New mixed ligand complexes of some metal ions Zn(II), Cd(II) and Hg(II) were prepared by reacting with mixture of two bidentate ligands [ HL = (P-methyl anilino) –P– chloro phenyl acetonitrile and en = ethylene diamine] in a molar ratio of 1:1:1[ M : HL : en] in ethanol . The ligand HL was previously prepared by Strecker’s procedure which includes the reaction of p- toluidine with P- chlorobenzaldehyde in the presence of KCN in acidic medium. The structures of new compounds were identified by elemental analyses, atomic absorption and thermal analyses TG/DTG in addition to FTIR and U.V-VIS. Spectra. The electrical conductivity measurements of metal complexes were also determined. From the obtained data the octahedral structure was s

In this study, doped thin cadmium peroxide films were prepared by pulsed laser deposition with different doping concentrations of aluminium of 0.0, 0.1, 0.3, and 0.5 wt.% for CdO2(1-X)Al(X) and thicknesses in the range of 200 nm. XRD patterns suggest the presence of cubic CdO2 and the texture factor confirms that the (111) plane was the preferential growth plane, where the texture factor and the grain size decreased from 2.02 to 9.75 nm, respectively, in the pure sample to 1.88 and 5.65 nm, respectively, at a concentration of 0.5 wt%. For the predominant growth plane, the deviation of the diffraction angle Δθ and interplanar distance Δd from the standard magnitudes was 2.774° and 0.318 Å, respectively, for the pure sample decreased to

In this study, SnO2 nanoparticles were prepared from cost-low tin chloride (SnCl2.2H2O) and ethanol by adding ammonia solution by the sol-gel method, which is one of the lowest-cost and simplest techniques. The SnO2 nanoparticles were dried in a drying oven at a temperature of 70°C for 7 hours. After that, it burned in an oven at a temperature of 200°C for 24 hours. The structure, material, morphological, and optical properties of the synthesized SnO2 in nanoparticle sizes are studied utilizing X-ray diffraction. The Scherrer expression was used to compute nanoparticle sizes according to X-ray diffraction, and the results needed to be scrutinized more closely. The micro-strain indicates the broadening of diffraction peaks for nano