The effect of contact time between alginate impression material and type III dental stone on the surface properties of stone casts
...Show More Authors

Background: Alginate impression material is the irreversible hydrocolloid material that is widely used in dentistry. The contact time between alginate and gypsum cast could have a detrimental effect on the properties of the gypsum cast. The objective of this study is to evaluate the impact of various contact time intervals of Alginate impressions & type III dental stone on surface properties of stone cast. Materials and Methods: Time intervals tested were 1hour, 6 hours and 9 hours. Surface properties of stone cast evaluated were surface detail reproduction, hardness and roughness. Surface detail reproduction was determined using cylindrical brass test block in accordance with ISO 1563. Surface roughness was measured by profilometer and hardness was measured by Durometer (Shore D). Results: The detail reproduction showed significant difference (P<0.05), at 6 hr., and 9 hr. showed better results. While surface roughness significantly decreased (p<0.01) with prolonged contact time. However, surface hardness increased significantly (p<0.01) with increased contact time. Conclusions: Surface detail reproduction increased with increasing the contact time and this was noticed at (6, 9 hours). However, 1hour time interval showed decreased surface detailed reproduction. Roughness decreased when the contact time was increased between type III dental stone and alginate impression whereas, hardness was improved significantly with increasing contact time.

Scopus Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Mon Jul 01 1996
Journal Name
Bulletin Of The Iraq Natural History Museum (p-issn: 1017-8678 , E-issn: 2311-9799)
HAEMOPROTEUS BURHINUSA NEW SPECIES FROM THE STONE CURLEW, BU RHINUS OEDICN EMUS SAHARAE (REICHENOW) IN IRAQ
...Show More Authors

Haemoproteus burhinus is described from the stone curlew, Burhinus oedicnemus saharae (Reichenow) from Al-Attariya, 45 km SE Baghdad city middle of Iraq. It is related to but differs from H. peireci in that it hypertrophied the erythrocyte and the erythrocyte nucleus is always laterally displaced in microgametocytes.

View Publication Preview PDF
Publication Date
Mon Dec 05 2022
Journal Name
F1000research
Enhancement of surface properties of polyetheretherketone implant material by fractional laser texturing
...Show More Authors

Background: Polyetheretherketone (PEEK) is a promising implant material due to its superior biomechanical strength. However, due to its hydrophobic nature and lack of cellular adhesion properties, it has poor integration with bone tissue. Methods: A fractional CO2 laser was used with various parameters for surface texturing of PEEK substrate to enhance its surface properties. An optical microscope and field-emission scanning electron microscope (FESEM) were used to examine the surface morphology of untextured and laser-textured samples. Energy dispersive X-ray spectroscopy (EDX) was performed to determine the effect of the laser on the microstructure of PEEK. Surface microroughness, atomic force microscopy (AFM), and wettability were invest

... Show More
View Publication Preview PDF
Crossref (3)
Scopus Crossref
Publication Date
Fri Sep 15 2017
Journal Name
Journal Of Baghdad College Of Dentistry
Evaluate the effect of surface treatments on shear bond strength between lithium disilicate ceramic and dentin.
...Show More Authors

Purpose: To evaluate the effect of different surface treatments on shear bond strength between dentin and IPS e.max lithium disilicate glass-ceramic. Materials and Methods: Eighteen extracted third molars were embeded in epoxy resin. The tooth was sectioned vertically in mesiodistal direction using a low speed hard tissue microtome. The buccal and lingual surfaces of each section were ground flat using 600 grit Silicone carbide paper. Eighteen ceramic discs consisted of lithium disilicate glass-ceramic were prepared with a diameter of 4.7mm and height of 2.2mm. The discs were divided in two groups (n=10): (1) IPS e.max treated with hydrofluoric acid and Monobond Plus (MBP) and (2) IPS e.max treated with Monobond Etch &Prime (MBEP). The toot

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Wed Sep 01 2021
Journal Name
Iraqi Journal Of Physics
The Effect of Etching Time On Structural Properties of Porous Quaternary AlInGaN Thin Films
...Show More Authors

