Biomimatic basic calcium phosphate ,known as Hydroxy apatite(HA), was
synthesised using calcium acetate and disodium phosphate dilute hot (boiling) solution of
both salts were added slowly to each other. A colloidal suspension formed was aged for few
days, then boiled for one hour to induced setting and coagulation of preapatite, and left to cool
until they reached room temperature.
The precipitate was filtered and washed with distilled water, then ethanol and dried.
The dried sample was calcined at 1100
o
C.The obtained solid lumps were then crushed
reground fine powder and analyzed for calcium to phosphorous ratio. X-ray analysis was
carried out to examine the solid sample. Chemical analysis for phosphorus and calcium had
been carried out using standard method.
The results proved that the calcined sample used in this investigation where Hydroxyapatite .
(2)
A new tridentate ligand has been synthesized derived from phenyl(pyridin-3-yl)methanone. Three coordinated metal complexes were prepared by complexation of the new ligand with Cu(II), Ni(II) and Zn(II) metal salts. The new Schiff base “benzyl -2-[phenyl(pyridin-3-yl)methylidene]hydrazinecarbodithioate” and the new metal complexes were characterized using various physico-chemical and spectroscopic techniques. From the analysis results, the expected structure to the metal complexes are octahedral in geometry for Cu(II) complex, square planner for Ni(II) and tetrahedral for Zn(II) complex. The new compounds are expected to show strong bioactivity against bacteria and cancer cells.
This work targeted studying organogel as a potential floating system. Organgel has an excellent viscoelastic properties, floating system posses a depot property. Different formulations of 12-hydroxyoctadecanoic acid (HOA) in sesame oil were gelled and selecting F1, F3 and F5 HOA organogels for various examinations: tabletop rheology, optical microscopy, and oscillatory rheology studies. Also, the floating properties studies were conducted at in vitro and in-vivo levels. Lastly, the in-vitro release study using cinnarizine (CN) was to investigate the organogel depot property. Based on the results, the selected concentrations of HOA in sesame oil organogels showed temperature transitions fr
... Show More
(2)
(2)
In this work, silver (Ag) self-metallization on a polyimide (PI) film was prepared through autocatalytic plating. PI films were prepared through the solution casting method, followed by etching with potassium hydroxide (KOH) solution, sensitization with tin chloride (SnCl2), and the use of palladium chloride (PdCl2) to activate the surface of PI. Energy-dispersive X-ray analysis (EDX) showed the highest peak in the (Ag) region and confirmed the presence of AgNPs. The diffraction peaks at 2θ = 38.2°, 44.5°, 64.6°, and 78.2° represented the 111, 200, 220, and 311 planes of Ag, respectively. The FT–IR an
... Show More
(4)
(1)
Four batches of sertraline HCl microspheres were prepared using a poly (D-L-lactide-co-glycolide) (PLGA) polymer ( Mw. 9, 27, 30 and 83 KDa) as a delivery system. The microspheres were prepared by a dispersion/solvent extraction-evaporation method and characterized for drug loading by UV, particle size by laser diffractometry and surface morphology by scanning electron microscopy (SEM). The in vitro sertraline HCl release was studied. Spherical microspheres with a mean diameter of 21 to 26 µm loaded with 24.6 – 38.2% were produced. The in vitro drug release was shown to be depend on polymer molecular weight and also on the drug loading. Differential scanning calorimetry (DSC) was employed to investigate the physical state
... Show More
Iraqi kaolin was used for the preparation and characterization of NaY zeolite for biodiesel production via esterification reaction. Oleic acid was used usually as a typical simulated feedstock of high acid number for the esterification reaction.
The chemical composition for the prepared Nay zeolite is as following: (Ca2.6Na1.K0.1)(Al6.3Si17.7)O48.16H2O, the silica to alumina ratio in the prepared catalyst was found equal to 2.6 and Na2O content was 12.26 wt. %, with relative crystallinity equal to 147.4 % obtained by the X-ray diffraction. The surface area result shows that the prepared catalyst has 330 m2
... Show MoreIn this study, polymeric ultrafiltration (UF) membranes were prepared by phase inversion method to obtain both antibacterial and organic antifouling properties. The membranes were cast from a solution of polyvinylidene fluoride (PVDF) and formative silver (Ag) nanoparticles were successfully immobilized on a polymer. This was done using a solvent N, N-dimethylformamide (DMF) which is a solvent for the PVDF polymer meanwhile it is a reducing agent for silver ion. The effect of silver nanoparticles additives on the performance of polymeric ultrafiltration membrane was verified. Chemical composition and morphology of the surfaces of the membranes were characterized by Fourier transform infrared spectroscopy
... Show More
(3)
This study was carried out to prepare and characterize domperidone nanoparticles to enhance solubility and the release rate. Domperidone is practically insoluble in water and has low and an erratic bioavailability range from 13%-17%. The domperidone nanoparticles were prepared by solvent/antisolvent precipitation method at different polymer:drug ratios of 1:1 and 2:1 using different polymers and grades of poly vinyl pyrolidone, hydroxy propyl methyl cellulose and sodium carboxymethyl cellulose as stabilizers. The effect of polymer type, ratio of polymer:drug, solvent:antisolvent ratio, stirring rate and stirring time on the particle size, were investigated and found to have a significant (p? 0.05) effect on particle size. The best formul
... Show More
(13)
The LiCoMnO4 spinel compound was prepared by a sol–gel method. Structural measurements were utilized to investigate the characteristics of LCMO powder. The powder crystallizes in the space group Rd-3m, with a trigonal crystallinity structure, according to XRD analysis (hexagonal axes). SEM images showed that the crystalline grains sizes were about 200 nm - 350 nm, which provides large surface area. The sample had soft magnetic characteristics, according to hysteresis behaviour analysis in the Vibrating Sample Magnetometer (VSM). The prepared material is thought to be a candidate for the applications of energy storage in lithium-ion batteries.
In this study, crop residues from rice husks were used to enhance the properties of the prepared
wood-plastic composites (W.P.C) are made from epoxy (EP) and unsaturated polyester (UPE) at
a ratio of (50:50) and reinforced with scales in different proportions, both types are fine
(300μm≤) and coarse (300μm>). These blends were undergoing (wear, impact, hardness,
differential scanning calorimetry (DSC), and thermal conductivity) tests and the results showed
the best weight fraction. is the fine particle weight fraction at 25% and coarse at 15%, depending
on the studied tribological characteristics. The results showed by thermal properties of glass
transition temperatures (Tg). For each of the (EP,