This study aims to find the effect of water-cement ratio on the compressive strength of concrete by using ultrasonic pulse velocity test (UPVT). Over 230 standard cube specimens were used in this study, with dimensions of 150mm, and concrete cubes were cured in water at 20 °C. Also, the specimens used in the study were made of concrete with varied water-cement ratio contents from 0.48 to 0.59. The specimens were taken from Diyarbakir-Turkey concrete centers and tested at the structure and material science lab, civil engineering, faculty of engineering from Dicle University.  The UPV measurement and compressive strength tests were carried out at the concrete age of 28 days. Their UPV and compressive strength ranged

In this paper, a polymer-based composite material was prepared by hand Lay-up method consisting of epoxy resin as a base material reinforced by magnesium oxide powder once and silicon dioxide powder again and with different weight ratios (3, 6, 9 and 12) wt %. The three-point bending test was performed in normal conditions and after immersion in sulfuric acid. The results showed that the bending value decreased with the increase of the weighted ratio of the reinforcement material (MgO, SiO2). The Bending of samples reinforced by SiO2 was found to be less than the bending of samples reinforced by particles (MgO). For example, the bending of the SiO2 sample (0.32 mm) at the weighted ratio (3%) and for the MgO (0.18mm) sample at the weight

This study Studied Ministry of Hamdy Al-Buchachy(the first)and explain the features of
this Ministry in a critical time in the history of Iraq. The second world war had began and its
end had reached .The political situation in Iraq is so complicated. The Ministry had made
many things. The Ministry had situated in internal and external complicated time. The
situation in Iraq was so difficult, therefore the recommendor (Abdul-Ilah)asked Hamdy Al-
Bachachy to make be the head of the new governments Al-Bachachy had made irrelevant
government, thus it didn’t last more than three months and the British governorate and of
direct in terference in Iraq who worked to reduce the Iraqi army and the Minister of Defence
refus

ABSTRACT : Fifteenth isolates of C. sakazakii were obtained from previous studies of the sample (infant formula, cerebrospinal fluid and blood). All isolates C. sakazakii identification based on microscopic, biochemical test and confirmed by 16SrRNA. We studied the movement of all isolates and study adhesion to polystyrene plate, adhesion and invasion to Esophageal adenocarcinoma (SKG-GT-4) for four isolates [Cerebrospinal fluid (CSF5), Bloods (B 1), Dialak (A1c), Novolac Allernova (C1)] and its cytotoxicity. Results showed that all isolates can move after 4 hours of incubation and increased after 8 hours, the isolates moved to different distances strong, medium, and weak. The results showed that the number of C. sakazakii colony adherent t

The most important topics that constitute the aesthetic and substantive aspect of the theatrical performance represented by the spatial environment of the presentation and the proposed virtual place that contains the technical and artistic elements of the presentation and highlights the strength of influence on it. In light of the above, the researchers divided the topic into four chapters.

The first chapter contained (the methodological framework), which included the research problem with regard to the directing treatments between the directors in establishing or creating theatrical venue, the importance of the research and the aim of the research, and the limits of the research to conclude the chapter by defining the terms.

SAPO-11 is synthesized from silicoaluminophosphate in the presence of di-n-propylamine as a template. The results show that the sample obtained has good crystallinity, 396m2/g BET surface area, and 0.35 cm3/g pore volume. The hydroisomerization activity of (0.25)Pt (1)Zr (0.5)W/SAPO-11 catalyst was determined using n-decane and base oil. All hydroisomerization experiments of n-decane were achieved at a fixed bed plug flow reactor at a temperature range of 200-275°C and  LHSV 0.5-2h-1.  The results show that the n-decane conversion increases with increasing temperature and decreasing LHSV, the maximum conversion of 66.7 % was achieved at temperature 275°C and LHSV of 0.5 h-1. Meanwhile, the same catalyst was used to improve base oil spec

   SAPO-11 is synthesized from silicoaluminophosphate in the presence of di-n-propylamine as a template. The results show that the sample obtained has good crystallinity, 396m²/g BET surface area, and 0.35 cm³/g pore volume. The hydroisomerization activity of (0.25)Pt (1)Zr (0.5)W/SAPO-11 catalyst was determined using n-decane and base oil. All hydroisomerization experiments of n-decane were achieved at a fixed bed plug flow reactor at a temperature range of 200-275°C and  LHSV 0.5-2h^-1.  The results show that the n-decane conversion increases with increasing temperature and decreasing LHSV, the maximum conversion of 66.7 % was achieved at temperature 275°C and LHSV of 0.5 h^-1

This paper presents the Taguchi approach for optimization of hardness for  shape memory alloy (Cu-Al-Ni) . The influence of  powder metallurgy parameters on hardness has been investigated. Taguchi technique and ANOVA were used for analysis. Nine experimental runs based on Taguchi’s L9 orthogonal array were performed (OA),for two parameters was study (Pressure and sintering temperature) for three different levels (300 ,500 and 700) MPa ,(700 ,800 and  900)^oC respectively . Main effect, signal-to-noise (S/N) ratio was study, and analysis of variance (ANOVA) using  to investigate the micro-hardness characteristics of the shape memory alloy .after application the result of study shown the hei