Using photo electrochemical etching technique (PEC), porous silicon (PS) layers were produced on n-type silicon (Si) wafers to generate porous silicon for n-type with an orientation of (111) The results of etching time were investigated at: (5,10,15 min). X-ray diffraction experiments revealed differences between the surface of the sample sheet and the synthesized porous silicon. The largest crystal size is (30 nm) and the lowest crystal size is (28.6 nm) The analysis of Atomic Force Microscopy (AFM) and Field Emission Scanning Electron Microscope (FESEM) were used to research the morphology of porous silicon layer. As etching time increased, AFM findings showed that root mean square (RMS) of roughness and po

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Wed Sep 20 2023
Journal Name
International Journal Of Dentistry
Improving Surface Properties of PEEK for Dental Applications by Using Piranha Solution
...Show More Authors

Background. “Polyetheretherketone (PEEK)” is a biocompatible, high-strength polymer that is well-suited for use in dental applications due to its unique properties. However, achieving good adhesion between PEEK and hydrophilic materials such as dental adhesives or cement can be challenging. Also, this hydrophobicity may affect the use of PEEK as an implant material. Surface treatment or conditioning is often necessary to improve surface properties. The piranha solution is the treatment of choice to be explored for this purpose. Methods. PEEK disks of 10 mm diameter and 2 mm thickness were used in this study. Those samples were divided into five groups (each group has five samples). The first is the control group, in which no

... Show More
View Publication Preview PDF
Scopus (2)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Wed Oct 01 2014
Journal Name
Journal Of The Faculty Of Medicine Baghdad
Management of Obstractive Jaundice Due to Common Bile Duct Stone in Baghdad Teaching Hospital.
...Show More Authors

Background: the most common cause of obstructive jaundice is CBD stones, and these can produce significant morbidity and mortality. The management of the obstructive jaundice due to CBD stones is in evolution; several methods of investigations and treatment have been introduced, and each one has its own advantages and disadvantages.

Objective: to study and evaluate the management of obstructive jaundice due to CBD stones in Baghdad teaching hospital.

Results: from the 125 patients presented with obstructive jaundice included in this study 14 patients were found to have a periampullary lesions, and they were excluded from the study, so the total number of the patients was

... Show More
View Publication Preview PDF
Crossref
Publication Date
Wed Mar 10 2021
Journal Name
Baghdad Science Journal
Removal of Suspended Solids Using Pumice Stone in Integrated Fixed Film Activated Sludge Process
...Show More Authors

Wastewater treatment plants operators prefer to make adjustments because they are more cost effective, to use the existing tank instead of building new ones. In this case an imported materials would be  used as bio-loads to increase biomass and thus maintain efficiency as the next organic loading increases.In the present study, a local substance "pumice stone" was used as a biological carrier in the aeration tank, and the experiments were carried out in five stages: without biological carriers, filling ratio of 4%,10%,20%, and25% with pumice stone, the maximum organic loading at each stage (1.1884, 1.2144, 1.9432, 2.7768, 3.3141)g BOD /l.d respectively.Other experiments were carried out to determine the best filling ratio, the SS remova

... Show More
View Publication Preview PDF
Scopus (1)
Scopus Clarivate Crossref
Publication Date
Wed Dec 25 2024
Journal Name
Journal Of Baghdad College Of Dentistry
Surface properties of heat treated with different durations of titanium alloy dental implants
...Show More Authors

Background: The surface properties of the titanium alloy plays a significant role in the bond of the dental implant with living bone and modification of the implant surface could enhance osseointegration. This study was aimed to investigate the effect of different durations of heat treatment on the surface properties of titanium alloy for dental implants. Materials and methods: Twenty disks of (Ti-6Al-4V) alloy were prepared. The sample was divided into four test groups to study the effect of different duration of heat treatment to the surface topography; surface chemistry, titanium oxide layer thickness, blood contact angle, & blood drop diameter of titanium alloy samples were investigated to evaluate the effect of different durations of

... Show More
View Publication Preview PDF
Publication Date
Sun Jul 02 2006
Journal Name
Journal Of The Faculty Of Medicine Baghdad
the effect of sublethal concentrations of silver nitrate on Alginate production by bseudomonas aeruginosa
...Show More Authors

Background:

View Publication Preview PDF
Crossref
Publication Date
Sun May 01 2011
Journal Name
Thin Solid Films
Effect of temperature and deposition time on the optical properties of chemically deposited nanostructure PbS thin films
...Show More Authors

View Publication
Scopus (51)
Crossref (48)
Scopus Clarivate Crossref