Background: The main purpose of this study is to find if there is any correlation between the level of C-reactive protein (CRP) in gingival crevicular fluid with its serum level in chronic periodontitis patients and to explore the differences between them according to the probing depth. Materials and methods: Forty seven male subjects enrolled in this study. Thirty males with chronic periodontitis considered as study group whom further subdivided according to probing depth into subgroup 1 with pocket depth ≤6mm, subgroup 2 with pocket depth >6mm. The other 17 subjects considered as controls. For all subjects, clinical examination where done for periodontal parameters plaque index (PLI), gingival index (GI), bleeding on probing (BOP), probing pocket depth (PPD) and clinical attachment level (CAL). The gingival crevicular fluid (GCF) were collected using filter paper size 30 from gingival sulcus of the controls and from (138) pocket site (75 sites > 6mm. and 63 ≤ 6mm.). The weight of the GCF was measured by reading the difference in the weight of filter paper before and after absorption of GCF. Crevicular level of CRP was measured calorimetrically. The serum level CRP was measured using latex test. Results: Highly significant difference in the weight of GCF, crevicular and serum level of CRP between chronic periodontitis and control groups. Subgroup 2 got higher scores of weight of GCF and positive record of crevicular and serum CRP compared with subgroup 1 with a non-significant difference. A highly significant difference in the number of sites with positive crevicular and serum CRP compared to the negative number between chronic periodontitis and control groups also between subgroup1 and subgroup 2. Weight of GCF gets a negative significant correlation with GI at control group and subgroup2. Serum level of CRP exhibits a negative significant correlation with PLI for chronic periodontitis and control group and positive significant correlation for GI at subgroup 1. The crevicular CRP get significant negative correlation with GI of subgroup 1. Conclusions: Crevicular fluid is very good marker for the degree of inflammation of the periodontal pocket. The crevicular level of CRP may be considered as a good tool for estimating the systemic effect and predictor for the effect of periodontitis on the general health and the correlation of crevicular with serum CRP aid to high light this effect.
Positron annihilation lifetime (PAL) technique has been employed to
study the microstructural changes of polyurethane (PU), EUXIT 101
and epoxy risen (EP), EUXIT 60 by Gamma-ray irradiation with the
dose range (95.76 - 957.6) kGy. The size of the free volume hole and
their fraction in PU and EP were determined from ortho-positronium
lifetime component and its intensity in the measured lifetime spectra.
The results show that the irradiation causes significant changes in the
free volume hole size (Vh) and the fractional free volume (Fh), and
thereby the microstructure of PU and EP. The results indicate that
the γ-dose increases the crystallinity in the amorphous regions of PU
and increas
(1)
Optical properties of chromium oxide (Cr2O3) thin films which were prepared by pulse laser deposition method, onto glass substrates. Different laser energy (500-900) mJ were used to obtain Cr2O3 thin films with thickness ranging from 177.3 to 372.4 nm were measured using Tolansky method. Then films were annealed at temperature equal to 300 °C. Absorption spectra were used to determine the absorption coefficient of the films, and the effects of the annealing temperature on the absorption coefficient were investigated. The absorption edge shifted to red range of wavelength, and the optical constants of Cr2O3 films increases as the annealing temperature increased to 300 °C. X-ray diffraction (XRD) study reveals that Cr2O3 thin films are a
... Show More
(1)
In this research, Mn-doped TiO2 thin films were grown on glass, Si and OIT/glass substrates by R.F magnetron sputtering technique with thicknesses (250 nm) using TiO2:Mn target under Ar gas pressure and power of 100 Watt. Through the results of X-ray diffraction, the prepared thin films are of the polycrystallization type after the process of annealing at 600°C for two hour The average crystalline size were 145.32, 280.97 and 261.23 nm for (TiO2:Mn) thin film on glass, Si and OIT/glass substrates respectively, while the measured surface roughness is between 0.981nm and 1.14 nm. The fabricated (TiO2:Mn) thin film on glass sensors have high sensitivity for hydrogen( H2 reducing gas) compared to the sensitivity for hydrogen gas on Si and OIT/
... Show More
(31)
Undoped and Co-doped zinc oxide (CZO) thin films have been prepared by spray pyrolysis technique using solution of zinc acetate and cobalt chloride. The effect of Co dopants on structural and optical properties has been investigated. The films were found to exhibit maximum transmittance (~90%) and low absorbance. The structural properties of the deposited films were examined by x-ray diffraction (XRD). These films, deposited on glass substrates at (400? C), have a polycrystalline texture with a wurtzite hexagonal structure, and the grain size was decreased with increasing Co concentration, and no change was observed in lattice constants while the optical band gap decreased from (3.18-3.02) eV for direct allowed transition. Other parameters
... Show More
Beryllium Zinc Oxide (BexZn1-xO) ternary nano thin films were deposited using the pulsed laser deposition (PLD) technique under a vacuum condition of 10-3 torr at room temperature on glass substrates with different films thicknesses, (300, 600 and 900 nm). UV-Vis spectra study found the optical band gap for Be0.2Zn0.8O to be (3.42, 3.51 and 3.65 eV) for the (300, 600 and 900nm) film thicknesses, respectively which is larger than the value of zinc oxide ZnO (3.36eV) and smaller than that of beryllium oxide BeO (10.6eV). While the X-ray diffraction (XRD) pattern analysis of ZnO, BeO and Be 0.2 Zn 0.8 O powder and nano-thin films indicated a hexa
... Show More
(1)
In this research tri metal oxides were fabricated by simple chemical spray pyrolysis technique from (Sn(NO3)2.20 H2O, Zn(NO3)2.6 H2O, Cd(NO3)2.4 H2O) salts at concentration 0.1M with mixing weight ratio 50:50 were fabricated on silicon substrate n-type (111). (with & without the presence of grooves by the following diemensions (20μm width, 7.5μm depth) with thickness was about ( 0.1 ±0.05 µm) using water soluble as precursors at a substrate temperature 550 ºC±5, with spray distance (15 cm) and their gas sensing properties toward H2S gas at different concentrations (10,50,100,500 ppmv) in air were investigated at room te
... Show More
(2)
In this work, (CdO)1-x (CoO)x thin films were prepared on glass slides by laser-induced plasma using Nd:YAG laser with (λ=1064 nm) and duration (9 ns) at different laser energies (200-500 mJ) with ratio (x=0.5), The influence of laser energy on structural and optical properties has been studied. XRD patterns show the films have a structure of polycrystalline wurtzite. As for AFM tests results for the topography of the surface of the film, where the results showed that the grain size and the average roughness increase with increasing laser energy. The optical properties of all films were also studied and the results showed that the absorption coefficient for within the wavelength range (280-1100 nm), The value of the optical power gap fo
... Show More
(4)
(9)
(17)
(15)
Background: Human semen contains high concentrations of fructose, zinc (Zn) and copper (Cu) in bound and ionic forms for Zn and Cu. The presence of abnormal levels of fructose and those trace elements may affect spermatogenesis with regard to production, maturation, motility and fertilizing capacity of the spermatozoa.Objective: To evaluate the levels of fructose, Zn and Cu in seminal plasma in different groups of male infertility and to correlate their concentrations with various sperm parameters.Methods: The concentrations of fructose, Zn and Cu were measured in 114 semen samples from normozoospermic, oligozoospermic, astheno-zoospermic, and azoospermic men using the electrothermal-atomic absorption spectrometry for Zn and Cu determinatio
... Show More