Introduction: The present study was performed to evaluate the influence of a 1064 nm fiber laser on shear bond strength (SBS) at the interface of titanium and resin cement. Methods: Forty titanium discs of 6 mm × 3 mm (diameter and thickness respectively) were categorized into four groups (n=10): control group without any surface treatment and three groups treated with a fiber laser with 81 ns pulse duration, 30 kHz frequency, 10000 mm/s scanning speed, 0.05 mm spot size, and different average power values (3, 5 and 7 W) depending on the tested group. Titanium disc characterization was performed by the scanning electron microscope (SEM) and surface roughness tester. Phase analysis was achieved using an X-ray diffractometer (XRD). F

Giardia lamblia is the worldwide most common intestinal protozoan parasite. It was indicated that Giardia is the most important agent that causes acute and chronic diarrhea in infants, young children and travelers. The aim was to detect the influence of host HLA alleles on the susceptibility to infection with G. lamblia in a sample of Iraqi patients. A total of (40) patients with giardiasis aged (14-39) years were registered. All of them were symptomatic and (40) healthy individuals matched age and sexes were included as controls. All patients were prepared to stool examination to detect G. lamblia and eliminated other pathogens, as well as human leukocyte antigen (HLA) class II alleles (DRB1) typing. The most common detected alleles in pat

Anastatica hierochuntica L. is distributed throughout Arabain Peninsula, and elsewhere it is locally called "Kuffe Maryam" .All parts of the plant are used in folk medicine. This study amid to investigate the effect of aqueous extract of anastatica hierochunctica L. on the cancer cell lines AMN-3. Anti cancer activity of aqueous extract of anastatica hierochunctica L. showed anticancer activity against AMN-3 cell line for twelve concentrations (0.04, 0.09, 0.195, 0.39, 0.78, 1.56, 3.125, 6.25, 12.5, 25, 50, 100) mg/mL in comparison with negative control.

Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction of (4% for AL

In the present study, the effect of Zinc nanoparticles on levels of (T3 , T4 and TSH) hormones was investigated. Zinc nanoparticles were synthesized by Laser induced plasma.The Nd: YAG Nd: YAG laser with a wavelength of 1064 nm was used to generate nanomaterials of the elements (zinc) upon collision with target atoms. Plasma generated by different laser intensity is generated. After confirming the preparation of zinc nanoparticles, XRD, AFM was examined, and the effect of these substances on the thyroid gland (T3, T4, TSH) was observed for two doses of each component (1 ml / kg, 4 ml / kg) after conducting a cytotoxicity examination of the lymphocytes of the rats extracted from Rat spleen was 1.8% less toxic to zinc, and as noted The

Anatomy studies were carried out in the experimental field, College of Agriculture, University of Baghdad to have better understanding of the influence of mulching with black polyethylene sheets, organic manure and chemical fertilizer on the anatomy changes in potato shoot and leaves tissues. Results showed that leaves area, leaves area index and chlorophyll percentage were significantly increased by using mulching and chemical fertilizer by (7463.70 cm2, 3.97, 45.33 SPAD units) respectively. Also this treatment significantly increased total stomata number and in both lower and upper sides of the leaf by (957,721,176) stomata /mm2 respectively. But by using mulching treatment with organic manure significantly increased vessels and sieve t

The creation and characterisation of biodegradable blend films based on chitosan and polyvinyl alcohol for application in a range of packaging is described. The compatibility between the chitosan and PVA polymers was good. Composite films had a compact and homogeneous structure, according to the morphology analysis. The mechanical test result of PVA/CH at concentrations 5% showed, that The higher values of TS recorded in sample (p1, with 40 MPa) while the lower values appeared in sample (p9, with 22.09 MPa), the TS decreased gradually as the amount of PVA increased in blend film. While the blend film of pure Chitosan exhibits a poor mechanical strength which makes it a poor candidate for packaging but Blending CH with PVA together improved