Several  amine  liquid selective  electrodes  were prepared based on

two  active   materials,   phenol  sulfonic   acid  and   l ,2-dihydroxy-3,5- disulfonic  acid   disodium   salt   with  several   plasticizers,  di-n-butyl phthalate(ORPH),  tri-n-butyl   phosphate   (TBP)   and  a-nitro   phenyl octyl  ether   (NPOE).   Electrode   parameters   were  studied   including, concentration range,  detection  limit,  slope,  life  time,  response  time and  

In this paper, a study of improving the physical properties, mechanical and thermal insulation are conducted to produce gypsum boards with lightweight from waste materials. These boards can be used as an internal packaging wall or partitions tile of non-Bering with a high thermal insulation. Gypsum plaster mixed with waste material like (PET Polyethylene terephthalate, sawdust in size4.75mm and rubber) in different ratio (5%, 7%, 10%, 15%, 20%, 25%and 30%) of plaster to produce boards and then to find out the effect of these materials on the properties of boards, so that tests of consistency, setting time, flexural strength, density and thermal conductivity were achieved for all samples to find out this effect. The result shows that the

The Neutron Fermi Age, t, and the neutron slowing down density,   q (r, t) , have been measured for some materials such as Graphite and Iron by using gamma spectrometry system UCS-30 with NaI (Tl) detector. This technique was applied for Graphite and Iron materials by using Indium foils covered by Cadmium and the measurements done at the Indium resonance of 1.46 eV. These materials are exposed to a plane ²⁴¹Am/Be neutron source with recent activity 38 mCi. The measurements of the Fermi Age were found to be t = 297 ± 21 cm² for Graphite, t = 400 ± 28 cm² for Iron. Neutron slowing down density was also calculated depending on the recent experimental t value and distance.

Ceramic body as a refractory was prepared by using shamoot, which is prepared by firing  kaolin Duekhla at 1450 ºC at 2hr ,Flint clay ,Asbestos fiber(Anthophylite type)and Sodium silicts,Phosphoric acid solution as a binder . After miling, siving ,and mixing ,samples were formed, followed that drying, firing at different temperature.     Phyical ,thermal and mechanical  properties were measured .The conclusion behind the results that the refractory prepared from; 37.5% shamoote,25% Asbestos ,37.5% Flint clay and Phosforic acid solution fired at 1300 ºC  gave a refractory material having  melting temperature ;1490 ºC, thermal shock resistance 7 cycle, thermal conductivity 2.1w/m2.K, apperan

Recently a large number of extensive studies have amassed that describe the removal of dyes from water and wastewater using natural adsorbents and modified materials. Methyl orange dye is found in wastewater streams from various industries that include textiles, plastics, printing and paper among other sources. This article reviews methyl orange adsorption onto natural and modified materials. Despite many techniques available, adsorption stands out for efficient water and wastewater treatment for its ease of operation, flexibility and large-scale removal of colorants. It also has a significant potential for regeneration recovery and recycling of adsorbents in comparison to other water treatment methods. The adsorbents described herein were

Background: The aim of this in vitro study was to evaluate and compare the microleakage between Vertise Flow T M composite material and other conventional (Filtek Z250, riva light cure and SDR) composite materials when restoring CII mesial box only cavity at gingival margin through die penetration test Materials and methods: Forty maxillary first premolars were prepared with class II box design only cavities. Samples were divided into four groups of ten teeth according to material used: group I (FiltekZ250 only). Group II (SDR+FiltekZ250). Group III (Vertise Flow +FiltekZ250). Group IV (Riva light cure+ FiltekZ250). After 24 hrs. immersion in 2% in methylene blue, samples were sectioned and micro leakage was estimated. Results: None of the

The Maxwell equations have been formulated for a composite slab waveguide at x-band wave propagation. The eigenvalues of the system equations are obtained by using MATLAB program. These eigenvalues are used to obtain the wave propagation constant and a number of modes inside the slabs. A good correspondence was seen between the number of modes and the cut off thickness. The parameter that affects the performance of waveguide is the slab thickness. The propagation constant is usually adopted to characterize this type of waveguide and show how the cutoff frequency of the mode in the slab is increased dramatically by decreasing the frequency.
Our study focused on lower modes, the results for the transmission coefficient are then used to