Background: This in vitro study measure and compare the effect of light curing tip distance on the depth of cure by measuring vickers microhardness value on two recently launched bulk fill resin based composites Tetric EvoCeram Bulk Fill and Surefil SDR Flow with 4 mm thickness in comparison to Filtek Z250 Universal Restorative with 2 mm thickness. In addition, measure and compare the bottom to top microhardness ratio with different light curing tip distances. Materials and Method: One hundred fifty composite specimens were obtained from two cylindrical plastic molds the first one for bulk fill composites (Tetric EvoCeram Bulk Fill and Surefil SDR Flow) with 4 mm diameter and 4 mm depth, the second one for Filtek Z250 Universal Restorative with 4 mm diameter and 2 mm depth. Each spcimen was light-cured using WOODPECKER LED CURING LIGHT for 20 sec. Polymerization was performed with the light tip positioned in direct contact, 2 mm, 4 mm, 6 mm and 8 mm distant from the top surface of the sample. After one day of storage in distilled water in a light proof container at 37ËšC, the hardness on the bottom and top surfaces of each specimen was tested using the Digital Micro Vickers Hardness Tester. Then the Data were analyzed statistically by ANOVA test, LSD test and t-test. Results: All experimental groups show top microhardness higher than bottom microhardness with high significant difference with all light tip distances. At 0 mm light tip distance all groups give the highest microhardness value. Filtek Z250 Universal Restorative shows accepted bottom to top microhardness ratio at all light tip distances. Surefil SDR Flow shows accepted bottom to top ratio only at 0, 2 and 4mm light tip distances while Tetric EvoCeram Bulk Fill shows the bottom to top microhardness ratio less than the accepted value with all light tip distances. Conclusion: From the results of this study we can conclude that the polymerization of bulk fill composite depends greatly on the distance from light curing tip, Tetric EvoCeram Bulk Fill composite not recommended to be used as bulk fill restoration in deep cavities and need further studies, while Surefil SDR Flow not recommended to be used in deep cavity when curing tip distance (6-8 mm), in addition we can conclude that the thickness of the increments is more important than light curing tip distance.
Two grades of paving asphalt with penetration of 46 and 65 are studied for determining changes in their physical and chemical properties caused by ageing.
The ageing process has been conducted on two petroleum paving asphalt cement using thin film oven test at 150, 163 and 175 C, and ageing time 5, 10,15, 20, 25 and 30 hours. The effect of ageing time and temperature on penetration, kinematic viscosity, softening point, solubility in trichloroethylene, heat loss and changes in chemical composition are investigated. The results of thin film oven test process indicte that the asphaltenes concentration of all aged asphalt increases with increasing ageing time, while the opposite was observed for polar-aromatic and naphthene-aromatic. The
(3)
(2)
This work aims at finding out the impact of teaching types blended learning strategies on academic students` achievement. A review of related literature indicates that almost no study has ever attempted to focus specifically on the effect of the different kinds of blended learning strategies on EFL students` achievement in the educational research writing, and the present study attempts to fill this gap. The study focused on the students at the Master's degree in Educational Research Writing in the first semester of the academic year 2020/2021. The sample has selected from the college of Education Ibn-Rushd (18) students. Material has been designed for the Master candidates’ participants of the study was divided into two groups: one an e
... Show MoreThe study concern with the preparation of three type of mixtures; which are prepared from different percentage of polyvenil Butyral, Di-n-butyl phathalate and paraffin wax pastillated. The solvent used is Xylolzul analyses. After washing, Drying and milling the kaolin Dukhla, as a matrix in this study, and by using sieving Tech. The range of particle size used is less than and less than as a mesh batch. The added percentage from prepared mixture were 5% and 10% to 95% and 90% of the matrix respectively. Then disk samples were prepared by using a compaction pressure with heating. After cooling and drying the samples were undergo heat treatment in the range of (1250 – 1350) oC. The measurement of shrinkage and Dielectric properties sho
... Show More
(5)
CuInSe2(CIS) thin films have been prepared by use vacuum thermal evaporation technique, of thickness750 nm with rate of deposition 1.8±0.1 nm/sec on glass substrate at room temperature and pressure (10-5) mbar. Heat treatment has been carried out in the range (400-600) K for all samples. The optical properties of the CIS thin films are been studied such as (absorption coefficient, refractive index, extinction coefficient, real and imaginary dielectric constant) by determined using Measurement absorption and transmission spectra. Results showed that through the optical constants we can make to control it are wide applications as an optoelectronic devices and photovoltaic applications.
(3)
(2)