Background: Adjustment of any premature occlusal contact of any zirconia restoration requires its polishing or glazing in order to restore the smoothness of the restoration. The objective of this in vitro study was to evaluate the effects of different polishing systems and glazing on the surface roughness of full-contour zirconia. Material and methods: Forty disks (diameter: 8 mm, thickness: 6.4 mm) were prepared from pre-sintered full-contoured zirconia block; they were colored and sintered in a high-temperature furnace at 1500˚C for 8 hours. The specimens were then leveled and finished using grinding and polishing machine and adjusted using diamond disk. The specimens were then randomly divided into four groups (n=10), group I involves samples that were polished using (karat diamond polishing set, Vita zahnfabrik, Germany), group II involves samples that were polished with (zirconia polishing kit, SMEdent, Shanghai, China), group III involves samples that were polished with (OptraFine® diamond polishing system, Ivoclar Vivadent, Germany), while group IV involves samples that were glazed using glazing medium (VITA Akzent Glaze AKZ 25, Vita zahnfabrik, Germany). Surface roughness values (Ra) (in µm) of all the specimens were recorded at each stage of surface treatment of zirconia disks (leveling and finishing, adjustment of the samples and polishing / glazing) using surface roughness tester. Statistical analysis was carried out using one-way ANOVA and LSD tests. Results: The results showed that the glazing group recorded the lowest surface roughness mean value, followed by (OptraFine® polishing system), then (zirconia polishing kit) and finally (karat polishing set) which showed the highest mean of surface roughness. For all groups, there was a statistically very high significant difference of (Ra) value before and after adjustment of the samples. Moreover, there was a statistically very high significant difference in (Ra) value when comparing the adjusted samples with the polished and glazed ones. Karat polishing set group showed a statistically highly significant difference with zirconia polishing kit group (P<0.01). Both, karat polishing set and zirconia polishing kit groups showed a statistically very highly significant difference (P<0.001) with (OptraFine® polishing system) and glazing groups. On the other hand, no statistically significant difference was found between glazing and (OptraFine® polishing system) groups (P>0.05). Conclusions: Adjusting full-contour zirconia with diamond bur or disk resulted in a significant increase in (Ra) that necessitates its polishing or glazing to restore the surface smoothness. Furthermore, both glazing and OptraFine® polishing system provided the best surface smoothness, so glazing can be substituted with chairside polishing using OptraFine® polishing system.
(8)
(6)
The nanocompsite of alumina (Al2O3) produced a number of beneficial effects in alloys. There is increasing in resistance of materials to surface related failures , such as the mechanical properties , fatigue and stress corrosion cracking .The experimental results observed that the adding of reinforced nanomaterials type Al2O3 enhanced the HB hardness, UTS, 0.2 YS and ductility of 2014 Al/Al2O3 nano composites . the analysis of experiments, indicated that The maximum enhancement was observed at 0.4 wt.% Al2O3. The ultimate improvement percentage were 15.78% HB hardness, 18.1% (UTS), 12.86% (
... Show More
(7)
This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3
... Show More
(6)
(4)
This study was undertaken to diagnose routine settling problems within a third-party oil and gas companies’ Mono-Ethylene Glycol (MEG) regeneration system. Two primary issues were identified including; a) low particle size (<40 μm) resulting in poor settlement within high viscosity MEG solution and b) exposure to hydrocarbon condensate causing modification of particle surface properties through oil-wetting of the particle surface. Analysis of oil-wetted quartz and iron carbonate (FeCO₃) settlement behavior found a greater tendency to remain suspended in the solution and be removed in the rich MEG effluent stream or to strongly float and accumulate at the liquid-vapor interface in comparison to naturally water-wetted particles. As su
... Show More
(13)
(14)
(17)
(5)
Background: Dental casts come into direct contact with impression materials and other items that are contaminated by saliva and blood from a patient's mouth, leaving the casts susceptible to cross-contamination. The disinfectant solutions of the impression materials cause various adverse reactions. Therefore, disinfection of dental casts may be effective in preventing cross infection. This study was carried out to evaluate the surface hardness, dimensional accuracy, reproduction of details and surface porosity of type III, type IV and type IV extra hard dental stone after immersion in and spray by using SOLO and Sodium hypochlorite disinfectant solutions. Materials and methods: 240 Stone samples were prepared in rubber rings, A total of 60
... Show MoreBackground: Dental casts come into direct contact with impression materials and other items that are contaminated by saliva and blood from a patient's mouth, leaving the casts susceptible to cross-contamination. The disinfectant solutions of the impression materials cause various adverse reactions. Therefore, disinfection of dental casts may be effective in preventing cross infection. This study was carried out to evaluate the surface hardness, dimensional accuracy, reproduction of details and surface porosity of type III, type IV and type IV extra hard dental stone after immersion in and spray by using SOLO and Sodium hypochlorite disinfectant solutions. Materials and methods: 240 Stone samples were prepared in rubber rings, A total of 60
... Show More