1-(4-amino-3-(benzo[d]thiazol-2-yldiazenyl)phenyl)ethanone has been synthezied by reaction the diazonium salt of 2-aminobenzothiazole with 4-aminoacetophenone. Specroscopic studies ( FTIR,UV-Vis, 1H and 13CNMR) and microelemental analysis (C.H.N.S.O) are use to identified of the azo ligand. Metal chelates of some transition metals were performed as well depicted. Complexes were identified using atomic absorption of flame, elemental analysis, infrared and UV-Vis spectral process as well conductivity and magnetic quantifications. Nature of compounds produced have been studied followed the mole ratio and continuous contrast methods, Beer's law followed during a concentration scope (1×10-4 - 3×10-4 mol/L). height molar absorbtivity of compoun

In this work, 332 Al alloy was prepared and reinforced with (0.5% and 1%) nano-Al₂O₃ particles. The prepared unreinforced and reinforced 332 Al alloy with nano-Al₂O₃ were solution heat treated (T6) at 510 ̊C and aged at 225 ̊C with different times (1, 3, and 5 h). Hardness test was performed on all the prepared alloys. All prepared alloys were dry slided under different applied loads (5, 10, 15, and 20 N) against steel counterface surface using pin on disk apparatus. The results showed that refinement effect was observed after addition of nano-Al₂O₃ particles and a change in silicon morphology after performing the solution heat treatment. The results also showed that har

In the present work, pulsed laser deposition (PLD) technique was applied to a pellet of Chromium Oxide (99.999% pure) with 2.5 cm diameter and 3 mm thickness at a pressure of 5 Tons using a Hydraulic piston. The films were deposited using Nd: YAG laser λ= (4664) nm at 600 mJ and 400 number of shot on a glass substrate, The thickness of the film was (107 nm). Structural and morphological analysis showed that the films started to crystallize at annealing temperature greater than 400 oC. Absorbance and transmittance spectra were recorded in the wavelength range (300-
4400) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of d

SnS has been widely used in photoelectric devices due to its special band gap of 1.2-1.5 eV. Here, we reported on the fabrication of SnS nanosheets and the effect of synthesis condition together with heat treatment on its physical properties. The obtained band gap of the SnS nanosheets is in the rage of 1.37-1.41 eV. It was found that the photo-current density of a thin film comprised of SnS nanosheets could be enhanced significantly by annealing treatment. The maximum photo-current density of the stack structure of FTO/SnS/CdS/Pt was high as 389.5 mu A cm(-2), rendering its potential application in high efficiency solar hydrogen production.

Metallic nanoparticles are increasingly studied for their biomedical applications due to their unique physicochemical and catalytic properties. Here, a broccoli-mediated gold/platinum nanohybrid (Au@Pt NH) was synthesized using an ultrasound-assisted green method with an aqueous extract of Brassica oleracea var. italica for multifunctional biomedical evaluation. XRD and TEM confirmed a crystalline nanohybrid with an average crystallite size of 7.56 nm and a mean particle diameter of 13.08 ± 7.58 nm. The broccoli extract produced no inhibition zones, whereas Au@Pt NH inhibited Staphylococcus aureus (18 mm), Staphylococcus epidermidis (21 mm), Escherichia coli (18 mm), Klebsiella pneumoniae (20 mm), and Candida albicans (21 mm). In vivo,

One of the most significant challenges of medical care is the infection of postoperative wounds, and conventional visual examination often fails to detect it early. This research proposes the design of an innovative, passive wireless telemetry system for non-intrusive monitoring of the wound-healing process.  The system integrates a biocompatible resonance circuit (LC) with a high-sensitivity piezoresistive sensor based on MXene (Ti3C2Tx). It operates within the standard industrial and medical (ISM) band at 13.56 MHz.The detection mechanism in the system is based on the principle of "impedance modulation" (Impedance Modulation), which arises from changes in the sensor's resistance under physiological tissue pressure. The system was

In this work a hybrid composite materials were prepared containing matrix of polymer (polyethylene PE) reinforced by different reinforcing materials (Alumina powder + Carbon black powder CB + Silica powder). The hybrid composite materials prepared are: • H1 = PE + Al2O3 + CB • H2 = PE + CB + SiO2 • H3 = PE + Al2O3 + CB + SiO2 All samples related to electrical tests were prepared by injection molding process. Mechanical tests include compression with different temperatures and different chemical solutions at different immersion times The mechanical experimentations results were in favour of the samples (H3) with an obvious weakness of the samples (H1) and a decrease of these properties with a rise in temperature and the increasing