In the drilling and production operations, the effectiveness of cementing jobs is crucial for efficient progress. The compressive strength of oil well cement is a key characteristic that reflects its ability to withstand forceful conditions over time. This study evaluates and improves the compressive strength and thickening time of Iraqi oil well cement class G from Babylon cement factory using two types of additives (Nano Alumina and Synthetic Fiber) to comply with the American Petroleum Institute (API) specifications. The additives were used in different proportions, and a set of samples was prepared under different conditions. Compressive strength and thickening time measurements were taken under different conditions. The amoun

Background: The main drawback of soft lining materials was that they debonded from the denture base after a certain period of usage. Therefore, the purpose of this research was to determine the impact of oxygen and argon plasma treatment on the shear bonding strength of soft liners to two different kinds of denture base materials: conventional acrylic resin and high impact acrylic resin. Materials and Methods: Heat cure conventional and high impact acrylic blocks (40 for each group) were prepared. A soft liner connected the final test specimen of two blocks of each acrylic material. Shear bond strength (SBS) was assessed using universal testing machine. Additional blocks were also prepared for analyzing Vickers microhardness, contact ang

Two series of 1,3,4-oxadiazole derivatives at the sixth position of the 2,4-di-tert-butylphenol group were synthesized.

A series of 4-(methylsulfonyl)aniline derivatives were synthesized in order to obtain new compounds as a potential anti-inflammatory agents with expected selectivity against COX-2 enzyme. In vivo acute anti-inflammatory activity of the final compounds 11–14 was evaluated in rat using an egg-white induced edema model of inflammation in a dose equivalent to 3 mg/Kg of diclofenac sodium. All tested compounds produced significant reduction of paw edema with respect to the effect of propylene glycol 50% v/v (control group). Moreover, the activity of compounds 11 and 14 was significantly higher than that of diclofenac sodium (at 3 mg/Kg) in the 120–300 minute time interval, while compound 12 expressed a comparable effect to that of di

Laboratory model tests were performed to investigate the behavior of shallow and inclined skirted foundations placed on sandy soil with R.D%=30 and the extent of the impact of the positive and negative eccentric-inclined loading effect on them. To achieve the experimental tests, it was used a box of (600×600) mm cross-sectional and 600mm in height and a square footing of (50*50) mm and 10 mm in thickness attached to the skirt with Ds=0.5B and various an angle of (10°, 20°, 30°). The results showed that using skirts leads to a significant improvement in load-carrying capacity and decreased settlement. In addition, when the skirt angle increased, the ultimate load improved. Load-carrying capacity decreased with increasing eccentri

The photooxidative degradation process of plastics caused by ultraviolet irradiation leads to bond breaking, crosslinking, the elimination of volatiles, formation of free radicals, and decreases in weight and molecular weight. Photodegradation deteriorates both the mechanical and physical properties of plastics and affects their predicted life use, in particular for applications in harsh environments. Plastics have many benefits, while on the other hand, they have numerous disadvantages, such as photodegradation and photooxidation in harsh environments and the release of toxic substances due to the leaching of some components, which have a negative effect on living organisms. Therefore, attention is paid to the design and use of saf