The Study Properties (Compressive And Tensile And Wear) For The Composite Materials Hybried
...Show More Authors

  This study included prepared samples of epoxy reinforced by the novolac , aluminum , glass powder and epoxy reinforced by aluminum , glass powder and epoxy alone .They are used as reinforced materials of volum fraction amounting 40% .  The mechanical properties inclouded ( tensile , compressive and wear) where the wear test inclouded different applied loads (5,10,15) . From the results showed the epoxy reinforced by aluminum and glass powder has higher compressive strength (56.91) Mpa and higher tensile strength (132.2) Mpa .But the epoxy alone has higher wear rate and the epoxy reinforced by aluminum and glass powder which have higher elasticity of modulus from the tensile test (315.7) Mpa

View Publication Preview PDF
Quick Preview PDF
Publication Date
Mon Aug 01 2011
Journal Name
Journal Of Engineering
CORRELATIONS OF POINT LOAD INDEX AND PULSE VELOCITY WITH THE UNIAXIAL COMPRESSIVE STRENGTH FOR ROCKS
...Show More Authors

Rock engineers widely use the uniaxial compressive strength (UCS) of rocks in designing
surface and underground structures. The procedure for measuring this rock strength has been
standardized by both the International Society for Rock Mechanics (ISRM) and American Society
for Testing and Materials (ASTM), Akram and Bakar(2007).
In this paper, an experimental study was performed to correlate of Point Load Index ( Is(50))
and Pulse Wave Velocity (Vp) to the Unconfined Compressive Strength (UCS) of Rocks. The effect
of several parameters was studied. Point load test, Unconfined Compressive Strength (UCS) and
Pulse Wave Velocity (Vp) were used for testing several rock samples with different diameters.
The predicted e

... Show More
View Publication Preview PDF
Crossref (9)
Crossref
Publication Date
Wed Nov 30 2022
Journal Name
Iraqi Geological Journal
A Predictive Model for Estimating Unconfined Compressive Strength from Petrophysical Properties in the Buzurgan Oilfield, Khasib Formation, Using Log Data
...Show More Authors

Unconfined compressive strength (UCS) of rock is the most critical geomechanical property widely used as input parameters for designing fractures, analyzing wellbore stability, drilling programming and carrying out various petroleum engineering projects. The USC regulates rock deformation by measuring its strength and load-bearing capacity. The determination of UCS in the laboratory is a time-consuming and costly process. The current study aims to develop empirical equations to predict UCS using regression analysis by JMP software for the Khasib Formation in the Buzurgan oil fields, in southeastern Iraq using well-log data. The proposed equation accuracy was tested using the coefficient of determination (R²), the average absolute

... Show More
View Publication
Crossref
Publication Date
Wed Dec 25 2024
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Effect of Temperature and Frequency on the Dielectric Properties of PVC/MnCl2 Composite
...Show More Authors

View Publication
Publication Date
Sun Aug 13 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Effect of Temperature and Frequency on the Dielectric Properties of PVC/MnCl2 Composite
...Show More Authors

       The dielectric properties of polyvinyl chloride (PVC)-MnCl2 composite were studied by using the impedance technique. The measurements were carried out as a function of frequency in the range from 10 Hz to 13 MHz and temperature range from 27oC to 55oC. Using a composite of 20 wt. % MnCl2 by weight, it was found that the dielectric constants and the dielectric loss of the prepared films increase with the increasing temperature at law frequency and the enhancement of the ionic conduction which is confirmed by the increase the of AC. conductivity and the decrease of the activation energy of the conduction mechanism at high applied frequency. The observed relaxation and polarization effects of composite a

... Show More
View Publication Preview PDF
Publication Date
Thu Mar 01 2018
Journal Name
Composite Structures
Computational homogenization of the elastic and thermal properties of superconducting composite MgB2 wire
...Show More Authors

View Publication
Scopus (37)
Crossref (35)
Scopus Clarivate Crossref
Publication Date
Sat Dec 30 2023
Journal Name
Iraqi Journal Of Science
Composite Resin Coating for The Protection of Surfaces and Metals
...Show More Authors

