This study focuses on studying the effect of reinforced steel in detail, and steel reinforcement (tensile ratio, compression ratio, size, and joint angle shape) on the strength of reinforced concrete (compressive strength) Fc' and searching for the most accurate details of concrete divisions, their behavior, and corner resistance of reinforced concrete joint. The comparison of this paper with previous studies, especially in the studied properties. The conclusions of the chapter are summarized that these effects had a clear effect and a specific effect on the behavior and resistance of the reinforced concrete corner joints under the negative moments and under their influence and the resulting stress conditions. The types of defects that can

The catalytic cracking of three feeds of extract lubricating oil, that produced as a by-product from the process of furfural extraction of lubricating oil base stock in AL-Dura refinery at different operating condition, were carried out at a fixed bed laboratory reactor. The initial boiling point for these feeds was 140 ºC for sample (1), 86 ºC for sample (2) and 80 ºC for sample (3). The catalytic cracking processes were carried out at temperature range 325-400 ºC and initially at atmospheric pressure after 30 minutes over 9.88 % HY-zeolite catalyst load. The comparison between the conversion at different operating conditions of catalytic cracking processes indicates that a high yield was obtained at 375°C, according to gasoline pr

Periodontal diseases are inflammatory diseases, for which, scaling and root planning is the main approach. Diode laser therapy as an adjunct to non-surgical periodontal treatment has shown some beneficial effects.

Aim: The objective of this single randomized controlled clinical study was to assess the effect of a 940 nm diode laser as an adjunct to SRP therapy in the treatment of periodontal pockets.

 Methods: In this study, twenty patients in need of periodontal treatment with periodontal pocket ≥ 4 mm were selected for this split-mouth clinical study. Test group treated by diode laser 940 nm as an adjunct with SRP, control group treated by SRP in contralateral quadrants. Clinical

Sulfamethoxazole (SMX) was added to P-N,N-dimethyl amino benzaldehyde (PDAB) by condensation reaction in acidic medium to form, a yellow colored dye compound which exhibits maximum absorption (λmax) at 450.5 nm. The concentration of (SMX) was determined spectrophotometrically. The optimum reaction conditions and other analytical parameters were evaluated. In addition to classical univariate optimization, design of experiment method has been applied in optimization of the variables affecting the color producing reaction.    Beer’s law obeyed in the concentration range of 0.1-10 μg.mL-1 with molar absorptivity of 5.7950×104  L.mol-1.cm-1. The limit of detection and Sandell's sensitivity value were 0.078 μ

The purpose of this research work is to synthesize conjugates of NSAIDs (ibuprofen, and naproxen) with sulfadiazine as possible mutual prodrugs to overcome the local gastric irritation of NSAIDs with free carboxyl group by formation of ester linkage that supposed to remain intact in stomach and may hydrolyze in intestine chemically or enzymatically; in addition to that attempting to target the synthesized derivative to the colon by formation of azo bond that undergo reduction only by colonic bacterial azoreductaze enzyme to liberate the parent compound to act locally (treatment of inflammation and infections in colon)

In this study, sulfur was removed from imitation oil using oxidative desulfurization process. Silicoaluminophosphate (SAPO-11) was prepared using the hydrothermal method with a concentration of carbon nanotubes (CNT) of 0% and 7.5% at 190 °C crystallization temperature. The final molar composition of the as-prepared SAPO-11 was Al2O3: 0.93P2O5: 0.414SiO2. 4% MO/SAPO-11 was prepared using impregnation methods. The produced SAPO-11 was described using X-ray diffraction (XRD) and Brunauer-Emmet-Teller (N2 adsorption–desorption isotherms). It was found that the addition of CNT increased the crystallinity of SAPO-11. The results showed that the surface area of SAPO-11 containing 7.5% CNT was 179.54 m2/g, and the pore volume was 0.31