Nanostructure of chromium oxide (Cr₂O₃-NPs) with rhombohedral structure were successfully prepared by spray pyrolysis technique using Aqueous solution of Chromium (III) chloride CrCl₃ as solution. The films were deposited on glass substrates heated to 450°C using X-ray diffraction (XRD) shows the nature of polycrystalline samples. The calculated lattice constant value for the grown Cr₂O₃ nanostructures is a = b = 4.959 Å & c = 13.594 Å and the average crystallize size (46.3-55.6) nm calculated from diffraction peaks, Spectral analysis revealed FTIR peak characteristic vibrations of Cr-O Extended and Two sharp peaks present at 630 and 578 cm-1 attributed to Cr-O “stretching

In this work, porous silicon gas sensor hs been fabricated on n-type crystalline silicon (c-Si) wafers of (100) orientation denoted by n-PS using electrochemical etching (ECE) process at etching time 10 min and etching current density 40 mA/cm2. Deposition of the catalyst (Cu) is done by immersing porous silicon (PS) layer in solution consists of 3ml from (Cu) chloride with 4ml (HF) and 12ml (ethanol) and 1 ml (H2O2). The structural, morphological and gas sensing behavior of porous silicon has been studied. The formation of nanostructured silicon is confirmed by using X-ray diffraction (XRD) measurement as well as it shows the formation of an oxide silicon layer due to chemical reaction. Atomic force microscope for PS illustrates that the p

This work aimed to investigate the prevalence of pathogenic fungi and evaluate the antifungal activity of Trichoderma orientale FMR12486 crude extract against pathogenic fungi isolated from patients attending the National Center for Thoracic and Respiratory Diseases (having a history of tuberculosis) and consultant of Dermatology of Baghdad hospital, Iraq. A total of 80 clinical specimens were collected: 20 skin scrapings specimens and 60 sputum specimens. The results of direct examination by KOH 10% and culture showed that 11 (55%) cases from 20 skin specimens were positive for fungal infections, while in the sputum specimens, 28 (47%) cases from 60 were positive. Candida albicans represented the most common fungal infection isolat

     This work involves preparation of new metal complexes via reaction of two anthraquinone ligands with Mn(II), Co(II), Ni(II), Cu(II), Zn(II) and Cd(II) metal ions . The ligands are prepared by treatment of 1- and 2-anthraquinone with acetic anhydride.

      The complexes are characterized by different physicochemical methods; microelemental analysis, molar conductivity, FT-IR, UV-Vis spectra and magnetic measurements. The discussion of the outcome data of the prepared complexes indicates that all complexes are octahedral.

      The biological activity properties of the ligands and most of their complexes are studied using gram-positive and gram-negative bacteria, which indicate that only two of th

        People are comfortable with e-banking services, but they are exposed to a great deal of danger these days due to fraudulent acts such as password hacking and personal information theft. Everything individuals do online relies heavily on passwords. Using a password protects one's identity online, in forums, and through email. Online transactions are vulnerable to identity theft if they do not have a secure password. Internet users with critical statements are vulnerable to various assaults, including the theft and exploitation of user IDs and passwords. This paper introduces novel password encryption by fingerprint and a random number to make each password unique and robust against attacks, with a magnificent time elapsed o

The CuInSe2 (CIS) nanocrystals are synthesized by arrested precipitation from molecular precursors are added to a hot solvent with organic cap- ping ligands to control nanocrystal formation and growth. CIS thin films deposited onto glass substrate by spray - coating, then selenized in Ar- atmosphere to form CIS thin films. PVs were made with power conversion efficiencies of 0.631% as -deposited and 0.846% after selenization, for Mo coated, under AM 1.5 illumination. X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS) analysis it is evident that CIS have the chalcopyrite structure as the major phase with a preferred orientation along (112) direction and the atomic ratio of Cu : In : Se in the nanocrystals is nearly 1 : 1 : 2

In this study, an experimental investigation had conducted for six high strength laced reinforced concrete one-way slabs to discover the behavior of laced structural members after being exposed to fire flame (high temperature). Self-compacted concrete (SCC) had used to achieve easy casting and high strength concrete. All the adopted specimens were identical in their compressive strength of ( , geometric layout 2000 750 150 mm and reinforcement specifics except those of lacing steel content, three ratios of laced steel reinforcement of (0.0021, 0.0040 and 0.0060) were adopted. Three specimens were fired with a steady state temperature of  for two hours duration and then after the specimens were cooled suddenly by spraying water. The

In this study, the effect of fire flame on the punching shear strength of steel fiber reinforced concrete flat plates was experimentally investigated using nine half-scale specimens with dimensions of 1500×1500 mm and a total thickness of 100 mm. The main investigated variables comprised the steel fiber volume fraction 0, 1, and 1.5% and the burning steady state temperature 500 and 600 °C. The specimens were divided into three groups, each group consists of three specimens. The specimens in the first group were tested with no fire effect to be the reference specimens, while the others of the second and third groups were tested after being exposed to fire-flame effect. The adopted characteristics of the fire test were; (one hour) b