The aim of this paper is to introduce the definition of a general fuzzy norned space as a generalization of the notion fuzzy normed space after that some illustrative examples are given then basic properties of this space are investigated and proved.

For example when V and U are two general fuzzy normed spaces then the operator  is a general fuzzy continuous at u  V if and only if u in V implies S(u) in U.

     Our goal in the present paper is to introduce a new type of fuzzy inner product space. After that, to illustrate this notion, some examples are introduced. Then we prove that that every fuzzy inner product space is a fuzzy normed space. We also prove that the cross product of two fuzzy inner spaces is again a fuzzy inner product space. Next, we prove that the fuzzy inner product is a non decreasing function. Finally, if U is a fuzzy complete fuzzy inner product space and D is a fuzzy closed subspace of U, then we prove that U can be written as a direct sum of D and the fuzzy orthogonal complement    of D.

Interest has largely centered on the use of plant fibers to reinforce plastics, because these fibers are abundant and cheap. Carrot fibers (Curran) have been extracted from carrot, left over from carrot juice manufacture. The fibers of two sizes fine (50<µm) and coarse (100-150 µm) have been mixed with epoxy in four levels of loading (10, 20, 30, 40 wt %) respectively. Impact test, shore d hardness test and three point bending test of epoxy and carrot fiber-epoxy composites samples have been determined. The impact strength values of samples prepared with fine and coarse fibers increased as compared with pure epoxy sample. Hardness values increased, and the Young’s modulus values decreased with fiber content of both sizes.

The conventional solid-state reaction method was utilized to prepare a series of superconducting samples of the nominal composition Bi_2-xPb_0.3W_xSr₂Ca₂Cu₃O_10+d with 0≤x≤0.5 of 50 nm particle size of tungsten sintered at 850⁰C for 140h in air . The influence of substitution with W NPs at bismuth (Bi) sites was characterized by the X-ray diffraction (XRD), scanning electron microscopy (SEM) and dc electrical resistivity. Room temperature X-ray diffraction analysis revealed that there exists two phases, i.e. Bi-(2223) and Bi-(2212), in addition to the impurity phases of (SrCa) _2Cu2O3, Sr₂Ca₂Cu_7<

Single crystals of pure and Cu+2,Fe+2 doped potassium sulfate were grown from aqueous solutions by the slow evaporation technique at room temperature. with dimension of (11x9 x4)mm3 and ( 10x 8x 5)mm3 for crystal doping with Cu &Fe respectively. The influence of doping on crystal growth and its structure revealed a change in their lattice parameters(a=7.479 Ã… ,b=10.079 Ã… ,c=5.772 Ã…)for pure and doping (a=9.687 Ã…, b=14.926 Ã… ,c= 9.125 Ã…) & (a=9.638 Ã… , b= 8.045 Ã… ,c=3.271 Ã…) for Cu & Fe respectively. Structure analysis of the grown crystals were obtained by X-Ray powder diffraction measurements. The diffraction patterns were analyzed by the Rietveld refinement method. Rietveld refinement plo

Thin films of iridium doped indium oxide (In2O3:Eu)with different doping ratio(0,3,5,7,and 9%) are prepared on glass and single crystal silicon wafer substrates using spray pyrolysis method. The goal of this research is to investigate the effect of doping ratio on of the structural, optical and sensing properties . The structure of the prepared thin films was characterized at room temperature using X-ray diffraction. The results showed that all the undoped and doped (In2O3:Eu)samples are polycrystalline in structure and nearly stoichiometric. UV-visible spectrophotometer in the wavelength range (200-1100nm)was used to determine the optical energy gap and optical constants. The optical transmittance of 83% and the optical band gap of 5.2eV

أدى التغير السريع في البيئة الخارجية للمنظمة إلى  ظهور حالة من التنافس الشديد مما زاد تخوف الشركات من فقدان الحصة السوقية والخسارة . مما حدا بالمنظمات إلى الاهتمام بوجود مدير يحمل صفات وخصائص قيادية لما فيه من ميزات في تنظيم الإنتاج  ومقابلة الطلب وتقليل التكاليف وتطوير الأداء للحصول على ميزة تنافسية تحافظ او تزيد من حصتها السوقية وإرباحها .

تسعى الدراسة الى تحديد عدد من الاهداف كان اهمها معرفة الع

In the current study, we investigate the effect of  (La) substitution  instead of (Cu) on the properties of the superconductor compound  (Bi2Sr2Ca2Cu3-xLaxO10+δ)  with (x=0,0.05,0.1,0.15,0.2). The samples were  prepared  by solid state reaction method(SSR). Xray diffraction technique (XRD) was used to estimate the structural  properties of the specimens which show an orthorhombic crystalline structure for all the specimens.       The results show that the change in ( La) concentration  leads to decrease the concentration of (Bi-2223), increment in (Bi-2212 ) and(Bi-2201) with appearance of some impurities. Also decrease the critical temperature(Tc) with the increase

In this study a polymeric composite material was prepared by hand
lay-up technique from epoxy resin as a matrix and magnesium oxide
(MgO) as a reinforcement with different weight fraction (5,10,15,
and 20)% to resin. Then the prepared samples were immersed under
normal condition in H₂So₄(1 M) solution, for periods ranging up to
10 weeks. The result revealed that the diffusion coefficient
decreasing as the concentration of MgO increase. Also we studied
Hardness for the prepared samples before and after immersion. The
result revealed that the hardness values increase as the concentration
of MgO increase, while the hardness for the samples after immersion
in H₂SO₄ dec