The Study of Wear Effect on the Unsaturated Resin Reinforced By Rice Husk
...Show More Authors

This study was performed by using the unsaturated polyester resin as matrix to the
composite materials with the rice husk as reinforced materials . The research included study
of wear test on the composite material The results show that the, wear is increased with the
increase of applied load and distance slipping and also with time increase . moreover the
shows that the higher value wear rate( 1.91gm/cm) from the load (20) N and the higher value
wear rate (1.43gm/cm) from the higher distance (4cm) and from the higher time (6min) higher
wear rate (5.33gm/cm).

View Publication Preview PDF
Quick Preview PDF
Publication Date
Tue Mar 15 2022
Journal Name
Journal Of Baghdad College Of Dentistry
Effect of Resin Infiltration and Microabrasion on the Microhardness of the Artificial White Spot Lesions (An in Vitro Study)
...Show More Authors

Crossref (3)
Crossref
Publication Date
Wed Mar 12 2025
Journal Name
Journal Of Baghdad College Of Dentistry
Effect of poly propylene fibers incorporation and their oxygen plasma treatment on tensile strength, wettability and wear resistance of heat cure denture base acrylic resin
...Show More Authors

Background: Recently, Poly propylene fibers with and without plasma treatment have been used to reinforce heat cure denture base acrylic but, so far some of properties like tensile strength , wettability and wear resistance not evaluated yet, the aim of the study is to clarify the influence of incorporation of treated and untreated fibers on these properties. Materials and methods: Twenty one specimens were fabricated for every tested property(tensile strength, wear resistance and wettability) that classified into three groups(control, untreated poly propylene fibers reinforced specimens and Oxygen plasma treated group)and for each test sevens amples were used(n=7). Tensile strength was tested using Instron universal testing machine, wear

... Show More
View Publication Preview PDF
Publication Date
Tue Nov 01 2022
Journal Name
Journal Of Engineering
Study The Impact of Geopolymer Mortar Reinforced by Micro Steel Fibers
...Show More Authors

In this research, geopolymer mortar had to be designed with 50% to 50% slag and fly ash with and without 1% micro steel fiber at curing temperature of 240℃. The molarity of alkaline solution adjusted with 12 molar sodium hydroxid to sodium silicate was 2 to 1, reaspectivly. The heat of curing increased the geopolymerization proceses of geoplymer mortar, which led to increasing strength, giving the best result and early curing age. The heat was applied for two days by four hours each day. It was discovered in the impact test that the value first crack of each mix was somewhat similar, but the failure increased 72%  for the mixture that did not contain fiber. For the energy observation results it was shown that the mixt

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sun Jun 03 2012
Journal Name
Baghdad Science Journal
Mechanical properties of carbon nanotube reinforced Epoxy Resin composites
...Show More Authors

Overlapped have been prepared from epoxy resin material added to carbon Nanotube and percentages weight (0.1, 0.05, 0.01) % Studied the mechanical properties of the composite (bending, tensile an d hardness) has been found that the Flexural and tensile modulus of the composites were higher than the pure epoxy resin this may be due to the high mechanical strength of carbon nano tube (CNT). The hardness of the epoxy carbon Nanotube composites increased and the reason is due to increased overlap and stacking between the additives and material basis, which reduces the movement of polymer molecules leading to increased resistance to scratching material and cutting, will become more resistance to plastic deformation.

View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Mon Nov 01 2010
Journal Name
Iraqi Journal Of Physics
The Effect of metals as Additives on Thermal conductivity of Epoxy Resin
...Show More Authors

A hand lay-up method was used to prepare Epoxy/ metal composites. Epoxy resin (EP) was used as a matrix with metal particles (Al, Cu, and Fe) as fillers.
The preparation method includes preparing square panels of composites with different weight percentage of fillers (10, 20, 30, 40, and 50%). Standard specimens (88mm in diameter) for thermal conductivity tests were prepared to measure thermal conductivity kexp.The result of experimental thermal conductivity kexp, for EP/metal composites show that, kexp increase with increasing weight percentage, For EP/ Al and EP/Cu composites, and it have have maximum values of 0.33 and 0.35 W/m.K, respectively. While kexp for EP/ Fe composite show slight increase with maximum value of 0.186 W/m.K.

