Background: Adjustment of any premature occlusal contact of any zirconia restoration requires its polishing or glazing in order to restore the smoothness of the restoration. The objective of this in vitro study was to evaluate the effects of different polishing systems and glazing on the surface roughness of full-contour zirconia. Material and methods: Forty disks (diameter: 8 mm, thickness: 6.4 mm) were prepared from pre-sintered full-contoured zirconia block; they were colored and sintered in a high-temperature furnace at 1500˚C for 8 hours. The specimens were then leveled and finished using grinding and polishing machine and adjusted using diamond disk. The specimens were then randomly divided into four groups (n=10), group I involves samples that were polished using (karat diamond polishing set, Vita zahnfabrik, Germany), group II involves samples that were polished with (zirconia polishing kit, SMEdent, Shanghai, China), group III involves samples that were polished with (OptraFine® diamond polishing system, Ivoclar Vivadent, Germany), while group IV involves samples that were glazed using glazing medium (VITA Akzent Glaze AKZ 25, Vita zahnfabrik, Germany). Surface roughness values (Ra) (in µm) of all the specimens were recorded at each stage of surface treatment of zirconia disks (leveling and finishing, adjustment of the samples and polishing / glazing) using surface roughness tester. Statistical analysis was carried out using one-way ANOVA and LSD tests. Results: The results showed that the glazing group recorded the lowest surface roughness mean value, followed by (OptraFine® polishing system), then (zirconia polishing kit) and finally (karat polishing set) which showed the highest mean of surface roughness. For all groups, there was a statistically very high significant difference of (Ra) value before and after adjustment of the samples. Moreover, there was a statistically very high significant difference in (Ra) value when comparing the adjusted samples with the polished and glazed ones. Karat polishing set group showed a statistically highly significant difference with zirconia polishing kit group (P<0.01). Both, karat polishing set and zirconia polishing kit groups showed a statistically very highly significant difference (P<0.001) with (OptraFine® polishing system) and glazing groups. On the other hand, no statistically significant difference was found between glazing and (OptraFine® polishing system) groups (P>0.05). Conclusions: Adjusting full-contour zirconia with diamond bur or disk resulted in a significant increase in (Ra) that necessitates its polishing or glazing to restore the surface smoothness. Furthermore, both glazing and OptraFine® polishing system provided the best surface smoothness, so glazing can be substituted with chairside polishing using OptraFine® polishing system.
Background: Orthodontic tooth movement is characterized by tissue reactions, which consist of an inflammatoryresponse in periodontal ligament and followed by bone remodeling in the periodontium depending on the forces applied. These processes trigger the secretion of various proteins and enzymes into the saliva.The purpose of thi study was to evaluate the activity of alkaline phosphatase (ALP) in saliva during orthodontic tooth movement using different magnitude of continuous orthodontic forces.
Materials and Methods: Thirty orthodontic patients (12 males and 18 females) aged 17-23 years with class II division I malocclusion all requiring bilateral maxillary first premolar extractions were randomly divided into three groups according t
A hand lay-up method was used to prepare Epoxy/ metal composites. Epoxy resin (EP) was used as a matrix with metal particles (Al, Cu, and Fe) as fillers.
The preparation method includes preparing square panels of composites with different weight percentage of fillers (10, 20, 30, 40, and 50%). Standard specimens (88mm in diameter) for thermal conductivity tests were prepared to measure thermal conductivity kexp.The result of experimental thermal conductivity kexp, for EP/metal composites show that, kexp increase with increasing weight percentage, For EP/ Al and EP/Cu composites, and it have have maximum values of 0.33 and 0.35 W/m.K, respectively. While kexp for EP/ Fe composite show slight increase with maximum value of 0.186 W/m.K.
