Ceramic body as a refractory was prepared by using shamoot, which is prepared by firing kaolin Duekhla at 1450 ºC at 2hr ,Flint clay ,Asbestos fiber(Anthophylite type)and Sodium silicts,Phosphoric acid solution as a binder . After miling, siving ,and mixing ,samples were formed, followed that drying, firing at different temperature. Phyical ,thermal and mechanical properties were measured .The conclusion behind the results that the refractory prepared from; 37.5% shamoote,25% Asbestos ,37.5% Flint clay and Phosforic acid solution fired at 1300 ºC gave a refractory material having melting temperature ;1490 ºC, thermal shock resistance 7 cycle, thermal conductivity 2.1w/m2.K, apperant porosity 22.69% ,apperant density 2.87gm/Cm 3 ,Linear shrinkage 3.5%, compressive strength 30.43 MPa and Impact strength 81.3J/Cm2 .
(115)
(107)
This current study was built on creating four electrodes based on molecularly imprinted polymers (MIPs). As the template using Cefalexin (CFX), 1-vinyl imidazole (VIZ) and vinyl acetate (VA) as monomer, and N, N-methylene bis acrylamide (MBAA) as cross-linkers and benzoyl peroxide as the initiator, two MIPs were prepared. The same composition was used in non-impressed polymers (NIPs) preparation, but without the template (Cefalexin). For the membranes preparation, numerous plasticizers, such as tri-oly phosphate (TOP) and di-octyl phthalate (DOP), were used in the PVC matrix, slop, detection limit, lifetime, and linearity range of CFX-MIPs electrodes are characteristics &nb
... Show MoreExperimental tests were carried to control lost circulation in the Khabaz oil field using different types of LCMs including Nano-materials. A closed-loop circulation system was built to simulate the process of lost circulation into formations. Two dolomite plugs were used from different depths of the formation of Azkand in Khabaz oil field. The experimentations were carried out to study the effect of different types of LCMs, cross-linked copolymer (FLOSORB CE 300 S), SiO2 NP, and Fe2O3 NP, on mud volume losses as a function of time.
The rheological measurements of the nanoparticles-reference mud system showed that both of the SiO2 NP and Fe2O3 NP w
... Show More
(4)
(4)
Background: to evaluate the effect of different dentifrices on the surface roughness of two composite resins (nanofilled-based and nanoceramic – based composite resins). Materials and methods: Forty specimens (diameter 12 mm and height of 2mm) prepared from different composite resin materials: Z350 (nanofilled composite, and Ceram-X (nanoceramic) .they were subjected to brushing simulation equivalent to the period of 1 year. The groups assessed were a control group brushed with distilled water (G1), Opalescence whitening toothpasteR (G2), Colgate sensitive pro-relief (G3) and Biomed Charcoal Toothpaste (G4). The initial and final roughness of each group was tested by surface roughness tester. The results were statistically analyzed using
... Show More
(1)
Background: Poly (methylmethacrylate) is not ideal in every aspect and has disadvantages such as insufficient surface hardness, increase water sorption and poor impact resistance and the latter being the primary cause of fracture of denture base resins. The aim of this study was to evaluate the effect of addition of silanized nano- hydroxyapatite (HA) on some properties of heat cured acrylic denture base material. Materials and methods: HA nano particles were first silanized with ï§MPS (tri methacryloxypropyletrimethoxy silane coupling agent) then ultrasonicated with methylmethacrylate (monomer) to disperse agglomerated nano particles and mixed with polymer. 2% by wt of HA nano particles was selected as the best concentration that add
... Show More
(4)
This study included prepared samples of epoxy reinforced by the novolac , aluminum , glass powder and epoxy reinforced by aluminum , glass powder and epoxy alone .They are used as reinforced materials of volum fraction amounting 40% . The mechanical properties inclouded ( tensile , compressive and wear) where the wear test inclouded different applied loads (5,10,15) . From the results showed the epoxy reinforced by aluminum and glass powder has higher compressive strength (56.91) Mpa and higher tensile strength (132.2) Mpa .But the epoxy alone has higher wear rate and the epoxy reinforced by aluminum and glass powder which have higher elasticity of modulus from the tensile test (315.7) Mpa
The main challenge is to protect the environment from future deterioration due to pollution and the lack of natural resources. Therefore, one of the most important things to pay attention to and get rid of its negative impact is solid waste. Solid waste is a double-edged sword according to the way it is dealt with, as neglecting it causes a serious environmental risk from water, air and soil pollution, while dealing with it in the right way makes it an important resource in preserving the environment. Accordingly, the proper management of solid waste and its reuse or recycling is the most important factor. Therefore, attention has been drawn to the use of solid waste in different ways, and the most common way is to use it as an alternative
... Show MoreThe current research is concerned with the prices of Goods and materials in the Iraqi slang a descriptive, lexicographic , and semantic study expressing the meanings of these names and their positions , as well as expressing the imaginations of Human mind , the popular mind in describing these goods with evaluating them besides the semantic of each word accordingly
The current research is divided into two parts , the first part is consisted of Vocalizations" words" That are arisen through cognitive naming that concentrate on the mental imaginations for the most important and sensitive such as colors , taste , shapes and forms impacts of Goods and materials according to users' ' taste for those words , on other hand, the second part of