The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di

  The species of Cr (III), Cr (VI) in biological samples and V(IV), V(V) in foods & plants samples were determined by spectrophotometric methods. Integrated spectral studies of complexes [Cr (III, VI)-DPC], [Cr (VI)-bipy], [VO-SH], [V (V)-8-HQ] which included a study of the optimum conditions for the complexes formation by the investigation of the chemical and physical variables affecting each complex formation, the nature of complexes, the preparation of calibration curves of the complexes and treated the resulted data by modern statistical methods and study the interfering species. Interferences were removed to explain the reactions thermodynamically by determining Eï‚°cell, Keq. and ∆G values and includes a study of

Pure and Fe-doped zinc oxide nanocrystalline films were prepared
via a sol–gel method using -
C for 2 h.
The thin films were prepared and characterized by X-ray diffraction
(XRD), atomic force microscopy (AFM), field emission scanning
electron microscopy (FE-SEM) and UV- visible spectroscopy. The
XRD results showed that ZnO has hexagonal wurtzite structure and
the Fe ions were well incorporated into the ZnO structure. As the Fe
level increased from 2 wt% to 8 wt%, the crystallite size reduced in
comparison with the pure ZnO. The transmittance spectra were then
recorded at wavelengths ranging from 300 nm to 1000 nm. The
optical band gap energy of spin-coated films also decreased as Fe
doping concentra

The aim of the work is synthesis and characterization of new bidentate chalcone ligand type (NO):[(E)-1-(3-aminophenyl)-3-(4-chlorophenyl) prop-2-en-1-one] [H2L], from the reaction of 3-amino acetophenone with 4-chloro benzaldehyde to produce the ligand [H2L], the reaction was carried out in ethanol as a solvent under stirring. The prepared ligand [H2L] was characterized by FT-IR, UV-Vis spectroscopy, 1H, 13C-NMR spectra, Mass spectra, (C.H.N) and melting point. The complexes of ligand [H2L] were prepared with metal ion M(Π).Where M(Π) = (Mn ,Co ,Ni and Cu) at reflux ,using ethanol as a solvent and KOH as a base with molecular formula [M (H2L)2] +2 where: H2L= (C15H12NOCl). All the complexes were characterized by spectroscopic met

 Calculations and predication a theoretical formulas for the electron drift velocity in a gas medium are achieved to deduced the electron distribution function for different gas concentrations. The calculations are achieved by using the numerical solution for  Boltzmann transport equation in two term approximation, using the NOMAD  program for the drift velocity in a gas medium. It's necessary to note that the solution is essentially depending upon the elastic and inelastic collision cross section. In order to fixe a good accuracy for the using cross section it's necessary to calculate the electron distribution function and therefore study their behavior. Results about the electron drift velocity show that a decreasing pro

A novel technique for nanoparticles with a chemical method and impact for resistance bacteria methicillin-resistant Staphylococcus aureus (MRSA), UV-visible analysis confirmed the by Fourier transform infrared spectroscopy (FT-IR) and Energy dispersive X-Ray (EDX), Scanning electron microscope (SEM) and X-ray diffraction pattern estimation antimicrobial excellent antibacterial activity against MRSA (with zone of inhibition of 11 ± 02 mm , 9 ± 01 mm,8 ± 03 mm and 7.5 ± 02 mm and 6.5 ± 02 mm) at different concentrations (0.5 ,0.25, 0.125, 0.0625, 0.03125) mg/ml while good activity was 16 ± 03 mm at 17 ± 02 mm zone at 0.25, 0.125 mg/mL, respectively. The increase in microorganism resistance to antibiotics a couple of have caused

     In vivo study was made for the coumpounds 3-(ocetyl Salicyloyl)-5,6-O-isoprpy lideneL-ascorbicocid,2,3-(acetyl Salicyloyl )-5,6-o- isopropylidene-L-ascorbic acid and 2,3,5,6(acetyl Salicyloyl )-L- ascorbic acid .And a measurement was mod for the concentration of the liberated aspirin in blood samples a fter (2,3,4,6,8,10) hours of the initial dose for the animal .The results showed that the highest concentration of aspirin was after four hours of giving the dose to the animal which is in accordance with pharmacokinetics studies

This work aimed to study the effect of laser surface treatment on the mechanical characteristics and corrosion behaviour of grey cast iron type A159. Many technical applications used conventional surface treatment, but laser surface hardening has recently been used to enhance the surface properties of many alloys. The mechanical characteristics, including microstructure, microhardness, and wear resistance of A159 grey cast iron, were studied, in addition to corrosion behaviour. The experimental laser parameters in this work were 0.9, 1.2, and 1.5 KW power with continuous wave carbon dioxide lasers with scanning speeds of 10 and 12 mm/s were used. The results found that phase-transitional alterations in microstructure were influenced by lase

 In this work, a reactive DC magnetron sputtering technique was used to prepare TiO₂ thin films. The variation in argon and oxygen gases mixing ratios (4:1, 2:1, 1:1, 1:2, 1:4) was used to achieve optimal properties for gas sensing. In addition, an analysis of the optical XRD properties of TiO₂ thin films is presented. High-quality and uniform nanocrystalline films were obtained at a working gas pressure of 0.25 mbar and  1:4 (Ar/O₂) gas mixture. The optical properties showed a transparent thin film with uniform adherence to the substrate. The average transmission of the TiO₂ films deposited on the glass substrates was higher than 95% over the range of 400 to 800 nm.

The aim of this study is to identify the effect of particle size and to increase the concentration of Iraqi bentonite on rheological properties in order to evaluate its performance and to know if it can be used as drilling fluid without additives or not. In this study, Iraqi bentonite was carried out by mineral composition (XRD), chemical composition (XRF) and Particle size distribution (PSD), and its rheological properties were measured at different particle size and concentration. The results showed that when the particle size of Iraqi bentonite decreased, and the rheological properties were increased with increased concentration of Iraqi bentonite. Also, Iraqi bentonite was unable to use as drilling fluid without certain additives.