Fabrication of Natural Gelcoats (Epoxy/ Pumpkin Peels Fibers) Composites with High Mechanical and Thermal Properties
...Show More Authors

     Pumpkin waste powder was used as a coloring and strengthening filler in epoxy to prepare a natural gelcoat . The Pumpkin powder was mixed with different weight ratios (1, 2, 3, 4, 5, 6, 7, and 8%) to the epoxy matrix to select the best value of powder addition. The effect of the pumpkin particle size on the mechanical properties (impact, flexural, hardness, and wear loss) using two different sizes (2.5 and 1.25 microns) was studied. The impact strength increased from (10.09 KJ/ m2) for neat epoxy to (14.79 KJ/ m2) for epoxy with  1% of micron pumpkin fibers ( MPF) with particle size 2.5 micrometer and (14.21 KJ/ m2) for epoxy with 4% (1.25 MPF), flexural strength increased from (41.94 MPa) for neat epoxy to (~ 46 MPa) for epoxy with  1% of  2.5 MPF  and to (50.17 MPa) for epoxy with 4% of 1.25 MPF, hardness of neat epoxy was (~ 77) and almost maintained its value for epoxy with  1% of 2.5 MPF and for epoxy with 4%  of 1.25 MPF. At almost the weight fractions addition of pumpkin fibers to epoxy, the (EP/1.25MPF) composite shows a higher wear resistance than the (EP/2.5MPF) composite. The density, thermal conductivity, and water diffusion (for 1-4 weeks' immersion) of (EP/2.5MPF) and (EP/1.25MPF) composites were carried out at different weight percentages of pumpkin fibers. SEM and EDS techniques were employed to fix the microstructure and the elemental composition of (EP/2.5MPF) and (EP/1.25MPF) composites, respectively. The internal structure of the composites has been linked with their macroscopic characteristics, such as the color degree of natural gelcoats and their mechanical and thermal properties.

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Wed Aug 09 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
The Study Effect of Addition Magnesia (MgO) on Some Physical and Mechanical Properties for Alumina
...Show More Authors

   A reseach is carried out by using Alumina material type α-Al2O3 which has partical size 63μm doped with different percentage weight of MgO (0.1%,0.3%and0.5%) and by using dry press method to prepare the samples ,A force press 50KN used and sintering to 1500oC with   soaking time  of  6 hours.        The physical properties were studied such as "Bulk density ,Porosity and water absorption "also the mechanical properties such as (hardness,compressive strength ), the result shows that the best ratio of maginsa(MgO) added to Alumina (Al2O3)is 0.5%and this  worked to improve   Physical and mechanical properties .

View Publication Preview PDF
Publication Date
Tue Nov 07 2023
Journal Name
Innovative Infrastructure Solutions
Enhancing load-bearing performance of hybrid recycled aggregate concrete-filled columns using SBR, steel fibers and polypropylene fibers
...Show More Authors

View Publication
Scopus (2)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Sat Aug 31 2019
Journal Name
Iraqi Journal Of Physics
Investigation the effect of post deposition thermal treatment on properties P3HT and P3HT:PCBM blend.
...Show More Authors

  This work reports the study of heat treatment effect on the structural, morphological, optical and electrical properties of poly [3-hexylthiophene] and its blend with [6,6]-phenyl C61 butyric acid methyl ester ( P3HT:PC61BM). X-ray diffraction (XRD) measurements show that the crystallinity of the films increased with annealing. The evaluation of surface roughness and morphology was investigated using atomic force microscope (AFM), and field emission scanning microscope(FESEM). The optical properties were emphasized a strong optical absorption of P3HT compared with the blend. Hall effect measurement was used to study the electrical properties which revealed there is an increase in the electrical conductivity and Hall mobility of th

... Show More
View Publication Preview PDF
Crossref
Publication Date
Thu Dec 31 2020
Journal Name
Iraqi Journal Of Market Research And Consumer Protection
STUDY THE SENSORY PROPERTIES OF SOME TYPES OF JUICES THAT MADE BY USING NATURAL SWEETENER POWDER (Stevia rebaudiana): STUDY THE SENSORY PROPERTIES OF SOME TYPES OF JUICES THAT MADE BY USING NATURAL SWEETENER POWDER (Stevia rebaudiana)
...Show More Authors

Increased diseases and obesity currently due to increased production and excessive consumption of foods manufactured from non-food sweeteners without attention to the risk of consuming those additional high calories due to consuming these refreshing products such as juices and other various drinks, especially in the summer season by most segments of Iraqi society, especially workers, children and school students the aim of this study. Therefore, the study designed to replace sucrose with 0.03, 0.04 and 0.05% of each of the white stevia crystals and milled dry stevia leaves in the laboratory manufacture of juices and its effect on the general and sensory characteristics and the extent of their acceptability among the specialized r

