In this paper, Cu2S/CdS solar cells were prepared with different thickness of CdS layer, these layers were prepared by using chemical spray pyrolysis technique. The chemical spray solution was prepared by mixing cadmium chloride CdCl2 and thiourea CS(NH2)2 of molar concentration 0.1 M/L, the CdS layer was formed after the solution was sprayed on hot Aluminum substrate at temperature 400°C. Experimentally the type of CdS film was found as n–type depending on the results of Hall Effect, the value of the Hall factor (RH) is about – 1.348 x 10–6 m3/C and the density of the majority charge carriers (N) is about 4.64x1018 cm–3. The prepared film was tested by using X-Ray diffraction; the result shows that the film was CdS with a polycrystalline structure. The Cu2S layer was prepared by using Chemical dip process; this layer was formed on the surface of the CdS film and it is always p-type. The heat treatment was utilized to form the p–n junction. The current-voltage characteristics of p-Cu2S\n-CdS solar cells was studied, the efficiency of the prepared cells of different thickness; (2.19, 2.52, 3.64, and 5.55) μm of CdS layer was calculated at 85.4 mW/cm2 light intensities, the results show that the thickness of the polycrystalline CdS film is an important parameter affecting the cell efficiency.
This work has been done with using of epoxy resin mixed with Granite powder were weighted by percent volume (5,10,15, and 20)%and then mixed with epoxy polymer to compose polymer composite. Hand lay-up technique is used in fabrication of the composite samples. Hardness test was carried out for the proper samples in both normal condition and after immersion in HCL (1 M and 2 M) solutions for periods ranging up to 10 weeks. After comparing the results between the polymer and their composite, the hardness increased with increasing Granite weight percent, it was found that Hardness were greater for the composites before immersion compared with their values after immersion.
In this paper an eco-epidemiological system has been proposed and studied analytically as well as numerically. The boundedness, existence and uniqueness of the solution are discussed. The local and global stability of all possible equilibrium point are investigated. The global dynamics is studied numerically. It is obtained that system has rich in dynamics including Hopf bifurcation.
The effect of the concentration of the colloidal nanomaterial on their optical limiting behavior is reported in this paper. The colloids of sliver nanoparticles in deionized water were chemically prepared for the two concentrations (31 ppm and 11ppm). Two cw lasers (473 nm Blue DPSS laser and 532 nm Nd:YAG laser) are used to compare the optical limiting performance for the samples. UV–visible spectrophotometer, transmission electron microscope (TEM) and Fourier Transformation Infrared Spectrometer (FTIR) were used to obtain the characteristics of the sample. The nonlinear refractive index was calculated to be in the order of 10-9 cm2/W. The results demonstrate that the observed limiting response is significant for 532nm. In addition, t
... Show MoreThis study was conducted to determine the effects of concentration of hydrochloric acids, temperature, and time on the hydrolysis of soya proteins (defatted soya flour) by determining the value of total protein nitrogen concentration, and amino nitrogen concentration of protein, peptides, and amino acids, and then calculated the hydrolysis rate of proteins.
The variables of the conditions of hydrolysis process was achieved in this study with the following range value of tests parameter:
- Concentration of HCl solution ranged between 1-7 N,
- Hydrolysis temperature ranged between 35-95 °C, and
- The time of hydroly
NiO0.99Cu0.01 films have been deposited using thermal evaporation
technique on glass substrates under vacuum 10-5mbar. The thickness
of the films was 220nm. The as -deposited films were annealed to
different annealing temperatures (373, 423, and 473) K under
vacuum 10-3mbar for 1 h. The structural properties of the films were
examined using X-ray diffraction (XRD). The results show that no
clear diffraction peaks in the range 2θ= (20-50)o for the as deposited
films. On the other hand, by annealing the films to 423K in vacuum
for 1 h, a weak reflection peak attributable to cubic NiO was
detected. On heating the films at 473K for 1 h, this peak was
observed to be stronger. The most intense peak is at 2θ = 37
ZSM-5 zeolite was synthesis under hydrothermal conditions at 175oC. The synthesis parameters have been investigated to find optimum synthesis method. Firstly, the crystallization time has been investigated to find the optimum crystallization time. Also, the ageing time was studied. The morphology, structure, and composition of the synthesized ZSM-5 zeolite were characterized using scanning electron microscopy (SEM), pH meter, viscometer, and X-ray powder diffraction (XRD). The bulk Si/Al ratio of ZSM-5 zeolite was in the range of 9.5—11.7. The synthesized ZSM-5 zeolite with appropriate ageing time could adjust crystal size and degree of the crystallinity. The crystal size of ZSM-5 zeolite obtained at an agei
... Show More
At atmospheric pressure and at a frequency of 9.1 kHz, a constructed magnetically stabilized tornado gliding arc discharge (MSGAD) system was utilized in this study to generate a non-thermal plasma with an alternating voltage source from 2,4,6,8 to 10 kV. Argon gas was used to generate the arc plasma with an adjustable flow rate using a flow meter regulator to stabilize the gas flow rate to 2 L/min. A gliding plasma discharge is achieved by a magnetic field for the purpose of a planned investigation. The influence of the magnetically stabilized tornado gliding arc discharge parameters such as magnetic field and applied voltage on microscopic tornado plasma parameters was studied. The electron temperature1was measured using a Boltzmann plot
... Show More
(2)
(2)
Abstract
In this research, a study of the behavior and correlation between sunspot number (SSN) and solar flux (F10.7) have been suggested. The annual time of the years (2008-2017) of solar cycle 24 has been adopted to make the investigation in order to get the mutual correlation between (SSN) and (F10.7). The test results of the annual correlation between SSN & F10.7 is simple and can be represented by a linear regression equation. The results of the conducted study showed that there was a good fit between SSN and F10.7 values that have been generated using the suggested mutual correlation equation and the observed data.