In this research, Mn-doped TiO2 thin films were grown on glass, Si and OIT/glass substrates by R.F magnetron sputtering technique with thicknesses (250 nm) using TiO2:Mn target under Ar gas pressure and power of 100 Watt. Through the results of X-ray diffraction, the prepared thin films are of the polycrystallization type after the process of annealing at 600°C for two hour The average crystalline size were 145.32, 280.97 and 261.23 nm for (TiO2:Mn) thin film on glass, Si and OIT/glass substrates respectively, while the measured surface roughness is between 0.981nm and 1.14 nm. The fabricated (TiO2:Mn) thin film on glass sensors have high sensitivity for hydrogen( H2 reducing gas) compared to the sensitivity for hydrogen gas on Si and OIT/

Organogel as a system was to estimate its capacity to delay and slow the drug release in the duodenum. The gelators, 12HSA (12-hydroxystearic acid), span 60. span 40 were used; the castor oil (CO) and anise oil (AO) also represented the liquid phase. To achieve the goal of this work was by using diclofenac sodium (DS). Organogels specifications were by estimating thermal attitude using tabletop rheology and differential scanning calorimetry (DSC). The organogel strength study was by applying oscillatory rheology tests the amplitude sweep and the frequency sweep. Realizing the morphology of the organogel was done utilizing an optical microscope. CO and AO binding capacity was also manifested. The transition temperatures for all organogels

The disposal of textile effluents to the surface water bodies represents the critical issue especially these effluents can have negative impacts on such bodies due to the presence of dyes in their composition. Biological remediation methods like constructed wetlands are more cost-effective and environmental friendly technique in comparison with traditional methods. The ability of vertical subsurface flow constructed wetlands units for treating of simulated wastewater polluted with Congo red dye has been studied in this work. The units were packed with waterworks sludge bed that either be unplanted or planted with Phragmites australis and Typha domingensis. The efficacy of present units was evaluated by monitoring of DO, Temperature, COD

The influence of fiber orientation and water absorption on fatigue crack growth resistance for cold cure acrylic (PMMA) reinforced by chopped and woven -glass-fibers were investigated. A weight of 2 g for chopped fibers and the same weight for woven -glass-fibers (one layer) were used to prepare samples. Some of these samples would storage in dry condition; the others were immersed in water for 15 days. Fatigue test was carried out. The results shows that, for PMMA, the initial bending stress for dry specimen was 3.392 N/cm2 and the number of cycles were 1364, the initial bending stress for wet samples was 4.20 N/cm2, and the number of cycles was 2411. The samples would cut in two pieces because of the cracks would propagated fast during

Reduce the required time for measuring the permeability of clayey soils by using new manufactured cell

In this research, main types of optical coatings are presented which are used as covers for solar cells, these coatings are reflect the infrared (heat) from the solar cell to increase the efficiency of the cell (because the cell’s efficiency is inversely proportional to the heat), then the theoretical and mathematical description of these optical coatings are presented, and an optical design is designed to meet this objective, its optical transmittance was calculated using (MATLAB R2008a) and (Open Filters 1.0.2) programs

سرطان البنكرياس هو مرض ذو معدل وفيات مرتفع، ولا يزال التشخيص المبكر لسرطان البنكرياس يمثل تحديًا. يظل معدل البقاء النسبي لمدة 5 سنوات أقل من 8%، والاستراتيجيات العلاجية غير فعالة في زيادة معدلات بقاء المريض على قيد الحياة. في خلايا سرطان البنكرياس، ارتبطت مقاومة العلاج بالتغيرات الجينية التي تؤدي إلى ظهور مسارات خلوية شاذة؛ ولذلك، هناك ما يبرر ايجاد استراتيجيات جديدة لعلاج هذا المرض. هنا، سعينا لاستكشاف

Transition metal complexes of Co(II), Ni(II), Cu(II), and Zn(II) with 2-(4-antipyrine azo)-4-nitroaniline derived from 4-aminoantipyrine and 4-nitroaniline were synthesized. Characterization of these compounds has been done on the basis of elemental analysis, electronic data, FT-IR, UV-Vis and 1HNMR, as well as magnetic susceptibility and conductivity measurements. The nature of the complexes formed were studied following the mole ratio and continuous variation methods, Beer's law obeyed over a concentration range (1×10-4 - 3×10-4 M). High molar absorbtivity of the complex solutions were observed. From the analytical data, the stoichiometry of the complexes has been found to be 1:2 (metal:ligand). On the basis of physicochemical data octa