... Show More
View Publication Preview PDF
Publication Date
Fri Jun 01 2018
Journal Name
Journal Of Taibah University Medical Sciences
Effect of nano-titanium oxide addition on some mechanical properties of silicone elastomers for maxillofacial prostheses
...Show More Authors

Objective This study evaluated the effects of adding titanium oxide (TiO2) nanofillers on the tear strength, tensile strength, elongation percentage, and hardness of room-temperature-vulcanized (RTV) VST50F and high-temperature-vulcanized (HTV) Cosmesil M511 maxillofacial silicone elastomers. Methods Two types of maxillofacial elastomers, VST50F RTV and Cosmesil M511 HTV, were used. Nano-TiO2 powder was applied as a nanofiller. A total of 120 specimens were fabricated, 60 each of VST50F and Cosmesil M511. The specimens of each type of elastomer were divided into three equal groups on which tests were conducted for tear strength, tensile strength, and hardness i.e., 20 specimens were used for each test. Each group of 20 specimens was further

... Show More
View Publication
Scopus (24)
Crossref (8)
Scopus Clarivate Crossref
Publication Date
Mon Dec 23 2024
Journal Name
Journal Of Baghdad College Of Dentistry
The effect of adding single walled carbon nanotube with different concentrations on mechanical properties of heat cure acrylic denture base material
...Show More Authors

Background: The most widely used material for fabrication of denture base is poly methyl methacrylate, despite its popularity, the main problems associated with it as a denture base material are poor strength particularly under fatigue failure inside the patient mouth, impact failure outside the patient mouth, which are the main causes for fracture of denture, several studies was done to increase mechanical properties of denture base. The present study was conducted to evaluate and compare the effect of addition single walled carbon nanotubes in different concentrations to polymethyl methacrylate on some mechanical properties (surface hardness, surface roughness, impact strength and transverse strength). Materials and methods: Forty eight

... Show More
View Publication Preview PDF
Publication Date
Fri Apr 19 2019
Journal Name
Iraqi Journal Of Science
Effects of TEOs aerogel particles size of TEOS aerogel on its mesoporous structure and thermal behavior via supercritical drying and high temperature
...Show More Authors

TEOS aerogel a is the most commonly used. a Aerogel has attracted increasing attention from both academic and industries due to its extraordinary performance and potentials. We have systematically studied the relationship between the densification temperature of the synthesis environment of silica aerogels on their resulting morphological, optical and thermal properties. SEM and BET measurements were employed as structural probes to ascertain the structural differences. Lee's disc apparatus was used for determining the thermal conductivity coefficient. There is a systematic correlation between the annealing temperature and the aerogel surface area, porosity, as well as pore size. The implemented autoclave was able to produce aerogel mono

... Show More
View Publication Preview PDF
Publication Date
Sun Apr 09 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Study the Effect of Addition of Some Oxides on the Mechanical properties on Unsaturated Polyester Resin Compsites
...Show More Authors

This study included preparation for the unsaturated polyester samples before and after reinforced by Alumina oxide powder and copper oxide powder of different volume fraction amounting (3%,5%,8%). And this reearch included study of some of mechanical properties such as (hardness,compressive and wear).The results showed that increase of the hardness and compressive strength after the reinforced and increase with the volume fraction increase.As the wear test show that the wear rate increases with applied load from the different load(5,10,15)N,and the wear rate decreases with the volume fraction increase.

View Publication Preview PDF
Publication Date
Sat Aug 01 2015
Journal Name
Journal Of Engineering
Influence of Internal Sulfate Attack on Some Properties of High Strength Concrete
...Show More Authors

One of the most important problems that faces the concrete industry in Iraq is the deterioration due to internal sulfate attack , since it reduces the compressive strength and increases the expansion of concrete. Consequently, the concrete structure may be damage .The effects of total and total effective sulfate contents on high strength concrete (HSC) have been studied in the present study. The research studied the effect of sulfate content in cement , sand and gravel , as well as comparing the total sulfate content with the total effective SO3 content. Materials used were divided into two groups of SO3 in cement ,three groups of SO3 in sand ,and two groups of SO3 in gravel. The results show that considering the total effective sulfate con

... Show More
Preview PDF
Publication Date
Thu Dec 13 2018
Journal Name
International Journal Of Engineering & Technology
Effect of Steel Fiber on Properties of High Performance No-Fine Concrete
...Show More Authors

No-fine concrete (NFC) is cellular concrete and it’s light weight concrete produced with the exclusion of sand from the concrete. This study includes the mechanical properties of lightweight reinforced by steel fiber, containing different proportions of steel fiber. This study was done using number of tests. These tests were density, compressive strength, flexural strength and absorption. These tests of the molds at different curing time. The results of tests that implication of fiber to No. fine concrete did not affect significantly on the compressive strength, While the flexural strength were gets better. Results explained that, the flexural strength of (1%) fiber No- fine concrete molds are four times that of the reference mold

... Show More
View Publication
Crossref (1)
Crossref