This study concerns the removal of a trihydrate antibiotic (Amoxicillin) from synthetically contaminated water by adsorption on modified bentonite. The bentonite was modified using hexadecyl trimethyl ammonium bromide (HTAB), which turned it from a hydrophilic to a hydrophobic material. The effects of different parameters were studied in batch experiments. These parameters were contact time, solution pH, agitation speed, initial concentration (C0) of the contaminant, and adsorbent dosage. Maximum removal of amoxicillin (93 %) was achieved at contact time = 240 min, pH = 10, agitation speed = 200 rpm, initial concentration = 30 ppm, and adsorbent dosage = 3 g bentonite per 1L of pollutant solution. The characterization of the adsorbent, modi

Thermal management has become a major issue in the latest high performance computing machines because high CPU temperatures result in inefficient performance and decreased hardware life span. In this work, the cooling performance of a finned metal foam heat sink (FMFHS) was examined. The pore density values of tested copper metal foam (CMF) samples with different values of PPI 5, 10 and 20, with a constant porosity of 90%. For reference, these samples were measured by a conventional Aluminum plate-fin heat sink (CHS). The work was performed under experimental conditions in which air directed over the heat sink surface at air velocities (2.5, 3.0 and 3.5 m/s). The environmental temperature was fixed at 27 °C. Findings

The introduction of concrete damage plasticity material models has significantly improved the accuracy with which the concrete structural elements can be predicted in terms of their structural response. Research into this method's accuracy in analyzing complex concrete forms has been limited. A damage model combined with a plasticity model, based on continuum damage mechanics, is recommended for effectively predicting and simulating concrete behaviour. The damage parameters, such as compressive and tensile damages, can be defined to simulate concrete behavior in a damaged-plasticity model accurately. This research aims to propose an analytical model for assessing concrete compressive damage based on stiffness deterioration. The prop

Nanofluids, liquid suspensions of nanoparticles (NPs) dispersed in deionized (DI) water, brine, or surfactant micelles, have become a promising solution for many industrial applications including enhanced oil recovery (EOR) and carbon geostorage. At ambient conditions, nanoparticles can effectively alter the wettability of the strongly oil-wet rocks to water-wet. However, the reservoir conditions present the greatest challenge for the success of this application at the field scale. In this work, the performance of anionic surfactant-silica nanoparticle formulation on wettability alteration of oil-wet carbonate surface at reservoir conditions was investigated. A high-pressure temperature vessel was used to apply nano-modification of oil-wet

Due to increasing cost of asphalt binder, significant economic savings can be realized by using the amount from reclaimed asphalt pavement (RAP) in the production of new hot mix asphalt (HMA). Moreover, this is an environmentally friendly option as it reduces the demand for virgin materials. It has to be remarked that in Iraq RAP is not used in the production of HMA and this valuable material is mostly degraded for use in lower value applications. Four mixtures were designed, which contains three different percent RAP, it is (0%, 5%, 15%) with asphalt grade (40-50) and (25%) with asphalt grade (60-70), it has been changed the grade of asphalt when adding RAP (25%) to compensate for the aged binder in the RAP when adding to mixture. All type

Allopurinol derivative were prepared by reacting the (1-chloroacetyl)-2-Hydropyrazolo{3,4-d}pyrimidine-4-oneiwith 5- methoxy- 2-aminoibenzothiazoleiunder certain conditions to obtain new compound ( N- (2-aminoacetyl (5-methoxy) benzothiazole -2yl) (A4), Reaction of 5-(P-dimethyl amine benzene)-2-amino-1,3,4- oxadiazole in the presence of potassium carbonate anhydrous to yield new compound (N-(2- aminoacetyl-5-(P-dimethyl amine benzene )-1,3,4-oxadiazoles-2-yl)(A30) and Azo compound (N-(5-(Azo-2-hydroxy-5-amino benzene)-1,3-Diazol-2yl)Allopurinol(A46). The structure of prepared compounds were confirmed by (FT-IR) technique and their physical properties. The synthesized compounds were tested for cytotoxicity, Xanthine oxidase inhibiti