Shrinkage Properties of Insulator Ceramic Body Porcelain Formed Using Local Material
...Show More Authors

   This work was carried out to investigate the shrinkage properties of insulator ceramic body, and the effect of changing the ratio of concentration of electrolyte solution on these properties. The electrical insulator body was prepared by using Iraqi local materials. These are :- kaolin Duakhla, Arudhuma Sand glass, and potash feldspar with weight percentage (45%, 25%,and 30%) respectively. The processes of milling, classification, mixing, forming and firing, through the process of mixing electrolyte solution and mineralizer were added at different concentrations for electrolyte solution, (1%, 0.7%, 0.5%, 0.2%, and 0.1%).  The electrolyte solution was prepared by mixing sodium carbonate and sodium silicate by (2:1) ratio, while the mineralize, Zinc Oxide, was added at fixed weight percentage.      The measurements were undertaken on rectangular sample burnt at sintering temperatures of (1250, 1300,and 1350) oC. The result was obtained at  (0.5%) electrolyte solution concentration has highest total shrinkage at (1300,1350) oC sintering temperature and also highest firing shrinkage .So that, it is the best concentration to get material property of insulating

View Publication Preview PDF
Quick Preview PDF
Publication Date
Sun Mar 30 2008
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Preparation of Polyvinyl Alcohol from Local Raw Material
...Show More Authors

Polyvinyl alcohol, (PVA) was prepared using polyvinyl acetate emulsion (manufactured by Al-Jihad factory,
That-Al-Sawary Company) as a local raw material. In this investigation, polyvinyl acetate emulsion was converted to
solid form by coagulation the polymer from its emulsion using sodium sulphate salt as coagulant aid, then alcoholyzed
the solid polyvinyl acetate in methanol using sodium hydroxide as catalyst, polyvinyl alcohol produced by this method is
a dry, white to yellow powder.
Three affecting variables on the degree of hydrolysis of PVA were studied, these variable are Catalyst to
polymer weight ratio in the range of 0.01 – 0.06, reaction time in the range of 20 – 90 min, and reaction temperature in
the

... Show More
View Publication Preview PDF
Publication Date
Sat Feb 13 2021
Journal Name
Journal Of Lasers In Medical Sciences
Effects of Different Laser Treatments on Some Properties of the Zirconia-Porcelain Interface
...Show More Authors

Introduction: This study was performed to compare the effect of Fractional CO2 laser or Q switched Nd:YAG laser of surface treatment on the shear bond strength of zirconia-porcelain interface. Methods: Fractional CO2 laser at 30 W, 2 ms, time interval 1 ms, distance between spots 0.3 mm, and number of scans is (4) or Q switched Nd:YAG laser at 30 J/mm2 and 10 Hz were used to assess the shear bond strength of zirconia to porcelain. Pre-sintered zirconia specimens were divided into three groups (n = 10) according to the surface treatment technique used: (a) untreated (Control) group; (b) CO2 group; (c) Nd:YAG group. All samples were then sintered and veneered with porcelain according to the manufacturer’s instructions. Surface morph

... Show More
View Publication
Scopus (9)
Crossref (6)
Scopus Clarivate Crossref
Publication Date
Sat Aug 01 2020
Journal Name
Journal Of Engineering Science And Technology
Using sustainable material in improvement the geotechnical properties of soft clayey soil
...Show More Authors

Preview PDF
Scopus (38)
Scopus
Publication Date
Wed Jul 01 2015
Journal Name
Journal Of Engineering
Studying of Some Mechanical Properties of Reactive Powder Concrete Using Local Materials
...Show More Authors

This research aims to investigate and evaluate a reactive powder concrete (RPC) cast using economical materials. Its mechanical properties were investigated and evaluated by studying the effects of using different cement and silica fume contents and locally steel fibers aspect ratios as reinforcement for this concrete. A compressive strength of about 155.2MPa, indirect tensile strength of 16.0MPa, modulus of elasticity of 48.7GPa, flexural strength of 43.5MPa, impact energy of 3294.4kN.m and abrasion loss 0.59%  have been achieved for reinforced RPC contains  910 kg/m3 cement content, silica fume content 185 kg/m3 of cement weight and fiber volume fraction 2%. The water absorption values w

