 5,5-diethylpyrimidine-2,4,6(1H,3H,5H)-trione and two moles of chloroacetylchloride in N, N-dimethyl formamide (DMF) and triethylamine (TEA) to product compound [I] ,then reacted the later compound with two moles of 4-hydroxybenzonitrile to yield nitrile compound [II]. Likewise, reaction 5,5-diethylpyrimidine-2,4,6(1H,3H,5H)-trione and two moles of ethylchloroacetate with fused sodium acetate in ethanol to create an ester compound [III], and then the later compound was reacted with two moles of hydrazine hydrate in ethanol to obtained hydrazide acid compound [IV]. After that, the compound [IV] reacted with two moles of ethyl acetoacetate in

The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

Ceramic coating compose from a ceramic mixture (MgO, Al₂O₃) and metall (Al-Ni) were produced by Thermal Spray Technique. The mixed ratio of used materials Al:Ni (50%) and 40% of Al₂O₃ and 10% MgO. This mixture was spray on a stainless steel substrate of type (316 L) by using thermal spray with flame method and at spraying distances (8, 12, 16 and 20) cm, then the prepared films were treated by laser and thermal treatment. After that performing a hardness and adhesion tests were eximined. The present study shows that the best value of the thermal treatment is 1000 ℃ for 30 mint; the optimum spray distance is 12 cm and most suitable laser is 500 mJ where the microscopic and mechanical character