Background: Polymethyl methacrylate (PMMA) is the most commonly used material in denture fabrication. The material is far from ideal in fulfilling the mechanical requirements, like low impact and transverse strength, poor thermal conductivity. The purpose of this study was to evaluate the effect of addition a composite of surface treated Nano Aluminum oxide (Al2O3) filler and plasma treated polypropylene fiber (PP) on some properties of denture base material. Materials and methods: One hundred fifty prepared specimens were divided into 5 groups according to the tests, each group consisted of 30 specimens and these were subdivided into 3 groups (unreinforced heat cured acrylic resin as control group),reinforced acrylic resin with( 0.5%wt Nano Al2O3 and2.5%wt plasma treated PP fibers) group and reinforced acrylic with(1%wt Nano Al2O3 and 2.5%wt plasma treated PP fibers group).The tests were impact strength, transverse strength, indentation hardness(shore D), surface roughness thermal conductivity. The results were statistically analyzed using ANOVA test. Results: A highly significant increase in impact strength, surface hardness, thermal conductivity with the addition of 0.5%wt. (Al2O3) and 2.5%wt PP fiber to(PMMA),also there is a significant increase in surface roughness and non significant increase in transverse strength. At the concentration of 1%wt nano (Al2O3) and 2.5%wt PP fiber there is a highly significant increase in impact strength surface hardness and thermal conductivity. Non-significant differences were shown in transverse strength and significant increase in surface roughness. Conclusion: The addition of a composite of Al2O3 nanoparticles and PP fiber to PMMA improves the impact strength, surface hardness and thermal properties, surface roughness while non-significant difference in transverse strength.
A field experiment was carried out at the research station of the College of Agriculture - Wasit University / Kut, during the fall season 2021 in soil with texture (sandy mixture) using the RCBD design in the arrangement of splintered plates and with three replications, to study the effect of spraying different combinations of organic emulsion (Appetizer) and NPK nano fertilizer with urea fertilizer on the growth of synthetic cultivars of yellow corn. The main panels included three synthetic varieties of yellow corn (Fajr1, Sumer and Baghdad3), which symbolized by (V1,V2,V3) in sequence, while the secondary panels included five fertilization treatments in which mineral fertilizer (urea) was used 46% nitrogen with the full recomme
... Show MoreHeat treatment by solid solution method in the ?+? phase region was used at 970°C for Ti-5Al-2.5Fe alloy. The specimens cooled under different cooling media [water quenched (WQ), air cooled (AC) and furnace cooled (FC)], and subsequently aged at 550°C for 4 hours. Five specimens from each treatment were immersed in simulated body fluid SBF for a period of time (3 months). The dependence of corrosion rate on compositional variation in the phases resulted from various type of cooling rates are discussed based on immersion tests. The EDXA results show the precipitation of phosphate and calcium compounds on the alloy after 3 months of immersion in blood plasma solution forming a bone-like apatite, which enhanced the alloy biocompatibility ma
... Show More
In this investigation insulator ceramic body was prepared by using iraqi local materials, these are kaolin, silica sand glass, feldspar with weight percentage (45%,25%, 30%)respectively. After the end of treating drying and milling of raw material mixing with different concentrations of sodium silicate(1%,0.7%,0.5%,0.2%,0.1%) while zinc oxide was added at fixed weight percentage. A disc samples was prepared after compaction and then fired by sintering temperatures (1250, 1350)oC respectively.A surface morphology was studied by using optical microscope and measurements of apparent density and porosity was under taken to the sintered samples by using Archimedes method.The study showed that the microscopic images for samples sur
... Show MoreBackground The application of nanotechnology to biomedical surfaces is explained by the ability of cells to interact with nanometric features. The aim of this study was to consider the role of nanoscale topographic modification of CPTi dental implant using chemical etching method for the purpose of improving osseointegration. Materials and methods: Commercial pure titanium rod was machined into 20 dental implants. Each implant was machined in diameter about 3mm, length of 8mm (5mm was threaded part and 3mm was flat part). Implants were prepared and divided into 2 groups according to the types of surface modification method used: 1st group (10 implant) remained without nano surface modification (control), 2nd group include (10 implant) etche
... Show MoreIn this manuscript has investigated the synthesis of plasma-polymerized pyrrole (C4H5N) nano-particles prepared by the proposed atmospheric pressure nonequilibrium plasma jet through the parametric studies, particularly gas flow rate (0.5, 1 and 1.5 L/min). The plasma jet which used operates with alternating voltage 7.5kv and frequency 28kHz. The plasma-flow characteristics were investigated based on optical emission spectroscopy (OES). UV-Vis spectroscopy was used to characterize the oxidization state for polypyrrole. The major absorption appears around 464.1, 449.7 and 435.3 nm at the three flow rate of argon gas. The chemical composition and structural properties of the
... Show More
(1)
Comsol multiphysics software is established to make a simulation that is comparable with experimental device. by utilizing comsol, the positive column domain of direct-current glow discharge with argon is considered for both of different applied voltage and working gas pressure. The calculations are exhibited by using a precise collision cross sections and Townsend coefficients for the argon. The impacts of voltage and pressure on the Debye length, number of particles in Debye sphere and plasma frequency are calculated and graphically delineated. With this regard to the dependence of plasma parameters on the applied voltage and pressure, some of them are found to be compatible with the experimental
... Show More
(1)
(18)
(13)
A particulate composite material was prepared by adding the Titanium dioxide (TiO2) with a particle size of (75-150) µm to Epoxy resin at weight percentage of (10%,20%,30%,40%,50%).The following some mechanical properties were studied,fracture toughness, hardness.casting preparation methods were used in this study includes preparing plate of matrix and composites. specimens were prepared according to ASTM for the Mechanical properties tests. After that Another samples were heat treated for three and six hour at 65C?. Fracture toughness (Kic) represent for stress intensity factor results were showed that the curve of three hours aging increases in fracture toughness (Kic) for composites but for six hours aging increases fracture tough
... Show More
Bending effects on the transmission of optical signal are investigated on a single mode
optical fiber (SMOF) of 10 m length, core radius of 5 μm and optical refractive index difference
0.003. The bending radii (R) were between 0.08 and 0.0015 m. A great decrease in the amplitude is
shown for radii below 0.01 m. Sudden break down occurs for radii less than 0.0015 m. Birefringence
(B) is difficult to measure for long fibers. Meanwhile, B was found by comparing with calibrated
fiber of the same properties but of length of 0.075 m. The results show an increase in propagation
constant (Δβ) and the decrease in beat length (Lb), and show that bending decreases the critical radius
of curvature (Rc) related to B. The chang