The curing process of epoxy resin was investigated with some additives and fillers such as nano fumed silica with primary particle diameter of 56–58 nanometers, fine ferric oxide with an average particle diameter of 0.4 micrometer, fine calcium carbonate with an average particle diameter of 0.58 micrometer, and plasticizer, a new composite resin has been obtained. Based on present experimental results, the new composite resin shows high impact strength and hardness as well as the ability of the composite withstand to degradation from water way in. Additionally, curing time of composite was reduced to the minimum set time than epoxy resin at different temperature. This new composite resin was used appropriately for coating to protect su

... Show More
View Publication Preview PDF
Publication Date
Thu Jun 15 2017
Journal Name
Journal Of Baghdad College Of Dentistry
The Effect of Different Light Cure Systems on Microhardness of Bulk Fill Composite Materials
...Show More Authors

Background: The aim of this study was to evaluate the effect of three types of light curing devices QTH, LED and Flashmax on the surface microhardness of three types of bulkfill composite resins; Filtek Bulkfill posterior composite ( 3M), Tetric Evo Ceram ( Ivoclar Vivadent) and Sonicfill composite ( Kerr) Materials and methods: Total number of 90 samples was prepared, 30 samples for each type of bulkfill composite, were divided into three main groups, group A: Filtek posterior bulkfil (3M), group B: Tetric Evo Ceram (Ivoclar Vivadent) and group C: contain Sonicfill composite (kerr). Which then divided into three subgroups (n= 10) (1) Samples cured by QTH system (2) Samples cured by LED system and (3) samples cured by Flashmax system the

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sun May 07 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
The Study of Wear Effect on the Unsaturated Resin Reinforced By Rice Husk
...Show More Authors

This study was performed by using the unsaturated polyester resin as matrix to the
composite materials with the rice husk as reinforced materials . The research included study
of wear test on the composite material The results show that the, wear is increased with the
increase of applied load and distance slipping and also with time increase . moreover the
shows that the higher value wear rate( 1.91gm/cm) from the load (20) N and the higher value
wear rate (1.43gm/cm) from the higher distance (4cm) and from the higher time (6min) higher
wear rate (5.33gm/cm).

View Publication Preview PDF
Publication Date
Wed Jun 30 2021
Journal Name
Iraqi Geological Journal
The Effect of Weighting Materials on the Rheological Properties of Iraqi and Commercial Bentonite in Direct Emulsion
...Show More Authors

Numerous drilling additives and materials are used continuously because they are necessary to support and give the required properties of the drilling fluid so that to ensure the stability of the borehole. This paper aspires to evaluate the rheological properties of bentonite (montmorillonite) Trefawey as an alternative to using commercial bentonite. Monitoring and evaluating of the rheological and filtration properties were prepared. This exertion aims to focus on the effect of hematite, and barite on the rheological properties of the three aforementioned bentonite types. An improvement in the rheological properties of bentonite (montmorillonite). Trefawey was observed after adding the previous heavy materials. Hematite has by some

... Show More
View Publication
Crossref
Publication Date
Tue Dec 19 2017
Journal Name
Al-khwarizmi Engineering Journal
Improve Wear Resistance on Al 332 Alloy Matrix- Micro -Nano Al2O3 Particles Reinforced Composite
...Show More Authors

The wear behavior of alumina particulate reinforced A332 aluminium alloy composites produced by a stir casting process technique were investigated. A pin-on-disc type apparatus was employed for determining the sliding wear rate in composite samples at different grain size (1 µm, 12µm, 50 nm) and different weight percentage (0.05-0.1-0.5-1) wt% of alumina respectively. Mechanical properties characterization which strongly depends on microstructure properties of reinforcement revealed that the presence of ( nano , micro) alumina particulates lead to simultaneous increase in hardness, ultimate tensile stress (UTS), wear resistances. The results revealed that UTS, Hardness, Wear resistances increases with the increase in the percentage of

... Show More
View Publication Preview PDF