Background: Lack of durability of the bond of the dental adhesive systems to tooth structure is one of the most important problems in tooth colored restorative work. This in vitro study was performed to evaluate the effect of 2% chlorhexidine gluconate(CHX) on dentin bond strength by using total etch adhesive system at twenty-four hours and three months of water storage. Material and methods:A flat dentin surface was prepared for forty sound human maxillary premolar teeth which were acid etched with 36% phosphoric acid gel after being divided randomly into four groups of ten teeth each according to storage time and CHX application, theCHX was applied for 60 seconds before adhesive application for groups I and III which were tested after twenty-four hours and three months respectively, while the distal water was applied for 60 seconds before the application of adhesive for group II and IV which were tested after twenty-four hours and three months respectively.The Prime and Bond® NT™ adhesive (Dentsply) was applied and cured, Composite (Ceram X mono, Dentisply) was applied through special mold with 2 mm thickness and light cured, Then all specimens were stored in distilled water 37oC until the time of testing of each group.Shear bond strength test was performed at the end of the storage period (24 hours or 3 months). Results:T-test results showed high statistically significant reduction in shear bond strength (SBS) in non CHX group IV (tested after 3 months) compared to non CHX group II (tested after 24 hours)(P< 0.01). In CHX groups I (tested after 24 hours) and III (tested after 3 months), results showed no statistically significant differences in shear bond strength(p> 0.05).On the other hand result showed statistically no significant differences between groups I and II in 24 hours shear bond strength (P> 0.05). After 3 months water storage, there was statistically high significant differences between the groups III and IV (P< 0.01). Conclusion: the use of 2 % CHX glocounate solution after acid etching and before bonding of dentin have no adverse effect on immediate bond strength (24 hours storage), and was effective in reducing degradation of resin-dentin bond interface after three months of water storage.
The experiment was conducted under shading (with the aid of Saran) condition on a nursery managed by the Baghdad Mayoralty during the season of 2014-2015 to study the effect of composed sheep manure extract on the growth and leaf nutrients content of tomato seedlings var. Wijdan. The experiment was composed of 6 treatments included the extract of sheep manure by hot (425C)and lmbient(205C) temperature water .The extract was diluted to the half by water and foliar applied to seedlings (multible application) or to the soil . Treatments also included the application of NPK chemical fertilizers as recommended and a control treatment through applying distilled water as foliar .The experiment was designed according to the randomized compl
... Show More
(1)
(1)
Thin films samples of Bismuth sulfide Bi2S3 had deposited on
glass substrate using thermal evaporation method by chemical
method under vacuum of 10-5 Toor. XRD and AFM were used to
check the structure and morphology of the Bi2S3 thin films. The
results showed that the films with law thickness <700 nm were free
from any diffraction peaks refer to amorphous structure while films
with thickness≥700 nm was polycrystalline. The roughness decreases
while average grain size increases with the increase of thickness. The
A.C conductivity as function of frequency had studied in the
frequency range (50 to 5x106 Hz). The dielectric constant,
polarizability showed significant dependence upon the variation of
thic
(1)
Educational of the mind is a weapon to a different knowledges which
benefit in ife and developed the mind in many field and practice him in a
regular form in a right thinking and practice sense on exactly recognizing and
conception things which is senses and regulating the memory and providing
with benefit information which fit to minded of person,the present research
aimed at answering the following two questions:
1-Does the concept of mind differ with age?
2-Does the recognition on function of mind developed with development of
age?
The research population consisted of the children in the primary schools
of Baghdad/center,and the students of the Education for woman
college/Baghdad university for the age
Rapid and continuous developments and changes in the modern business environment in all areas of economic, environmental, social, technology and communications push economic units to search for modern methods and methodologies to produce products at low cost as well as produce products that meet the wishes of customers in terms of quality and environment to maintain their market position, and accounting for the costs of the flow of materials is one of the most prominent environmental management accounting techniques capable of providing information to help produce
(3)
(2)
The electrical properties of polycrystalline cadmium telluride thin films of different thickness (200,300,400)nm deposited by thermal evaporation onto glass substrates at room temperature and treated at different annealing temperature (373, 423, 473) K are reported. Conductivity measurements have been showed that the conductivity increases from 5.69X10-5 to 0.0011, 0.0001 (?.cm)-1 when the film thickness and annealing temperature increase respectively. This increasing in ?d.c due to increasing the carrier concentration which result from the excess free Te in these films.
Crude oil still affects many countries because it is one of the essential fuel sources. It makes life more manageable in modern communities and cannot be overstated because it is easy to use and find. However, the pollution caused by its use in industries such as mining, transportation, and the oil and gas business, especially soil pollution, cannot be ignored. Soil pollution is an issue in most communities because it influences people and ecology. Accidental infusions and spills of ore oils are prevalent occurrences leading to the entire or fractional exchange of the soil pore fluid by oil-contaminated soils that have affected the geotechnical engineering properties. The liquid limitations for polluted soil grades silty loam and sa
... Show More
(14)
(15)
Thermal conductivity measurement was done for specimens of Polystyrene/ titanium dioxide, Polycarbonate/ titanium dioxide and Polymethylmetha acrylate/ titanium dioxide composites for weight ratio of 1.9/ 0.1 and 1.8/ 0.2 wt% for different thickness of the samples. The experimental results show that the thermal conductivity is increased with the increasing of thickness of layers and with the weight ratio of TiO2