Background:Nocturnal Enuresis is a common problem affecting 20% of five years old children and up to 2% of adolescent and young adult. Although it is a self limiting benign condition, it has social and psychological impact on the child and his family. Many pathophysiological theories had been suggested, but none is confirmed. Hypercalciuria has been suggested to be associated with higher incidence of nocturnal enuresis. Objectives:The aim of our study to test the value of Ca/Cr ratio, on random urine sample, in diagnosing hypercalciuria in enuretic children. Type of study: Cross sectional study.Methods:Forty four enuretic children were enrolled in this study and forty five children without nocturnal enuresis were taken as control group. Results:The prevalence of abnormal Ca/Cr ratio was higher among enuretic children when compared with control group; the result was statistically significant (P. value0.002). Among the enuretic children, higher Ca/ Cr ratio was statisticallyassociated with urinary symptoms, abnormal general urine examination, and positive family history. Nosuch association was found with the gender or frequency of bed wetting per week. Conclusions:the results of this study suggest that hypercalciuria has a significant association with NE, rendering routine screening of hypercalciuria by Ca/Cr ratio on a random urine sample, is reasonable. Furthermore, a large scale studies are needed to confirm the role of low calcium diet, and other measures in treatment of idiopathic hypercalciuria, in the management of enuretic children with abnormal Ca/Cr ratio
This study aimed to study the inhibition activity of purified bacteriocin produced from the local isolation Lactococcuslactis ssp. lactis against pathogenic bacteria species isolated from clinical samples in some hospitals Baghdad city. Screening of L. lactis ssp. Lactis and isolated from the intestines fish and raw milk was performed in well diffusion method. The results showed that L. lactis ssp. lactis (Lc4) was the most efficient isolate in producing the bacteriocin as well observed inhibitory activity the increased that companied with the concentration, the concentration of the twice filtrate was better in obtaining higher inhibition diameters compared to the one-fold concentration. The concentrate
... Show MoreThe current work concerns preparing cobalt manganese ferrite (Co0.2Mn0.8Fe2O4) and decorating it with polyaniline (PAni) for supercapacitor applications. The X-ray diffraction findings (XRD) manifested a broad peak of PAni and a cubic structure of cobalt manganese ferrite with crystal sizes between 21 nm. The pictures were taken with a field emission scanning electron microscope (FE-SEM), which evidenced that the PAni has nanofibers (NFs) structures, grain size 33 – 55 nm, according to the method of preparation, where the hydrothermal method was used. The magnetic measurements (VSM) that were conducted at room temperature showed that the samples had definite magnetic properties. Additionally, it was noted that the saturation magnetizatio
... Show More
(1)
(1)
The existing investigation explains the consequence of irradiation of violet laser on the structure properties of MawsoniteCu6Fe2SnS8 [CFTS] thin films. The film was equipped by the utilization of semi-computerized spray pyrolysis technique (SCSPT), it is the first time that this technique is used in the preparation and irradiation using a laser. when the received films were processed by continuous red laser (700 nm) with power (>1000mW) for different laser irradiation time using different number of times a laser scan (0, 6, 9, 12, 15 and 18 times) with total irradiation time (0,30,45,60,75,90 min) respectively at room temperature.. The XRD diffraction gave polycrysta
... Show More
(3)
(6)
(6)
Copper zinc tin sulfide selenide, Cu2 ZnSn(S1−x Se x)4 , absorbers are promising earth-abundant and environmentally benign materials for low-cost photovoltaic applications. This study investigates the structural and optical properties of Cu 2 ZnSn(S1−x Se x)4 nanostructured thin films prepared by pulsed laser deposition using melt-quenched targets with selenium compositions x = 0.0–1.0. X-ray diffraction revealed that films with low selenium content remained amorphous, whereas higher selenium incorporation promoted the formation of polycrystalline kesterite–stannite phases with preferred orientations along (112), (200), (220), and (312). The crystallite size increased from 12.3 to 17.9 nm as selenium reached x = 1.0, indicating enha