The problem of the damage caused by terrorist acts has raised many difficulties in many countries, including Iraq, which requires the existence of a law that sets out sufficient rules for compensating the victims of terrorist acts, in order to compensate them for the harm they have not suffered. It may be difficult or impossible for them to identify causing damage, and therefore unable to obtain compensation by applying the traditional rules of liability that require proof of fault and identify the culprit. The security funds come as an appropriate alternative that pays compensation in such cases for victims to reparation for the damage they suffered. Therefore, this problem remains one of the most problems that Iraq suffers from it, which

Alloy of (HgTe) has been prepared succesful in evacuated qurtz ampoule at pressure 4×10-5torr, and melting temperature equal to 823K for five days. Thin films of HgTe of thickness 1μm were deposited on NaCl crystal by thermal evaporation technique at room temperature under vacuum about 4×10-5torr as well as investiagtion in the optical porperties included (absorption coefficient , energy gap) of HgTe films and The optical measurements showed that HgTe film has direct energy gap equal to 0.05 eV. The optical constants (n, k, εr, εi) have been measured over will range (6-28)μm.

Background Many antidiabetic medications with distinct modes of action are available, The sodium glucose cotransporter-2 (SGLT-2) inhibitors are among the most recent oral antihyperglycemic medications. The American Diabetes Association recommends metformin, a biguanide medication, as the first option for oral control of type 2 diabetes because it has demonstrated promise in this regard. Aim of the study To evaluate and compare the effects of metformin and SGLT-2 inhibitors on general urine parameters in T2DM patients from Iraq. Method a prospective cohort study where 101 adult patients of both sexes aged under 70 years and newly diagnosed with T2DM, patients were divided into two groups, Metformin group (n=52), where metformin was p

SARS-CoV-2 stands for severe acute respiratory syndrome coronavirus 2 which is the causative agent of spreading coronavirus disease 2019 that is known as COVID-19 pandemic, the disease leads to severe acute respiratory illness. Matrix metalloproteinases- 9 (MMP-9) plays several important physiological functions. This enzyme could also be implicated in the "cytokine storm" in some way, which may represent one of the possible scianrios during coronavirus infection, in addition to its role in the mechanism of lung fibrosis on molecular basis.. The tissue inhibitors of metalloproteinase (TIMPs) are well characterized for controlling the activity of MMPs in extracellular matrix remodeling. They also considered as signaling molecules anal

SARS-CoV-2 stands for severe acute respiratory syndrome coronavirus 2 which is the causative agent of spreading coronavirus disease 2019 that is known as COVID-19 pandemic, the disease leads to severe acute respiratory illness. Matrix metalloproteinases- 9 (MMP-9) plays several important physiological functions. This enzyme could also be implicated in the "cytokine storm" in some way, which may represent one of the possible scianrios during coronavirus infection, in addition to its role in the mechanism of lung fibrosis on molecular basis.. The tissue inhibitors of metalloproteinase (TIMPs) are well characterized for controlling the activity of MMPs in extracellular matrix remodeling. They also considered as signaling molecules anal

Compounds were prepared from In2O3 doped SnO2 with different doping ratio by mixing and sintering at 1000oC. Pulsed Laser Deposition PLD was used to deposit thin films of different doping ratio In2O3: SnO2 (0, 1, 3, 5, 7 and 9 % wt.) on glass and p-type wafer Si(111) substrates at ambient temperature under vacuum of 10-3 bar thickness of ~100nm. X-ray diffraction and atomic force microscopy were used to examine the structural type, grain size and morphology of the prepared thin films. The results show the structures of thin films was also polycrystalline, and the predominate peaks are identical with standard cards ITO. On the other side the prepared thin films declared a reduction of degree of crystallinity with the increase of doping ra

Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K

The main aim of the research is to identify the impact of the application of IFRS for SMEs on optimizing the utility of information for financial reports. To answer the questions and test the hypotheses of the research, researchers relied on the descriptive analytical approach. First, the researchers clarified the theoretical aspect through previous studies, and then they analyses d the results of the applied study by testing the hypothesis using the SPSS.

A questionnaire was distributed after evaluation and arbitration by a number of specialists on selected sample. The sample of 120 respondents consists of general managers, department directors, head of departments, accountants, auditors and financial controllers working in the

The study of surface hardness, wear resistance, adhesion strength, electrochemical corrosion resistance and thermal conductivity of coatings composed from sodium silicate was prepared using graphite micro-size particles and carbon nano particles as fillers respectively of concentration of (1-5%), for the purpose of covering and protecting the oil distillation towers. The results showed that the sodium silicate coating reinforced with carbon nano-powder has higher resistance to stitches, mechanical wear, adhesive and thermal conductivity than graphite/sodium silicate composite especially when the ratio 5% and 1%, the electrochemical corrosion test confirmed that the coating process of stainless steel 304 lead to increasin

Zinc Oxide (ZnO) thin films of different thickness were prepared
on ultrasonically cleaned corning glass substrate, by pulsed laser
deposition technique (PLD) at room temperature. Since most
application of ZnO thin film are certainly related to its optical
properties, so the optical properties of ZnO thin film in the
wavelength range (300-1100) nm were studied, it was observed that
all ZnO films have high transmittance (˃ 80 %) in the wavelength
region (400-1100) nm and it increase as the film thickness increase,
using the optical transmittance to calculate optical energy gap (Eg
opt)
show that (Eg
opt) of a direct allowed transition and its value nearly
constant (~ 3.2 eV) for all film thickness (150