... Show More
View Publication Preview PDF
Publication Date
Tue Jan 31 2017
Journal Name
Journal Of Engineering
Studying the Adsorption of Lead from aqueous Solution using Local Adsorbent Material Produced from Waste Tires by Pyrolysis
...Show More Authors

In this research a local adsorbent was prepared from waste tires using two-step pyrolysis method. In the carbonization process, nitrogen gas flow rate was 0.2L/min at carbonization temperature of 500ºC for 1h. The char products were then preceded to the activation process at 850°C under carbon dioxide (CO2) activation flow rate of 0.6L/min for 3h. The activation method produced local adsorbent material with a surface area and total pore volume as high as 118.59m2 /g and 0.1467cm3/g, respectively. The produced . local adsorbent (activated carbon) was used for adsorption of lead from aqueous solution. The continuous fixed bed column experiments were conducted. The adsorption capacity performance of prepared activated carbons in this work

... Show More
View Publication Preview PDF
Publication Date
Sun Apr 30 2017
Journal Name
Journal Of Engineering
Compatibility between Hydraulic and Mechanical Properties of Ceramic Water Filters
...Show More Authors

In this paper, ceramic water filters were produced by using ten mixtures of different ratios of red clay and sawdust under different production conditions. The physical properties of these filters were tested. The production conditions include five press pressures ranged from 10 to 50MPa and a firing schedule having three different final temperatures of 1000, 1070, and 1100˚C. The tests results of the physical properties were used to obtain best compatibility between the hydraulic and the mechanical properties of these filters. Results showed that as the press pressure and the firing temperature are increased, the bulk density and the compressive and bending strengths of the produced filters are increased, while, the porosity and absorp

... Show More
View Publication Preview PDF
Publication Date
Mon Apr 20 2020
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Measurement of Radioactivity in Some Commercial Porcelain Samples by Using HPGe Detector
...Show More Authors

     Estimations of specific activity concentrations in eight commercial porcelain tiles made in different countries were performed by the use of HPGe detector. We have found that the highest specific activity concentrations for 238U, 40K were equal to (21.120 Bq/kg) and (283.862 Bq/kg) respectively, Iranian origin, while the highest specific activity concentration for 232Th was found to be equal to (29.292 Bq/kg), Iraqi origin; all of which were less than their corresponding recommended values given by (UNSCEAR, 2000). The radiation hazard indices [IÉ£ , Hin ,Hex , Raeq ,DÆ” , (AEDE) in and (AEDE) out] w

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Thu May 25 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Numerical Estimation of Some Properties of Magnesium Aluminum Silicate Glass Ceramic
...Show More Authors

Magnesium aluminum silicate of glass ceramic having different amounts of magnesium fluoride in the range (0-13.2)%. Thermal expansion coefficient and micro hardness of the base glass and glass ceramic samples are seen to be interdependent but due to the multi – component system, the behaviour is seen to be somewhat complex, with an increase in Mg F2 content. The thermal expansion coefficient increase and micro harness decrease, numerical simulation of thermal expansion and hardness is useful in this study, L2 – regression is used to calculate the two parameters associated with each glass component, by comparing the measured parameters and the calculated parameters ,it is useful to use such a method to calculate the quantity

... Show More
View Publication Preview PDF
Publication Date
Sun Sep 24 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Using The Ultrasonic Waves For Studying Thermal And Elastic Properties as a Function of Porosity in Sintered ceramic
...Show More Authors

Ultrasonic pulse echo measurements on porous alumina as ceramic

material with porosities ranging from (20-40)% showed effect of volume

fraction of porosity on both thermal and elastic properties. A quadratic relationships, by using a least squares method, is deduced for the dependence of the shear velocity, longitudinal velocity, shear modulus, Young's modulus,  bulk  modulus, Poisson 's ratio, Debye temperature, specific heat, and thermal conductivity on the total  porosity. By these relationships,  the  thermal  and  elastic  properties  results  of  pore-free alumina  were  calculated.  The  elastic  properties  results  of  

... Show More
View Publication Preview PDF
Publication Date
Sat Oct 01 2022
Journal Name
Nuclear Instruments And Methods In Physics Research Section B: Beam Interactions With Materials And Atoms
Shielding properties and buildup factor of Al2O3/PbO-based ceramic materials