... Show More
View Publication Preview PDF
Publication Date
Wed Dec 30 2009
Journal Name
Iraqi Journal Of Physics
Effect of Nanocomposites TiO2 addition on the Dielectric Properties of Epoxy resin
...Show More Authors

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.
Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

View Publication Preview PDF
Publication Date
Sat Oct 01 2011
Journal Name
Iraqi Journal Of Physics
The Effect of metals as additives on adhesion properties of epoxy resin
...Show More Authors

EP/ metal composites were prepared as adhesives between two steel rods. Epoxy resin (EP) was used as a matrix with metal as fillers (Al, Cu, Fe,).
The preparation method for tensile adhesion tests includes two steel rods with adhesive composites between the rods to measure adhesion strength Sad and adhesion toughness Gad.
Results of tensile adhesion tests show that EP/ metals composite have maximum strength Sad for certain weight percentage of metals 2.95 and 9MPa at 10% for EP/Al and EP/Cu composite and 8.2MPa at 40% for EP/Fe composites

View Publication Preview PDF
Publication Date
Tue Dec 05 2023
Journal Name
Engineering, Technology & Applied Science Research
The Fire Effect on the Performance of Reinforced Concrete Beams with Partial Replacement of Coarse Aggregates by Expanded Clay Aggregates
...Show More Authors

This paper aims to investigate the flexural behavior of reinforced concrete beams considering fire resistance by adding Lightweight Expanded Clay Aggregates (LECA) to the concrete mix as partial coarse aggregate replacement. LECA is a type of porous clay with a uniform pore structure with fine, closed cells and hard, tightly sintered skin. The experimental work comprised four reinforced self-compacted concrete beams. All the specimens were identical in their geometrical layout of 1600×240×200 mm, reinforcement details, and support condition (simply supported). For all the beams, the main reinforcement was provided by two bars, each having a diameter of 12 mm, while a bar of 6 mm diameter was employed for the top and shear reinforc

... Show More
View Publication
Crossref (1)
Scopus Clarivate Crossref
Publication Date
Thu Apr 20 2023
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Effect of Pistachio Husks Powder Additive on Unsaturated Polyester Composites
...Show More Authors

In this study, polyester composites reinforced with pistachio shells powder (P.) with an average
diameter (150 – 200 μm) with different weight ratios (0.5%, 1%, 1.5%, 2%, and 2.5%) were
prepared to the resin. The Shore D hardness, thermal conductivity (K), and the glass transition
temperature (Tg) of the samples were examined. The results showed that the Shore D hardness
increases with the increase of the reinforcement ratio and its maximum value is (87.55) at (2.5%
P.) While the value of hardness at (0%) is (86.5). The thermal conductivity increases slightly with
the increase in the percentage of reinforcement and its maximum value is (0.213253 W/ m. K) at
(2.5% P.), while the value of K at (0% P.)

... Show More
View Publication Preview PDF
Crossref
Publication Date
Thu Aug 24 2023
Journal Name
Environmental Monitoring And Assessment
Rice husk coated with copper oxide nanoparticles for 17α-ethinylestradiol removal from an aqueous solution: adsorption mechanisms and kinetics
...Show More Authors

The 17 α-ethinylestradiol (EE2) adsorption from aqueous solution was examined using a novel adsorbent made from rice husk powder coated with CuO nanoparticles (CRH). Advanced analyses of FTIR, XRD, SEM, and EDSwere used to identify the classification parameters of a CRH-like surface morphology, configuration, and functional groups. The rice husk was coated with CuO nanoparticles, allowing it to create large surface area materials with significantly improved textural qualities with regard to functional use and adsorption performance, according to a detailed characterization of the synthesized materials. The adsorption process was applied successfully with elimination effectiveness of 100% which can be kept up to 61.3%. The parameters of ads

... Show More
View Publication
Scopus (4)
Crossref (4)
Scopus Clarivate Crossref