Background: This in vitro study was carried out to evaluate the effect of various endodontic irrigants (sodium hypochlorite, ethylene diaminetetracetic acid and normal saline) on sealing ability of (Biodentine, mineral trioxide aggregate, and amalgam) used to repair furcal perforations. Material and methods: One hundred and twenty extracted human molars with divergent roots were used in this study. A standard root canal access cavity was prepared in each tooth and furcal perforation was made and was standardized by using k file size 100 instrument to get a perforation of (1.32mm) in diameter .The teeth were randomly divided in to three groups of 40 teeth according to the type of material used to repair the perforations (Group A: The furcal perforations were repaired with Biodentine, Group B: The furcal perforations were repaired with MTA ,Group C: The furcal perforations were repaired with Amalgam). Each group was then subdivided into 4 subgroups according to irrigation regimens applied over the repair site (Subgroup 1: without irrigation, Subgroup 2: the pulp chamber was gently irrigated with 10 mL 5.25% Sodium hypochlorite for 10 minutes, Subgroup 3: Pulp chamber was gently irrigated with 10 mL 17% Ethylene Diaminetetracetic acid for 10 minutes, Subgroup 4: pulp chamber was gently irrigated with 10 mL normal saline for 10 minutes. Each tooth was coated with two layers of nail varnish and then sticky wax except 1 to 2 mm around the perforation site. Each tooth was placed in glass vial containing 3 ml of buffered Methylene blue dye at (37°C, pH 7) and kept in an incubator for 72 hour at 100% humidity. After dye application, the teeth were washed in running water for 5 min. Each tooth was sectioned longitudinally in a buccolingual direction. Results: The results showed that group A has least mean of dye penetration and the difference was highly significant with group C and non-significant with group B.Saline and NaOCl increase the sealing of all groups while EDTA significantly increased the dye penetration of Biodentine and MTA respectively. Conclusions: Biodentine has the best sealing ability of the tested materials while amalgam showed the highest dye penetration of all tested materials. Saline and NaOCl increase the sealing ability of Biodentine and MTA where as EDTA decreased the sealing efficacy of MTA and Biodentine.
This study was carried out in the botanical garden / department of biology /college of science in Mustansiriyah University, Baghdad. During spring 2017 under controlled environmental conditions in greenhouse to study the role of Nano ZrO2 activity in decrease negative effect of salinity under two levels from NaCl . The treatments included (Salinity levels : natural soil , 3000 ppm and 6000 ppm NaCl) and ( Applications : control , 100 , 300 Zirconium oxide , 5 ppm of liquorice root extract and 10 ppm liquorice root extract and 300 ppm GA3) , The collected data were analyzed statistically using factorial completely randomized design. The results appeared that 300 ppm nano zirconium gave the highest
... Show MoreBackground: Propolis has received great interest because of its wide range antimicrobial activity. Propolis also called (bee glue) due to its collection by (Apismellifera) honeybees from various plants resinous substance. The aim of this study was to determine the antibacterial effect of propolis extracts (aqueous and alcoholic) on anaerobic periodontal pathogen namely Aggregatibacteractinomycetemcomitans. Materials and Methods: Strains of Aggregatibacter actinomycetemcomitans wasisolated from pockets of systemically healthy patients aged between 35-55 years old suffering from chronic periodontitis with pocket depths of 5-6 mm, the bacteria cultured on special blood Agar plates solid media. Propolis was extracted by using water and alcohol.
... Show MoreBackground: Herbs are being widely explored to discover alternatives to synthetic antibacterial agents.Small Cardamom often referred to as queen of spices because of its very pleasant aroma and taste, have a history as old as human race. Most people use cardamom as a spice and are largely unaware of its numerous health benefits. The purpose of this study was to evaluate the effect of different concentrations of water and alcoholic cardamom extracts on sensitivities, growth, and adherence of Mutans streptococci in vitro. Materials and Methods: In this study, saliva was collected from ten volunteers (College students 18-22 years). Agar well technique was used to study the sensitivities of Mutans streptococci to different concentrations of s
... Show MoreBackground: Spices and herbs have been used by many cultures to enhance the flavor and aroma of food and for their medicinal value. Black cardamom is one of these spices widely used in cooking because of its unique taste and powerful flavor. The aim of study was to test the effect of black cardamom on Mutans Streptococci in comparison to chlorhexidine gluconate (0.2%) and de-ionized water. Materials and methods: Dried fruits of black cardamom were extracted by using alcohol (70% ethanol). Saliva was collected from seven volunteers. Agar well technique with different concentrations of black cardamom extracts was used to test the sensitivities of Mutans Streptococci, as well black cardamom extracts effect on viable counts of Mutans Streptococ
... Show More
(1)
Objective. This study aimed to evaluate and compare the force degradation of two types of elastomeric chains following different periods of immersion in zinc-containing mouthwashes. Materials and Methods. Four hundred and forty pieces of Elasto-Force and Super Elasto-Force elastomeric chains were divided into two control and eight experimental groups. The pieces were stretched to 25 mm on pins mounted on an acrylic block and stored in distilled water at 37°C. The experimental groups were immersed in four different types of mouthwash for one minute twice a day throughout the test period. Ten continuous thermocycles per day between cold and hot water baths (5–55°C) were carried out. Forces were measured at six-time intervals (in
... Show More
(6)
(4)
We aimed to examine the effect of amoxicillin and azithromycin suspensions on the microhardness of sliver-reinforced glass ionomer and nano-resin modified glass ionomer (GI). Method: Thirty discs (2mm height x 4mm diameter) of each type of GI were prepared, which were randomly assigned to amoxicillin, azithromycin, and artificial saliva groups. Microhardness was evaluated by Vickers hardness test before and after three immersion cycles. Results: The overall model (P < 0.001), before/after intervention (P < 0.001), intervention group (type of antibiotic) (P=0.013), and type of glass ionomer (P < 0.001) showed significant differences among study groups (P < 0.001). Post hoc test showed only non-significant before/after difference for Azithrom
... Show More
(4)
Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c
(3)
This study compares the effects of plasma jet and plasma-activated water on teeth root canals contaminated with Escherichia coli bacteria. A plasma jet system was developed for biological purposes that operate at atmospheric pressure. The plasma jet works with argon gas and is generated by a power supply, which supplies a sinusoidal alternating voltage of 12 kV of 20 kHz frequency. The system was optically diagnosed, as it was found that the peaks of the nitrogen spectrum were obtained at the wavelength (300- 450) nm with the appearance of hydroxide peaks at 380 nm. Extracted teeth with one root canal were used, which were contaminated with bacteria and divided into two groups to be treated with a plasma jet and plasma-activated
... Show More
(1)
Background: The marginal adaptation has a key role in the success and longevity of the fixed dental restoration, which is affected by the impression and the fabrication techniques .The objective of this in vitro study was to evaluate and compare the marginal fitness of lithium disilicate crowns using two different digital impression techniques (direct and indirect techniques) and two different fabrication techniques (CAD/CAM and Press techniques). Materials and Methods: Thirty two sound upper first premolar teeth of comparable size extracted for orthodontic reason were selected in this study .Standardized preparation of all teeth samples were carried out with modified dental surveyor to receive all ceramic crown restoration with 1 mm deep
... Show More
(1)