Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f

The research aims to investigate the possibility of joint auditing in improving the market value of Iraqi companies listed on the Iraq Stock Exchange. The sample was represented by 10 Iraqi companies listed in the Iraq market for the period from 2014-2017 (2 years before implementation and 2 years after implementation) and the research was based on the idea that joint auditing enhances investor confidence and raises their level of security as a result of providing quality and reliable reports, and thus This indicates good news in the market that reflects on the performance of stocks and the market value of companies that adopt joint auditing. The results of the analysis indicate an improvement in the market value, but this improv

Nigella sativa seeds (NSS) are reputed traditionally and scientifically as a potent agent that promote milk secretion (galactagogue), but their mechanism of action is studied trivially. One suggestion was that these seeds are bio-transformed to sex hormones within the ovaries. Therefore, this investigation was designated to throw light on the action of these seeds in the absence of ovaries i.e. in male rats. Thirty Norway male albino rats were used in this investigation. They were divided into experimental (n=20,fed NSS 2g/ Kg body weight /day for 14 days) and control (n=10, fed placebo for 14 days). After sacrifice mammary gland and blood samples were obtained. Experimental rats revealed a significant increase (p (0.01>in

Background: Uncontrolled hyperphosphatemia is the main difficulty facing staff treating patients with end-stage renal disease on hemodialysis. Sevelamer and calcium-containing phosphate binders have been associated with cost burden and tissue calcification, respectively. Therefore, the current trial was targeted to investigate the efficacy of a new phosphate binder, ferric citrate, in a sample of Iraqi patients with end-stage renal disease on hemodialysis. Keywords: Ferric citrate, Hemodialysis Phosphate binder

Background: Sealers should demonstrate adhesive properties to dentin, decreasing the chance of endodontic treatment failure. Increased adhesive properties to dentin may lead to greater strength of the restored tooth, which may provide greater resistance to tooth fracture and clinical longevity of an endodontically treated tooth. The aim of this study was to evaluate the shear bond strength of Bioceramic iRoot SP sealer, AH plus sealer and Apexit plus sealer in absence or presence of smear layer using push out bond strength test. Materials and Methods: Sixty straight single roots of the mandibular premolars were selected for this study. All canals were instrumented using ProTaper rotary instruments to achieve tapered canal walls, instrumenta

The aim of this research is to identify the effect of Webinar technique on digital culture in the College of Education for pure sciences at Ibin Haitham, University of Baghdad. The research samples consisted of (68) male and female students from the Chemistry Department who are following classes during the (2019- 2020) academic year. The samples represent (42%) of the total number of (162) students split into control and experimental groups. For this purpose, the scientific contents for testing were determined. The experimental part is based on analysis of the results from experiments in (preliminary standard solutions, refractive index, Beer-Lambert law). To achieve the aim of the research in testing the measure of student's digital cultur

The effect of using different R -molar ratio under variable reaction conditions (acidic as well as basic environment and reaction temperature) have been studied. The overall experiments are driven with open and closed systems. The study shows that there is an optimum value for a minimum gelling time at R equal 2. The gelling time for all studied open system found to be shorter than in closed system. In acidic environment and when R value increased from 2 to 10, the gelling time of closed systems has increased four times than open systems at T=30 ?C and fourteen times when temperature reaction increased to 60 ?C. While in basic environment the influence of increasing R value was limited.