The present paper talks about balance between two poems which are the Nouniya for Ibn Zaidoun and Andalusia for Ahmed Shawqi. This study is not claimed to be the first of its kind but we found some artistic aspects that deserve to stop at them. This what makes the two the focus of critics and scholars as well in addition to their emphasis on the unity of the human feelings and immortality through the poet's ability to employ those feelings and emotions in a way that it can express the human soul in every time and place. That is what we believe Ibn Zaidoun had reached in his poem. Therefore, the present paper has come into the conclusion that Ibn Zaydoon's Nouniya is better than Shawqi's Andalusia due to what we got through reading and an

The Topography, Physical and Optical properties of as-deposited copper oxide CuO absorption layer sprayed using homemade fully computerized CNC spray pyrolysis deposition technique at different deposition speed are reported. These layers are characterized by UV-Visible spectrophotometer, optical microscope, and thickness monitor studies. The optical transmittance study indicates that these layer exhibit high absorption coefficient in the visible range. The optical band gap is found to be at about at speeds (3,6 mm/s). Better homogeneity in CuO layer is found at the speed 5 mm/s. The film thickness lies within the 129-412 nm range.

In this study, composite materials were prepared using unsaturated polyester resin as binder with two types of fillers (sawdust and chopped reeds). The molding method is used to prepare sheets of UPE / sawdust composite and UPE / chopped reeds composite. The mechanical properties were studied including flexural strength and Young's modulus for the samples at normal conditions (N.C). The Commercial wood, UPE and its composite samples were immersed in water for about 30 days to find the weight gain (Mt%) of water for the samples, also to find the effect of water on their flexural strength and Young's modulus. The results showed that the samples of UPE / chopped reeds composite gained highest values of flexural strength (24.

     The superconductor compound (YBa2Cu2.8Zn0.2O7+δ) is prepared by solid state reaction (SSR), Sol-gel (SG) and laser Pulse deposition (PLD) methods. We used the X-ray diffraction technique, which shows an orthorhombic crystalline system for all the samples, and increase in the high-phase (Y-123) and decrease in low-phase and vary in proportion according to the method of preparation with the emergence of some impurities. The behavior of the samples in terms of electrical resistance and critical temperature was investigated all samples showed superconducting behavior. The properties of the dielectric (real dielectric constant, imaginary dielectric constant, loss tangent, alternating electrical conductivity) were s

The most important topic for psychologist generally is factor of education and it's active tools because learning needs active perception for stimulus that recived by the educator and give it avalue and meaning , Need for cognition is
very important in the various daily fields of life , especially in learning and teaching and the academy work , it help with shifting the learning level for people , and icreas the intense and challenge between them
The research endeavored to achieve the following aim :
1- Measuring the level of peripheral perception for the university student .
2- Measuring the level of need for cognition for the university student .
3- Measuring the level of peripheral perception for the university student

The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

In this study, epoxy was used as a matrix for composite materials, with E-glass fiber, jute and PVC fiber which was woven roving fiber, as reinforcement with volume fraction (Vf= 30%). There are two of prepared types of epoxy non reinforced, epoxy reinforced with E-glass, jute and PVC fibers including study of mechanical tests (Impact test, Bending test) different temperature and thermal conductivity and calculating the temperatures coefficient at different temperature. Results show that elastic modulus at rate values decrease to the increase of temperature and the impact strength, impact energy and thermal conductivity increase with increase temperature.

In this research prepared Epoxy – Talc powder composites with weight ratio of Talc powder (0,5,10,15,20,25)% . The value of thermal conductivity increase with increasing ratio of talc powder and water absorption increase with increasing ratio of talc powder because the structure from magnesium silicate hydroxide and hydrophilic nature .Ethanol absorption decrease with increasing percentage talc powder compared with epoxy pure

  Alloys of Bi2[Te1-x Sex]3 were prepared by melting technique with different values of  Se percentage (x=0,0.1,0.3,0.5,0.7,0.9  and 1). Thin films of these alloys were prepared by using thermal evaporation technique under vacuum of 10-5 Torr on glass substrates, deposited at room temperature with a deposition rate (12nm/min) and a constant thickness (450±30 nm). The concentrations of the initial elements Bi, Te and Se in the Bi2 [Te1-x Sex]3 alloys with different values of Se percentage (x), were determined by XRF,The morphological and structural properties were determined by AFM and XRD techniques.  AFM images of Bi2[Te1-x Sex]3 thin films  show that the average diameter and the average surface roughness inc