In the present work effect of recycled heating and cooling on the values of concrete compressive strength due to high temperature of 400⁰C was studied.

    The tests show that the percent of reduction in compressive strength of the samples which exposed to a temperature of 400⁰C for one cycle was 32.5%, while the reduction was 52.7% for the samples which were exposed to recycled heating and cooling of ten times .      

   Moreover a study of the effect of specimen sizes on the percentages of compressive strength reduction due to high temperature

This research presents a new study in kinetics under reactive distillation by using consecutive two – step reaction : the saponification reaction of diethyl adipate with sodium hydroxide solution . The distillation process takes the role of withdrawing the intermediate product (sodium monoethyladipate SMA) which otherwise converts to the final product of low purity.The effect of three parameters were studied through a design of experiments applying 2³ factorial design. These parameters were : the mole ratio of DA to NaOH solution (0.1 and 1) , NaOH solution concentration (3 N and 8 N) , and batch time (1.5 hr. and 3.5 hr.) . The conversion of DA to sodium monoethyladipate(SMA)(intermediate product) was the effect of these pa

In the present work, the surface properties of mixed binary surfactants containing sodium dodecylbenzene sulfate (SDBS) and Tween 80 (TW80) surfactants in aqueous solutions were studied at temperature 293 K using surface tension measurements. The critical micelle concentration (cmc) magnitude for both individual surfactants and their mixtures were established the obtained results revealed  that the magnitude of cmc of the mixtures are less than the magnitude of individual surfactants and decrease with the increase in Tween 80 percent in solution which indicate the nonideal  mixing of the two surfactants. The values of molecular interaction parameters  and the mole fraction of surfactants in the micelle (X1) were calculated

Nigella sativa seeds (NSS) are reputed traditionally and scientifically as a potent agent that promote milk secretion (galactagogue), but their mechanism of action is studied trivially. One suggestion was that these seeds are bio-transformed to sex hormones within the ovaries. Therefore, this investigation was designated to throw light on the action of these seeds in the absence of ovaries i.e. in male rats. Thirty Norway male albino rats were used in this investigation. They were divided into experimental (n=20,fed NSS 2g/ Kg body weight /day for 14 days) and control (n=10, fed placebo for 14 days). After sacrifice mammary gland and blood samples were obtained. Experimental rats revealed a significant increase (p (0.01>in

 Lighting is a very important element of treatment if the color contains many imaging system (digital cameras) and the unit of light and the light within these units are not strong , but usefel when the light is low , in different lighting intensities conditions image quality will not persist good enough and image may become dark or slightly exposed to light which leads to lower the details in image where we can not modify contrast or light ness to compensate thr decrease without losing the light and dark deatials . So we went in this research to study the variation colored texts written on the painting and lighting cases of non –regular ( a few) and different distances . As the diversity of these texts written on the board a

Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f