The possible effect of the collective motion in heavy nuclei has been investigated in the framework of Nilson model. This effect has been searched realistically by calculating the level density, which plays a significant role in the description of the reaction cross sections in the statistical nuclear theory. The nuclear level density parameter for some deformed radioisotopes of (even- even) target nuclei (Dy, W and Os) is calculated, by taking into consideration the collective motion for excitation modes for the observed nuclear spectra near the neutron binding energy. The method employed in the present work assumes equidistant spacing of the collective coupled state bands of the considered isotopes. The present calculated results for f
... Show More
Two grades of paving asphalt with penetration of 46 and 65 are studied for determining changes in their physical and chemical properties caused by ageing.
The ageing process has been conducted on two petroleum paving asphalt cement using thin film oven test at 150, 163 and 175 C, and ageing time 5, 10,15, 20, 25 and 30 hours. The effect of ageing time and temperature on penetration, kinematic viscosity, softening point, solubility in trichloroethylene, heat loss and changes in chemical composition are investigated. The results of thin film oven test process indicte that the asphaltenes concentration of all aged asphalt increases with increasing ageing time, while the opposite was observed for polar-aromatic and naphthene-aromatic. The
Free cement refractory concrete is a type of refractory concrete with replacing alumina cement by bonding materials such as white kaolin, red kaolin and fumed silica. The free cement refractory concrete used in many applications like Petrochemicals, iron furnaces and cement production industries. The research clarifies the effect of steel fibers with two types crimped steel fibers and hooked steel
fibers with percentages 0.5%, 1% and 1.5% by volume from weight of bauxite aggregates. The additions of steel fibers with two types gave good properties in high temperatures where the specimens keep the dimension without failure and the properties made the best. the percentage of increasing for thermal conductivity was 44% for 1.5% crimped
(7)
Contemporary residential neighborhoods suffer from weak sustainability of urban residential environments as a result of the adoption of inefficient spatial organization at the neighborhood unit level. This resulted negative characteristics which affected the achievement of sustainable development plans for the residential environment that constitute the majority of the urban fabric of cities.
The physical affordances ,within the vocabulary of recent times,overcame the spiritual ones and affected the residential environment. Accordingly,the concept of space changed in contemporary residential areas through the dominance of the physical aspect (mass) on the symbolic aspect (space).The modern technology occupied an important level b
... Show More
(4)
Carrageenan extract is a compound of sulfated polyglycan that is taken out from red seaweeds. Being hydrocolloid in nature, carrageenan has gelling, emulsifying and thickening properties allowing it to be commonly used in the oral healthcare products and cosmetics. Due to its bioactive compounds, carrageenan has been shown to have antimicrobial, antiviral, and antitumor properties. The purpose of this work is to study the probable use of carrageenan on the diseases that are related to oral cavity and on the genomic DNA in in vitro experimental model
In this study, the effects of k-carrageenan on four different cell lines related to the cancer and normal cells which cultured on selective media were done. Moreover, the eff
... Show More
(5)
(4)
The present study aim at preparing frusemide in liquid form suitable for oral use. This is achieved through preparing different liquid forms of frusemide. The frusemide liquid is prepared in the following forms: oral solution, syrup and elixir with intensity of 1, 0.4 and 0.8% weight /volume respectively and in combination with potassium carbonate, polysorbate 80, alcohol and phosphate buffer solution of pH8 to dissolve the frusemide in the above mentioned forms. The different forms of the prepared medicine have been stored in glass bottles that can provide protection against light and at 40, 50, 600C for four months. Besides the pH has been checked to decide the period of validity. The results show that the expiration date of
... Show More
This work describes the effect of temperature on the phase transformation of titanium dioxide (TiO2) prepared using metal organic precursors as starting materials. X-ray diffraction (XRD) was used to investigate the structural properties of TiO2 gels calcined at different temperatures (300, 500, 700) ?C. the results showed that the samples have typical peaks of TiO2 polycrystalline brookite nanopowders after calcined at (300 ?C), which confirmed by (111), (121), (200), (012), (131), (220), (040), (231), (132) and (232) diffraction peaks. Also, XRD diffraction spectra showed the presence of crystallites of anatase with low proportion of rutile phase where calcined at (500 ?C), while rutile phase domains at (700 ?C). The crystallite size of