Background: The PMMA polymer denture base materials are low mechanical properties, adaptation of the denture base to underlying tissue is important for retention and stability of denture. The aim of the study was toevaluate the effect of mixtureZrO2-Al2O3 nanoparticles on impact strength, transverse strength, hardness, roughness, denture base adaptation of heat cured acrylic resin denture base material. Materials and methods: One hundred (100) specimens were prepared, the specimens were divided into five groups (20 specimens to each) according to the test type, each group was subdivided in to two subgroups (control and experimental) each subgroup consist of 10 specimens, the experimental group included mixture of 2% (ZrO2-Al2O3ratio2:1) b

New membrane electrodes for determination of ciprofloxacin hydrochloride were prepared depending on ciprofloxacin hydrochloride - phosphotungstic acid (CFH-PT) as an active material and these electrodes were made with three plasticizers: Di-octylphenylphosphonate(DOPH), Di-butyl phosphate (DBP)Tri-n-butyl phosphate(TBP), in PVC matrix. One of the ciprofloxacin electrodes was gave Nernstian slope equal to 57.21 mV/ decade for DOPH membrane with concentration range from 1.5×10-5 to1.0×10-1 M, and detection limit equal to 1.5×10-6 M .Lifetime was 93 days. Non- Nernstian responses equal to 39.40 and 30.70 mV/ decade for membranes DBP, TBP, respectively. These electrodes were gave concentration range from 1.0× 10-5 to 1.0×10-2 and from 4.0

Background: The marginal seal is essential for sealant success because penetration of bacteria under the sealant might allow caries onset or progression. The aim of the present study was to estimate and compare the microleakage of pit and fissure sealant after various methods of occlusal surface preparation. Materials and methods: Thirty non-carious premolars extracted for orthodontic reasons were equally divided into three groups. In group one, occlusal fissures were opened with round carbide bur, in group two, occlusal surfaces of the teeth were cleaned with a dry pointed bristle brush and samples of group three were cleaned with a slurry of fine flour of pumice in water using rubber cup. Then fissures of all teeth were etched using 35% p

The study showed that all extracts (aqueous, ethanolic and acetonic) of the leaves of Eucalyptus and Myrtus plants had a inhibitory effect on the growth of all types of yeasts studied, acetone extract recorded the highest inhibition of yeastat 100ppm concentration,The inhibition was 35mm, 34mm, 24mm and 20mm for Candida parapsilosis, Candida glabrata, Candida tropicalis and Candida albicans respectively, The experiments above showed the least significant differences at 0.05 level.The results ofE. Cammldulensis ethanolic tincture analysis has shown the presence of 44 biologically active substances. The main Eucalyptus leaves component was: 2-Bicyclo (2-2.1) heptanol (12.37%), Ledol (8.23%),1,2,4- Benzenetriol (8.45%) and that contain spathul

A new benzylidene derivative, namely N-benzylidene-5-phenyl-1,3,4-thiadiazol-2-amine (BPTA), has been synthesized and instrumentally confirmed with Elemental Analysis (CHN), Nuclear Magnetic Resonance (NMR), and Fourier Transform Infrared Spectroscopy (FT-IR). Titanium Dioxide (TiO2) nanoparticles (NPs) were synthesized and characterized by X-ray. The mutualistic complementary dependence of BPTA with TiO2 nanoparticles as anti-corrosive inhibitor on mild steel (MS) in 1.0 M hydrochloric acid has been tested at various concentrations and various temperatures. The methodological work was achieved by gravimetric measurement methods complemented with surface analysis. The synthesized inhibitor concentrations were 0.1 mM to 0.5 mM and the temper