Graphene oxide (GO) was prepared from graphite (GT) with Hammer method, the GO was reduced with hydrazine hydrate to produce a reduced graphene oxide (RGO). The RGO was reacted with thiocarbohydrazide (TCH) to functionalize the RGO with 4-amino-3-symbol-1h-1, 2, 4-triazol-5 (4H) –thion group and to obtain (RGOT). All the prepared nanomaterial and the product of the functionalization RGOT were characterized with Fourier transformer infrared (FT-IR) spectroscopy, X-ray diffraction (XRD) analysis. RGOT mixed with ultrasonic device at different pH values of phosphate buffer solution (PBS), the mixture used to modifying a screen printed carbon electrodes SPCE and with cyclic voltammetry the sensitivity of selectivity of the new modifying elect

Volumetric chemical adsorption was done in a volumetric apparatus using hydrogen gas at room temperature on eleven platinum catalyst, commercial catalysts (RG-412,RG-402 ,RG-432, RG-451, RG-482, and PS-10) and prepared platinum catalysts with 0.1, 0.2 , 0.45 , and 0.55% by weight of Pt supported with Y-alumina. The results show that the metal crystallite area increases with increasing platinum content. The dispersion and particle size of metal crystallite located between 48.2-96.1% and 3.85-12.72 nm, respectively. For bimetallic catalysts, the hydrogen intake decrease in the following order : Re < Sn < Ir.

In this work, the adsorption of reactive yellow dye (Remazol yellow FG dye) by granular activated carbon (GAC) was investigated using batch and continuous process. The batch process involved determination the equilibrium isotherm curve either favorable or unfavorable by estimation relation between adsorption capacity and concentration of dye at different dosage of activated carbon. The results were fitted with equilibrium isotherm models Langmuir and Freundlich models with R2value (>0.97). Batch Kinetic study showed good fitting with pseudo second order model with R2 (0.987) at contact time 5 h. which provesthat the adsorption is chemisorptions nature. Continuous study was done by fixed bed column where breakthrough time was increased

chloride or poluacrulic acid with different primary amines to mesuring==================================638one hundred three patinents with rheumatic symptoms were include in this study and their sera tested for

Indium oxide In2O3 thin films fabricated using thermal evaporation of indium metal in vacuum on a glass substrate at 25oC using array mask, after deposition the indium films have been subjected to thermal oxidation at temperature 400 °C for 1h. The results of prepared Indium oxide reveal the oxidation method as a strong effect on the morphology and optical properties of the samples as fabricated. The band gap (Eg) of In2O3 films at 400 °C is 2.7 eV. Then, SEM and XRD measurements are also used to investigate the morphology and structure of the indium oxide In2O3 thin films. The antimicrobial activity of indium oxide In2O3 thin films was assessed against gram-negative bacterium using inhibition zone of bacteria which improved higher ina

Five different bacterial isolates [ Vibrio cholera (Ogawa) , Vibrio cholera (Inaba) , Salmonella typhi , Salmonella paratyphi and ? Salmonella typhimurium ] were obtained from the Central Health Laboratory . Both sensitivity tests (MIC , MBC and wells method ) against these bacteria were performed by using the aqueous of leaves extract of Marjoram plant. The results cleared that the values of MIC for Vibrio cholera serotypes Ogawa and Inaba were 100 mg/ml , while the value of MBC was 200 mg/ml. The value of the Inhibition zone at 100 mg /ml concentration for both Ogawa and Inaba were 13 mm and 9 mm respectively. Our results showed that the three types of Salmonella didn’t show any inhibition zone at 200 mg/ml .