Background: Polymethylmethacrylate (PMMA) has relatively unsatisfactory mechanical properties such as low flexural strength and impact strength also dimensional instability. Material and method: Zirconium silicate nanoparticles were coated with a layer of trimethoxysilylpropylmethacrylate (TMSPM) before sonication in monomer (MMA) with the percentages 1% and 1.5% by weight then mixed with powder using conventional procedure, (150) samples were prepared and divided into three groups, each group consisted of (50) samples, the first group prepared from PMMA without addition (control), another group with the addition of 1% wt Zrsio4 nanoparticles (experimental) and the third one with 1.5% wt Zrsio4 nanoparticles (experimental). Each group was divided into 5 sub-groups according to the test performed. The tests conducted impact strength, transverse strength, indentation hardness (shore D), surface roughness, water sorption and solubility. The size, shape and distribution of nanofiller were estimated using scanning electron microscope (SEM) .The results were statistically analyzed using ANOVA and LSD test. Result: Highly significant increase in impact strength, transverse strength and surface hardness occurred with the incorporation of 1.5% wt Zirconium silicate nanofiller but non-significant increase in impact strength, significant increase in transverse strength and highly significant increase in surface hardness occurred with the incorporation of 1% wt Zrsio4 nanofiller. Non-significant increase in surface roughness with both 1% and 1.5% wt Zrsio4 . Highly significant decrease in water sorption and solubility with 1.5% wt Zrsio4 nanofiller and non-significant decrease in water sorption and solubility with 1% wt Zrsio4 compared with control group. Conclusion: The maximum increase in impact strength, transverse strength, and surface hardness was observed in denture base nano composite containing 1.5% Zrsio4. In addition, highly significant decrease in water sorption and solubility and non-significant increase in surface roughness was also noticed.
This study was conducted in Al-Salam station for Dairy cattle/private sector, for the period from 1-11-2016 to 1-11-2017, to determine the association between BTN1A1 gene polymorphism and reproductive efficiency indicator and heat tolerance in 50 Holstein cows. The results of BTN1A1 gene analysis showed a highly significant Different (P<0.01) between genotypes of BTN1A1 gene’s genotypes AA, AB the percentage were 72.00, 28.00 % respectively. Results showed that services per conception and days open was significantly (P<0.05) affected by polymorphism of BTN1A1 gene and for cows with AA genotype, there was also a significant difference (P<0.05) between the genotypes of BTN1A1 gene for IgG concentration in calves blood who belong to mother
... Show More
(2)
يهدف البحث الى أعداد بعض تمرينات الاساسية لسلاح الشيش بأستخدام المرايا في تطوير قدرة مستوى تعلم الطالبات في المبارزة ومعرفة الفروق بين المجموعتين التجريبي والضابطة بتأثير استخدام المرايا في مستوى اداء بعض مهارات سلاح الشيش لطالبات المرحلة الثالثة , وقد أستخدمت الباحثتان المنهج التجريبي على عينة من طالبات المرحلة الثالثة , وقد بلغ عددهم (45) طالبة , وقد خرجت الباحثتين بعدة أستنتاجات وهي:- - أن المنهاج التعليمي
... Show More
(1)
In this work Study effect of annealing temperature on the Structure
of a-Se and electrical properties of a-Se/c-Si hetrojunction have been
studied.The hetrojunction fabricated by deposition of a-Se film on c-
Si using thermal evaporation.
Electrical properties of a-Se/ c-Si heterojunction include I-V
characteristics, in dark at different annealing temperature and C-V
characteristics are considered in the present work.
C-V characteristics suggested that the fabricated diode was
abrupt type, built in potential determined by extrapolation from
1/C2-V curve. The built - in potential (Vbi) for the Se/ Si System
was found to be increase from 1.21 to 1.62eV with increasing of
annealing temperature
Through this study, the following has been proven, if is an algebraically paranormal operator acting on separable Hilbert space, then satisfies the ( ) property and is also satisfies the ( ) property for all . These results are also achieved for ( ) property. In addition, we prove that for a polaroid operator with finite ascent then after the property ( ) holds for for all.
(1)
في الدراسة الحالية، تم تصنيع جسيمات ZrO2 النانوية باستخدام مستخلص نباتي مشتق من نبات Vitex agnus castus، ووسط قلوي مثل هيدروكسيد الصوديوم. تم استخدام أسلوب التخليق الحيوي لتحضير جزيئات أوكسيد الزركونيوم النانوية لهذا المشروع البحثي. تتميز هذه الطريقة عن غيرها بسبب فعاليتها من حيث التكلفة وبساطتها وقلة المخاطر المحتملة. وتم تشخيص العينات المحضرة باستخدام المجهر الإلكتروني النافذ TEM، المجهر الإلكتروني الماسح SEM،
... Show More
(2)
Thin films of Nb2O5 have been successfully deposited using the DC reactive magnetron sputtering technique to manufacture NH3 gas sensors. These films have been annealed at a high temperature of 800°C for one hour. The assessment of the Nb2O5 thin films structural, morphological, and electrical characteristics was carried out using several methods such as X-ray diffraction (XRD), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDS), Hall effect measurements, and sensitivity assessments. The XRD analysis confirms the polycrystalline composition of the Nb2O5 thin films with a hexagonal crystal structure. Furthermore, the sensitivity, response time, and recovery time of the gas sensor were evaluated for the Nb2O5 thin film
... Show More
(2)
(1)
In the present work, pulsed laser deposition (PLD) technique was applied to a pellet of Chromium Oxide (99.999% pure) with 2.5 cm diameter and 3 mm thickness at a pressure of 5 Tons using a Hydraulic piston. The films were deposited using Nd: YAG laser λ= (4664) nm at 600 mJ and 400 number of shot on a glass substrate, The thickness of the film was (107 nm). Structural and morphological analysis showed that the films started to crystallize at annealing temperature greater than 400 oC. Absorbance and transmittance spectra were recorded in the wavelength range (300-
4400) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of d
(2)
(35)
(34)