Background: Polymethyl methacrylate (PMMA) is used in denture fabrication and considered as the most reliable material for the construction of removable prosthodontic appliances. The material is far from ideal in fulfilling the mechanical requirements and the effect of autoclave processing has not been fully determined. The purpose of this study was to evaluate the effect of addition of salinized (ZrO2) Nano fillers in percentages 3%, 5% and 7% by weight on some properties of heat cured acrylic processed the by autoclave and compare it with 0% (control) group . Materials and methods: The silanized(ZrO2) Nano-particles was added to PMMA powder by weight in three different percentages 3%, 5% and 7%, mixed by probe ultra-sonication machine.Two hundred specimens were constructed and processed by autoclave and divided into 5 groups according to the test (each group consist of 40 specimens ) and each group was subdivided into 4 sub-groups according to the percentage of added (ZrO2) nano-particles( with 10 specimens for each subgroups) . The tests conducted were transverse strength, hardness (shore D), Impact strength test, surface morphology and apparent porosity. AFM can provide 3D image of the specimen the homogeneity of nanostructure film, roughness of surface and crystallite size. Scanning electron microscope SEM of control and salinized Nano ZrO2 reveal the Nano fillers distribution and it is shaped. Results: Highly significant increase in impact strength recorded when acrylic (vertex) mixed with 3%, 5% ZrO2 nano filler, while a non-significant reduction was observed with 7% ZrO2 addition in comparison to control. Non-significant improvement in transverse strength when 3% ZrO2 was added, 5% nano addition ZrO2 improved transverse strength significantly while 7% nano addition showed anon significant reduce when these groups compared to the control group .Anon significant reduction in the deformity was seen within 3% nano addition ZrO2 also 5% nano ZrO2 addition reduce the deformity significantly and significant increase was recorded when 7% nano addition ZrO2 was add and when these groups are compared to the control group. A significant increase in surface hardness was observed with the addition of (ZrO2) nano-particles to (PMMA) at the percentage of 3%, highly significant increase at 5% and 7% with addition of modified nano-ZrO2. A non-significant decrease in apparent porosity at 3% and highly significant decrease in apparent porosity at 5% and 7% with addition of modified nano-ZrO2 were observed. SEM results showed a good distribution of the modified nano-ZrO2 fillers at 3%, 5% and showed aggregation at 7% in the polymer matrix. Conclusion: The addition of modified nano-ZrO2 particles to acrylic resin cured by autoclave improved impact and transverse strength of denture base nano composite containing 5% of nano-ZrO2. And this strength decreases with further increase of nano-ZrO2 filler content. Also addition of modified nano-ZrO2 slightly increaseshardness, thesurface roughness and the apparent porosity also decrease by addition of nano ZrO2 percentage increase. Key words: Salinized (ZrO2) nano fillers, PMMA.
The effect of the aqueous extract of fig (Ficus carica) fruit was studied by using different concentrations of this fruit (15, 20 and 25 mg/kg of body weight) on some hematological parameters (hemoglobin concentration, packed cell volume, white blood cell count and platelets count) in female rabbits. Twenty female rabbits were randomly divided into four groups (five animals in each group). Three groups were dosed with the concentrations mentioned above, while the last was administered with distilled water and considered as control group. These animals were orally dosed by aqueous extract using a micropipette. The results showed that there was a significant (P<0.05) increase in hemoglobin concentration and packed cell volume means for all
... Show More
(1)
This research discloses the synthesis of various polyester resins, the polyesters containing homoring aromatic and others heterocyclic were synthesized by the condensation polymerization of suitable monomers (which are containing variety function groups in different structures) with phthalic anhydride. The main objective is synthesis of new polyester with keeping a reasonable electrical insulating behavior. The structural of polymer was characterized by Fourier Transform infra-red spectroscopy FTIR and HNMR. The dielectric constant (real ε' and imaginary parts ε") and AC conductivity (σAC) for all the polyester samples are studied by varying the frequency (30, 50, 70, 90, 120, 300, 500Hz and 1KHZ) at 25⁰ C. Indeed, study of the electri
... Show MoreThis research aims to investigate and evaluate a reactive powder concrete (RPC) cast using economical materials. Its mechanical properties were investigated and evaluated by studying the effects of using different cement and silica fume contents and locally steel fibers aspect ratios as reinforcement for this concrete. A compressive strength of about 155.2MPa, indirect tensile strength of 16.0MPa, modulus of elasticity of 48.7GPa, flexural strength of 43.5MPa, impact energy of 3294.4kN.m and abrasion loss 0.59% have been achieved for reinforced RPC contains 910 kg/m3 cement content, silica fume content 185 kg/m3 of cement weight and fiber volume fraction 2%. The water absorption values w
... Show MoreAbstract:Porous Silicon (PSi) has been produced in this work by using Photochemical (PC) etching process by using a hydrofluoric acid (HF) solution. The irradiation has been achieved using quartz- tungsten halogen lamp. The influence of various irradiation times on the properties of PSi اmaterial such as layer thickness, etching rate and porosity was investigated in this work too. The XRD has been studied to determine the crystal structure and the crystalline size of PSi material
Porous Silicon (PSi) has been produced in this work by using Photochemical (PC) etching process by using a hydrofluoric acid (HF) solution. The irradiation has been achieved using quartz- tungsten halogen lamp. The influence of various irradiation times on the properties of PSi اmaterial such as layer thickness, etching rate and porosity was investigated in this work too.
The XRD has been studied to determine the crystal structure and the crystalline size of PSi material