The bacterial isolates were obtained from Al-Kindi Hospital were diagnosed by the Vitek-2 system and re confirm by 16srRNA gene as S. aurous, the results were shown 20 isolates (66.7%) out of 30 isolates were positive to protease production. All bacterial isolates (100%) were sensitive to Gentamicin and Levofloxacin. but resistant (100%) to aztreonam. The best temperature for enzyme production from bacteria was 37 °C, and the best pH for enzyme production was 7. Partial purification of the bacterial enzyme (protease) was carried out using short steps included ammonium sulfate 65% saturation, ion exchange using DEAE- cellulose column and then applied on gel filtration chromatography using Sephadex G-200 column. The enzymatic activit

The present research had dealt with preparing  bars  with the length of about  (13 cm) and  adiametar  of  (1.5 cm) of composite materials with metal  matrix  represented by (Al-Cu-Mg) alloy cast enforced by (ZrO₂) particles with chosen weight  percentages (1.5, 2.5 ,3.5, 5.5 %). The base  cast and the composite  materials were prepared by casting method by uses vortex  Technique inorder to  fix up (ZrO₂) particles in homogeneous way on  the  base cast. In addition to  that, two main groups of composite materials were prepared depending on the particles size of (ZrO₂) , respectively.       &n

The problem of research is that there are ways to protect and sustain environmentally important sites in Iraq. There are no documentary sources for these sites, such as the natural landscape of natural and important natural resources, which suffer from severe environmental neglect

The Bi2Se3 compound was synthesis by fusing initial compounds consisting of
extra pure elements in stoichiometric ratio from elements compound, charged inside
quartz ampoule. The crystal growth of Bi2Se3 carried out using Brighaman technique
process from melting f (Bi+Se ) at temperature of 810 ºC for about 48 hrs. Single crystal
of Bi2Se3 has been grown in direction (211) after slow cooling on account of heat
gradient to zone furnaces at cooling rate (1-3) C/hr. The structure study of the compound
was determined by x-ray diffraction technique, which it has bismuthinite structure and
orthorhombic unit cell with lattice parameters of a=10.2678 Å, b=11.2392 Å and
c=5.1737 Å

In this paper thermo-hydrodynamic characteristics were investigated experimentally for a new type shell-helical coiled tube heat exchanger used as a storage tank of closed loop solar water heater system. Triple concentric helical coils were made of copper tubes of (12.5mm OD and 10mm ID) with coils diameter of (207, 152.2, 97mm) for outer, middle and inner coils respectively. The experiments were carried out during a clear sky days of (March and April 2012). The parameters studied in this work are: history of average temperature of shell side of the storage tank, collector heat gain, heat rejected from coils to shell side of the storage tank, collector efficiency, thermal effectiveness of the heat exchanger (storage tank), and pressure d

AlPO4 solid acid catalyst was prepared in order to use it in transesterification reaction of edible oil after supporting it with tungsten oxide. The maximum conversion of edible oil was obtained 78.78% at catalyst concentration (5gm.), temperature 70°Ϲ, 30/1 methanol/edible oil molar ratio, and time 5hr. The study of kinetics of the transesterification reaction of edible oil indicates that the reaction has an order of 3/2, while the value of activation energy for  transesterification reaction is 51.367 kJ/mole and frequency factor equal 26219.13(L/ mol.minute).

The study included 20 birds of Pekin duck (Anas platyrhnchos domesticus) for study the histological of uropygial gland (10 males + 10 females), the weights were between (1411-1582 gm) for males and (1350-1980 gm) female. Routine Histological Techniques was done and stained by Hematoxylin and Eosin (H&E), Periodic Acidic Schiff (PAS), Masson's trichrome stains. Histological sections of the uropygial gland of Pekin ducks showed that the gland consist of the capsule, parenchyma, isthmus and uropygial papillae. The capsule consist of Dense irregular connective tissue. The mean thickness of capsule around the gland lobes were (56.321?17.206µm) and around the uropygial papillae were (67.208?14.996 µm). The capsule tissues continuous in betwe

The structural properties of ternary chalcopyrite AgAlSe2 compound alloys and thin films that prepared by the thermal evaporation method at room temperature on glass substrate with a deposition rate (5±0.1) nm s-1 for different values of thickness (250,500 and 750±20) nm, have been studied, using X-ray diffraction technology. As well as, the optical properties of the prepared films have been investigated. The structural investigated shows that the alloy has polycrystalline structure of tetragonal type with preferential orientation (112), while the films have amorphous structure. Optical measurement shows that AgAlSe2 films have high absorption in the range of wavelength (350-700 nm). The optical energy gap for allowed direct transition we