Undoped and Al-doped CdO thin films have been prepared by vacuum thermal evaporation  on  glass  substrate  at  room  temperature  for  various  Al  doping ratios (0.5, 1 and 2)wt.% . The films are characterized by XRD and AFM surface morphology properties. XRD analysis showed that CdO:Al films are highly polycrystalline and exhibit cubic crystal structure of lattice constant averaged to 0.4696 nm with (111) preferred orientation. However, intensity of all peaks rapidly decreases which indicates that the crystallinity decreases with the increase of Al dopant. The grain size decreases with Al content (from 60.81 to 48.03 nm). SEM and AFM were applied to study the morphology an

Abstract Background: One of the most important methods to replace lost teeth is dental implants. In order to increase the strength of connection of the implant with the jaw bone to provide early loading after placement, implant is coated by different coating materials that achieved that purpose. The aim of this study was to evaluate the influence of coating CP Ti implant with calcium carbonate on the strength of bone-implant interface after two and six weeks of implantation in rabbit femur bone by torque removal test, histological and histomorphometric analysis. Materials and methods: Coating the surface of commercially pure titanium screws with extra pure synthetic calcium carbonate via electrophoretic deposition method (EPD) was done. The

In this work, thiadiazole derivatives were prepared by taking advantage of active sites in (2-amino-5-mercapto-1, 3, 4-thiadiazole) as a starting material base. The main heterocyclic compounds (1, 3, 4-thiadiazole, oxazole) etc, 2-amino-5-mercapto-1,3,4-thiadiazole compound (1) was prepared by cyclic closure of thiosemicarbazide compound with anhydrous sodium carbonate and carbon disulfide. Oxidation of (1) via hydrogen peroxide, to have (2) which was treated with chloro acetyl chloride to get (3). Preparation of thiazole ring (4) was from reacting of (3) with thiourea. Synthesis of diazonium salts (5) from compound (4) using sodium nitrite and HCl. Compound (5) reacted with different ester compounds to prepare a new azo compounds (6–8).C

ABU OBAYDA and Syntax Studies

    Lipase was extracted by Sodium acetate buffer (pH=6; 0.05M) Containing 0.1M NaCl. Enzyme content of crude extract was concentrated by gradual addition of ammonium sulfate at 30-60% saturation. The dialyzed extract was purified on ion-exchange chromatography through DEAE–Cellulose and gel-filtration chromatography through sephacryl S-200 column. The specific activity, enzyme yield and fold purification were 54.06 unit/mg, 42.6% and 10.88 respectively. The molecular weight of the Lipase was 43.651 KDa as determined by gel-filtration chromatography through sephacryl S-200 column. Partial purified lipase used for the improvement of the flavor of butter fat after 12 hours for storage.

In this study, a packed bed was used to remove pathogenic bacteria from synthetic contaminated water. Two types of packing material substrates, sand and zeolite, were used. These substrates were coated with silver nanoparticles (AgNPs), which were prepared by decomposition of Ag ions from AgNO3 solution. The prepared coated packings were characterized using scanning electron microscopy, energy-dispersive X-ray spectroscopy and transmission electron microscopy. The packed column consisted of a PVC cylinder of 2 cm diameter and 20 cm in length. The column was packed with silver nanoparticlecoated substrates (sand or zeolite) at a depth of 10 cm. Four types of bacteria were studied: Escherichia coli, Shigella dysenteriae, Pseudomonas aerugi

In this study, the use of non-thermal plasma theory to remove toxic gases emitted from a vehicle was experimentally investigated. A non-thermal plasma reactor was constructed in the form of a cylindrical tube made of Pyrex glass. Two stainless steel rods were placed inside the tube to generate electric discharge and plasma condition, by connecting with a high voltage power supply (up to 40 kV). The reactor was used to remove the contaminants of a 1.25-liter 4-cylinder engine at ambient conditions. Several tests have been carried out for a ranging speed from 750 to 4,500 rpm of the engine and varying voltages from 0 to 32 kV. The gases entering the reactor were examined by a gas analyzer and the gases concentration ratio

In this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed f