Background: Lack of durability of the bond of the dental adhesive systems to tooth structure is one of the most important problems in tooth colored restorative work. This in vitro study was performed to evaluate the effect of 2% chlorhexidine gluconate(CHX) on dentin bond strength by using total etch adhesive system at twenty-four hours and three months of water storage. Material and methods:A flat dentin surface was prepared for forty sound human maxillary premolar teeth which were acid etched with 36% phosphoric acid gel after being divided randomly into four groups of ten teeth each according to storage time and CHX application, theCHX was applied for 60 seconds before adhesive application for groups I and III which were tested after twenty-four hours and three months respectively, while the distal water was applied for 60 seconds before the application of adhesive for group II and IV which were tested after twenty-four hours and three months respectively.The Prime and Bond® NT™ adhesive (Dentsply) was applied and cured, Composite (Ceram X mono, Dentisply) was applied through special mold with 2 mm thickness and light cured, Then all specimens were stored in distilled water 37oC until the time of testing of each group.Shear bond strength test was performed at the end of the storage period (24 hours or 3 months). Results:T-test results showed high statistically significant reduction in shear bond strength (SBS) in non CHX group IV (tested after 3 months) compared to non CHX group II (tested after 24 hours)(P< 0.01). In CHX groups I (tested after 24 hours) and III (tested after 3 months), results showed no statistically significant differences in shear bond strength(p> 0.05).On the other hand result showed statistically no significant differences between groups I and II in 24 hours shear bond strength (P> 0.05). After 3 months water storage, there was statistically high significant differences between the groups III and IV (P< 0.01). Conclusion: the use of 2 % CHX glocounate solution after acid etching and before bonding of dentin have no adverse effect on immediate bond strength (24 hours storage), and was effective in reducing degradation of resin-dentin bond interface after three months of water storage.
According to the famous saying of the medieval physician Paracelsus, "There is no substance without poison. Only the dose determines the extent of the toxic effect." Here, the effect of monosodium glutamate (MSG) on human health and the risks to the health of its frequent use in the short term was addressed and the long term was evaluated according to the studies of several researchers specializing in this regard. Monosodium glutamate (MSG) is known as one of the most popular food additives that classified as a flavor enhancer. Parts of the evidence were reviewed from the literature explaining its effect on immune system cells in addition to metabolic disorders by exposing individuals to obesity and what is known as metabolic syndrome, as w
... Show MoreThis work presents an experimental study of heat transfer and flow of distilled water and metal oxide nanofluid Fe3O4-distilled water at concentrations of (φ = 0.3, 0.6, 0.9 %) by volume in a horizontal pipe with constant magnetic field. All the tests are carried out with Reynolds number range (2900-9820) and uniform heat flux (11262-19562 W/m2). The results show that, the nanofluid concentration and magnetic intensity increase, the Nusselt number increases. The maximum enhancement in Nusselt number with magnetic nanofluid is (5.4 %, 26.4 %, 42.7 %) for volume concentration (0.3, 0.6, 0.9 %) respectively. The enhancement is maximized with magnetic intensity (0.1, 0.2, 0.3 tesla) respectively to (43.9, 44
... Show MoreInflation is one of the important issues that the economic authorities in all countries of the world care about, where the loss of money for its function is one of the most important and largest inflationary effects that this phenomenon leaves on the economy, and Iraq, like other countries, has had its share of the problem of inflation for a long time due to the circumstances that He went through it, whether it was the wars he fought or the economic blockade that was imposed on him in the nineties of the last century. Economically, the problem of inflation is addressed through the use of fiscal policy tools, including tax increases in order to abso
... Show MoreInflation is one of the important issues that the economic authorities in all countries of the world care about, where the loss of money for its function is one of the most important and largest inflationary effects that this phenomenon leaves on the economy, and Iraq, like other countries, has had its share of the problem of inflation for a long time due to the circumstances that He went through it, whether it was the wars he fought or the economic blockade that was imposed on him in the nineties of the last century. Economically, the problem of inflation is addressed through the use of fiscal policy tools, including tax increases in order to abso
... Show MoreIn this study a polymeric composite material was prepared by hand
lay-up technique from epoxy resin as a matrix and magnesium oxide
(MgO) as a reinforcement with different weight fraction (5,10,15,
and 20)% to resin. Then the prepared samples were immersed under
normal condition in H2So4(1 M) solution, for periods ranging up to
10 weeks. The result revealed that the diffusion coefficient
decreasing as the concentration of MgO increase. Also we studied
Hardness for the prepared samples before and after immersion. The
result revealed that the hardness values increase as the concentration
of MgO increase, while the hardness for the samples after immersion
in H2SO4 dec
The research aims to conduct a comparative study between the events (800) m and (1500) m track in the types of muscular strength and to identify the differences between them among Iraqi sports club players. The sample represented the players participating in the Iraqi Athletics Championship for the period between (02/11/2023) and (04 /11/2023), and their number was (16) players (8) for each event, as the selection was made intentionally. The researchers used the descriptive approach to achieve the goal of the research and used the statistical package (SPSS) to process the data statistically. According to the results collected, it was found that there was superiority among the intermediate track players (800) m in explosive power and the s
... Show More
(10)
(5)
This article presents the results of an experimental investigation of using carbon fiber–reinforced polymer sheets to enhance the behavior of reinforced concrete deep beams with large web openings in shear spans. A set of 18 specimens were fabricated and tested up to a failure to evaluate the structural performance in terms of cracking, deformation, and load-carrying capacity. All tested specimens were with 1500-mm length, 500-mm cross-sectional deep, and 150-mm wide. Parameters that studied were opening size, opening location, and the strengthening factor. Two deep beams were implemented as control specimens without opening and without strengthening. Eight deep beams were fabricated with openings but without strengthening, while
... Show More
(28)
This article presents the results of an experimental investigation of using carbon fiber–reinforced polymer sheets to enhance the behavior of reinforced concrete deep beams with large web openings in shear spans. A set of 18 specimens were fabricated and tested up to a failure to evaluate the structural performance in terms of cracking, deformation, and load-carrying capacity. All tested specimens were with 1500-mm length, 500-mm cross-sectional deep, and 150-mm wide. Parameters that studied were opening size, opening location, and the strengthening factor. Two deep beams were implemented as control specimens without opening and without strengthening. Eight deep beams were fabricated with openings but without strengthening, while
... Show More
(29)
(28)
Samarium(III) ions react with (l-2(2-benzoinidazolyl-azo)-2-hydroxy-3-naphthoic acid in basic medium (pH = 8.0) forms a red-orange complex at A.max (550nm). The complex was found to be stable for at least 48 hrs. at the given pH. The apparent molar absorptivity is 7776.77 L.mol-1.Cm-1 and a linear calibration curve is obtained in the range (0.639x 10-5M - 6.350x 10 -5M). The stoichiometry of complex was confirmed by using mole ratio method which indicated that ratio of reagent to metal is 3:1. The effects of the presence of different cations and anions as interferences in the determination of samarium(III) under the given conditions were investigated