Background: Removal of bacteria from the pulp system by instrumentation of an infected root canal, will be significantly reduced the number of bacteria, but it is well documented that instrumentation alone can-not clean and kill all bacteria found on the root canal walls. Antibacterial irrigants are needed to kill the remaining microorganisms. The aims of this study was to assess antibacterial effect of titanium tetrafluoride (TiF4) solution and brewing green tea against root canal bacteria and to compare with sodium hypochlorite and normal saline through microbiological and molecular studies. Materials and methods: Microbiological study was carried out to determine the concentration of titanium tetrafluoride and brewing green tea at which

The study included examination of three types of different origin and orange juice at the rate of recurring per sample, the results showed that the highest rates of acid (pH) in the A and juice were (4). And salts of calcium is 120 ppm in juice C and 86 ppm of magnesium in the juice B, for heavy metals the highest rate of lead .18 recorded ppm in juice B, 1.32 ppm of copper in juice A, 5 ppm of iron in the juice B, 1.3 ppm of zinc in the juice B, 0.05 ppm of aluminum in each of the sappy B and A, 0.02 ppm of cobalt in the juice B, 0.3 ppm of nickel in the juice B, 170.6 ppm sodium in C juice, but for the acids, organic that the highest rates were 3.2 part Millions of acid in the juice owner a, 260 ppm of the acid in the juice the ascorbi

Research includes three axes, the first is the average estimate time of achievement (day) to work oversight, to five supervisory departments in the Office of Financial Supervision Federal and then choose the three control outputs and at the level of each of the five departments above, and after analyzing the data statistically back to us that the distribution of the times of achievement It is the exponential distribution (Exponential Distribution) a parameter (q), and the distribution of normal (Normal Distribution) with two parameters (μ, σ²), and introduced four methods of parameter estimation (q) as well as four modalities parameter to estimate (

 Eight soil samples were selected around Najaf governorate at depth levels 40-50 cm. X-Ray Fluorescence (XRF) was used to determine the concentrations of major and trace elements. Liner and mass attenuation coefficient (µ, µ_ρ) have been determined at gamma energies (662, 1172,1332) keV using NaI (Tl) detector. The range of linear attenuation coefficients for calculated samples were (0.553-1.163) cm^-1, (0.122-0.178) cm^-1 and (0.049-0.105) cm^-1 at (662, 1172,1332) keV respectively. The range of mass attenuation coefficients obtained (0.39-0.76) cm²/gm, (0.087-0.117) cm²/gm and (0.0336-0.074) cm²/gm at (662, 1172,1332) keV respectively. The result

In the present work, lead silicate glasses have been prepared with
different amount of lead oxide content. Structure properties such as
X-ray diffraction, AFM, and FTIR analyses have been done. The
exceeding of PbO content more than 25wt% revealed a decreasing in
density. The X- ray revealed that the strongest peak related to
Hexagonal silica dioxide and the other crystal phases formed were
related to silica oxide (SiO2) and lead oxide (PbO). Growth and
decayed phases in X-ray have been observed with changing lead
oxide content. Homogeneous surface was obtained using AFM
analyzer with an average diameter around 100 nm. Infrared spectrum
is characterized by the presence of large absorption band between
120

     The change in the optical properties for samples of pure PVA and PVA /K2CrO4composite have been studied .The samples were prepared with different percentage (1,3,5,and 7)%wt of K2CrO4 by casting method technique .In this work ,we are study the absorption ,reflectance spectra ,absorption  coefficient, energy gap ,extinction coefficient ,and transmittance spectra as a function of wavelength range (200-800)nm ,Also  real and imaginary part of dielectric constant have been studied in the range of wave length .The results exhibit the optical properties change by the increase of K2CrO4 concentration, and the values of energy gap for indirect transitions decrease by the increase of the concentration of  K2CrO4

The local asphalt concrete fracture properties represented by the fracture energy, J-integral, and stress intensity factor are calculated from the results of the three point bending beam test made for pre notches beams specimens with deformation rate of 1.27 ^mm/min. The results revealed that the stress intensity factor has increased by more than 40% when decreasing the testing temperature 10˚C and increasing the notch depth from 5 to 30^mm. The change of asphalt type and content have a limited effect of less than 6%.

Cadmium Oxide thin films were deposited on glass substrate by spray pyrolysis technique at different temperatures (300,350,400, 500)oC. The optical properties of the films were studied in this work. The optical band-gap was determined from absorption spectra, it was found that the optical band-gap was within the range of (2.5-2.56)eV also width of localized states and another optical properties.