Objective: The aim of this study was to compare the marginal microleakage between bulk-fill, preheated bulk-fill, and bulk-fill flowable composite resins above and below cemento-enamel junction (CEJ) using micro-computed tomography. Methods: Sixty freshly extracted premolar teeth were prepared with a slot shaped cavities of a total of 120 Class II: 3mm (bucco-lingual), 2mm (mesio-distal) with mesial-gingival margin located 1mm coronal to CEJ, and distal gingival margin located 1mm apical to the CEJ. The samples were randomly divided into two main groups according to the restorative material (Tetric EvoCeram and 3M Filtek), and each group was further sub-divided into three subgroups according to the consistency (bulk fill, preheated bulk fil

       Copper Phthalocyanine (CuPc) thin film with and without multi-walled carbon nanotubes (MWCNTs) is prepared using the solution based method and used in gas sensor and solar cell applications. The structural characteristics of the CuPc thin films showed a single peak around 7^o with the preferred orientation for charge transportation. Using atomic force microscopy (AFM), morphological properties show a rough surface with some aggregates and ribbons. The optical absorption properties were determined using UV-Visible absorption spectroscopy; the optical band gap has varied after adding MWCNTs to CuPc. Electrical conductivity of CuPc:MWCNTs composite is higher than that of the pure CuPc. The CuPc thin film sensr have sh

     Charge extraction layers play a crucial role in developing the performance of the inverted organic solar cells. Using a transparent metal oxide with appropriate work function to the photoactive layer can significantly decrease interface recombination and enhance charge transport mechanism. Therefore, electron selective films that consist of aluminium-doped titanium dioxide (TiO₂:Al) with different concentrations of Al (0.4, 0.8, and 1.2)wt %  were prepared using sol-gel technique. The inverted organic solar cells PCPDTBT: PCBM with Al doped TiO2 as electron extraction layer were fabricated. It is well known that Al doping concentration potentially affects the physical characteristics of the TiO₂ by control

The present work aimed to study effect of (N749 & N3) dyes on TiO2 optical and electrical properties for optoelectronic application. The TiO2 paste prepared by using a doctor blade method. The samples were UV-VIS specterophometricall analyzes of TiO2 before and after immersed in dyes (N749 & N3). The results showed absorption spectra shift toward the visible region due to the adsorption of dye molecules on the surface of oxide nanoparticles. It is seen that the Eg determined to give a value of 3.3eV for TiO2 before immersing in dyes, and immersing in dyes (N749 & N3) are (1.4 &1.6 eV) respectively. The structural properties (XRD), (FTIR) and (SEM) for the sample prepared were investigated and (J-V) characteristics was stu

ABSTRACT:In this paper, Cd10–xZnxS (x = 0.1, 0.3, 0.5) films were deposited by using chemical spray pyrolysis technique, the molar concentration precursor solution was 0.15 M/L. Depositions were done at 350°C on cleaned glass substrates. X-ray dif- fraction technique (XRD) studies for all the prepared film; all the films are crystalline with hexagonal structure .The optical properties of the prepared films were studied using measurements from VIS-UV-IR spectrophotometer at wave- length with the range 300 - 900 nm; the average transmission of the minimum doping ratio (Zn at 0.1%) was about 55% in the VIS region, it was decrease at the increasing of Zn concentration in the CdS films, The band gap of the doped CdS films was varied as 3.7, 3

In this work, A new strategy for enhancing the efficiency of dye sensitized solar cells (DSSC) by doping foreign ion and co- doping TiO2 / Fe and Cu (38 nm ) was prepared by sol-gel method and successfully used as a photoanode for (DSSC). The samples were characterized by using X-ray diffraction ( XRD) is used to calculate grain size, before and after Fe, Cu- doping and co- doping. Glass coating process with a thin layer on (Fluorine doped tin oxide) FTO glass by using doctor Blade technique .The optimum thickness utilized for TiO2 paste is (15μm) on a conductive glass. The best experimental results for doping and co- doping TiO2 with additive Copper (II) nitrate Cu (NO3)2 as improved it was VOC=0.6 V, ISC=1.92 mA, Imax=1.8 mA and Vmax=

      Compounds from tin oxide doped with gallium oxide and cerium oxide were synthesized. Thin films from (SnO₂:Ga₂O₃,CeO₂) with different doping ratios were prepared on glass and single crystal silicon as substrates with the use of the pulsed laser deposition technique. The results of FTIR spectrums analysis was presented. Varies heterojunctions were fabricated from (SnO₂:Ga₂O₃,CeO₂ /Cu₂S/c-pSi) heterojunctions solar cell which are formed from two layers: the first was Cu₂S and the second was layer from tin oxide doped with two oxides named gallium oxide and cerium oxide with different doping ratios (0, 0.03, 0.05, and 0.0